Chitosan aerogels conjugates the characteristics of nanostructured porous materials, i.e., extended specific surface area and nano scale porosity, with the remarkable functional properties of chitosan. Aerogels were obtained from solutions of chitosan in ionic liquids (ILs), 1-butyl-3-methylimidazolium acetate (BMIMAc), and 1-ethyl-3-methyl-imidazolium acetate (EMIMAc), in order to observe the effect of the solvent in the structural characteristics of this type of materials. The process of elaboration of aerogels comprised the formation of physical gels through anti-solvent vapor diffusion, liquid phase exchange, and supercritical CO2 drying. The aerogels maintained the chemical identity of chitosan according to Fourier transform infrared spectrophotometer (FT-IR) spectroscopy, indicating the presence of their characteristic functional groups. The internal structure of the obtained aerogels appears as porous aggregated networks in microscopy images. The obtained materials have specific surface areas over 350 m2/g and can be considered mesoporous. According to swelling experiments, the chitosan aerogels could absorb between three and six times their weight of water. However, the swelling and diffusion coefficient decreased at higher temperatures. The structural characteristics of chitosan aerogels that are obtained from ionic liquids are distinctive and could be related to solvation dynamic at the initial state.

Arabinoxylans (AXs) with high ferulic acid (FA) content (7.18 µg/mg AXs) were cross-linked using laccase. Storage (G’) modulus of AX solutions at 1% (AX-1) and 2% (AX-2) (w/v) registered maximum values of 409 Pa and 889 Pa at 180 min and 83 min, respectively. Atomic force microscopy revealed the grained and irregular surface of the AX-1 gel and the smoother surface without significant depressions of the AX-2 gel. Cured AX gels exhibited a liquid phase surrounding the samples indicating syneresis. The syneresis ratio percentage (% Rs) of the gels was registered over time reaching stabilization at 20 h. The % Rs was not significantly different between AX-1 (60.0%) and AX-2 (62.8%) gels. After 20 h of syneresis development, the dimers of the FA in the AX-1 and AX-2 gels significantly increased by 9% and 78%, respectively; moreover, the trimers of the FA in the AX-1 and AX-2 gels, by 94% and 300%, respectively. Scanning electron microscopy showed that, after syneresis stabilization, AX gels presented a more compact microstructure. Syneresis development in the gels of highly ferulated AXs could be related to the polymer network contraction due to the additional formation of dimers and trimers of the FA (cross-linking structures), which may act like a “zipping” process, increasing the polymer chains′ connectivity.