The thermoelectric behavior and stability of Cu 2 SnS 3 (CTS) has been investigated in relation to different preparations and sintering conditions, leading to different microstructures and porosities. The studied system is CTS in its cubic polymorph, produced in powder form via a bottom-up approach based on high-energy reactive milling. The as-milled powder was sintered in two batches with different synthesis conditions to produce bulk CTS samples: manual cold pressing followed by traditional sintering (TS), or open die pressing (ODP). Despite the significant differences in densities, ~75% and ~90% of the theoretical density for TS and ODP, respectively, we observed no significant difference in electrical transport. The stable, best performing TS samples reached zT ~0.45, above 700 K, whereas zT reached ~0.34 for the best performing ODP in the same conditions. The higher zT of the TS sintered sample is due to the ultra-low thermal conductivity ( κ ~0.3-0.2 W/mK), three-fold lower than ODP in the entire measured temperature range. The effect of porosity and production conditions on the transport properties is highlighted, which could pave the way to produce high-performing TE materials.

The present work focused on the microstructural, thermal, electrical, and damping characterization of NiMnGa samples produced through a powder pressing and a sintering process; the effect of sintering times and of the starting powder size were evaluated. Moreover, an observation of the evolution of martensitic transformation typical of NiMnGa ferromagnetic shape memory alloy was conducted in comparison with the cast material behavior and in correlation with the material densification. The optimum powder size and sintering time for the process, i.e., 50 µm or lower and 72 h, were identified considering the investigated physical properties of the sintered samples in comparison to the cast material. The corresponding sample showed the best compromise between density, thermal and electrical properties, and damping and functional behaviour. In general, the outcomes of this study could be the basis of a useful tool for production processes that include a sintering step as well as being a starting point for the evaluation of an alternative low cost fabrication method of this alloy.