Objectives: The aim of this study is to assess the micro-tensile bond strength and the mode of failure of a bioactive hybrid self-adhesive composite (Surefil one) under various dentin conditions. Methods: Thirty-two extracted human molar teeth were used to test the micro-tensile bond strength of Surefil one under different dentine conditions (no treatment, 37% phosphoric acid etching, and universal adhesive) in comparison with a resin-modified glass ionomer (RIVA). All restorations were light cure-bonded onto flat dentine and then sectioned into beams. Then, fractured specimens were observed under a light microscope to evaluate the mode of failure. Results: The Surefil one no-treatment group (NTG) exhibited the highest micro-tensile bond strength. Furthermore, there was no statistically significant difference observed between the Surefil one adhesive group (EAG) and the Surefil one acid etch group (EG). However, compared to other groups, the resin-modified glass ionomer (RIVA) produced the lowest results, which are statistically significant. Conclusion: Surefil one offers superior bond strength values when compared to resin-modified glass ionomers. Furthermore, Surefil one requires no dentin condition and has more straightforward clinical steps. [ABSTRACT FROM AUTHOR]

Objectives: Current dental resins exhibit polymerization shrinkage causing microleakage, which has the potential to cause recurrent caries. Our objectives were to create and characterize low-shrinkage-stress (LSS) composites with dimethylaminododecyl methacrylate (DMADDM) as an antibacterial agent to combat recurrent caries. Methods: Triethylene glycol divinylbenzyl ether and urethane dimethacrylate were used to reduce shrinkage stress. DMADDM was incorporated at different mass fractions (0%, 1.5%, 3%, and 5%). Flexural strength, elastic modulus, degree of conversion, polymerization stress, and antimicrobial activity were assessed. Results: The composite with 5% DMADDM demonstrated higher flexural strength than the commercial group (p < 0.05). The addition of DMADDM in BisGMA-TEGDMA resin and LSS resin achieved clinically acceptable degrees of conversion. However, LSS composites exhibited much lower polymerization shrinkage stress than BisGMA-TEGDMA composite groups (p < 0.05). The addition of 3% and 5% DMADDM showed a 6-log reduction in Streptococcus mutans (S. mutans) biofilm CFUs compared to commercial control (p < 0.001). Biofilm biomass and lactic acid were also substantially decreased via DMADDM (p < 0.05). Conclusions: The novel LSS dental composite containing 3% DMADDM demonstrated potent antibacterial action against S. mutans biofilms and much lower polymerization shrinkage-stress, while maintaining excellent mechanical characteristics. The new composite is promising for dental applications to prevent secondary caries and increase restoration longevity. [ABSTRACT FROM AUTHOR]