Search

PLA and its blends are the most extensively used materials for various biomedical applications such as scaffolds, implants, and other medical devices. The most extensively used method for tubular scaffold fabrication is by using the extrusion process. However, PLA scaffolds show limitations such as low mechanical strength as compared to metallic scaffolds and inferior bioactivities, limiting their clinical application. Thus, in order to improve the mechanical properties of tubular scaffolds, they were biaxially expanded, wherein the bioactivity can be improved by surface modifications using UV treatment. However, detailed studies are needed to study the effect of UV irradiation on the surface properties of biaxially expanded scaffolds. In this work, tubular scaffolds were fabricated using a novel single-step biaxial expansion process, and the surface properties of the tubular scaffolds after different durations of UV irradiation were evaluated. The results show that changes in the surface wettability of scaffolds were observed after 2 min of UV exposure, and wettability increased with the increased duration of UV exposure. FTIR and XPS results were in conjunction and showed the formation of oxygen-rich functional groups with the increased UV irradiation of the surface. AFM showed increased surface roughness with the increase in UV duration. However, it was observed that scaffold crystallinity first increased and then decreased with the UV exposure. This study provides a new and detailed insight into the surface modification of the PLA scaffolds using UV exposure. [ABSTRACT FROM AUTHOR]

The surface of dental implants plays a vital role in early and more predictable osseointegration. SLA (sandblasted large grit and acid-etched) represents the most widely accepted, long-term clinically proven surface. Primarily, dental implants are manufactured by either commercially pure titanium (CP-Ti) or Ti6Al4V ELI alloy. The acid etch behavior of CP-Ti is well known and its effects on the surface microstructure and physicochemical properties have been studied by various researchers in the past. However, there is a lack of studies showing the effect of acid etching parameters on the Ti6Al4V alloy surface. The requirement of the narrow diameter implants necessitates implant manufacturing from alloys due to their high mechanical properties. Hence, it is necessary to have an insight on the behavior of acid etching of the alloy surface as it might be different due to changed compositions and microstructure, which can further influence the osseointegration process. The present research was carried out to study the effect of acid etching parameters on Ti6Al4V ELI alloy surface properties and the optimization of process parameters to produce micro- and nanotopography on the dental implant surface. This study shows that the Ti6Al4V ELI alloy depicts an entirely different surface topography compared to CP-Ti. Moreover, the surface topography of the Ti6Al4V ELI alloy was also different when etching was done at room temperature compared to high temperature, which in turn affected the behavior of the cell on these surfaces. Both microns and nano-level topography were achieved through the optimized parameters of acid etching on Ti6Al4V ELI alloy dental implant surface along with improved roughness, hydrophilicity, and enhanced cytocompatibility. [ABSTRACT FROM AUTHOR]