Search

Photoelectrocatalysis (PEC) has been already proposed as a polishing treatment for wastewater treatment plants (WWTPs) effluents. In this work, the impact of polarization reversal during PEC process has been studied and evaluated on the basis of the removal of organic substance and color, biodegradability of the matrix, and inactivation of the catalyst. Effluents were sampled from a full-scale WWTP and alternatively treated by electrochemical oxidation (EC), photolysis (PL), photocatalysis (PC), photoelectrocatalysis, and photoelectrocatalysis with reverse polarization (PECr). The efficiency and the kinetics of the process, in terms of removal of organic substance and color, were not affected by reverse polarization and very similar results were obtained by PEC and PECr. The biodegradability of the effluents strongly increased both by PECr (RSBR: 0.84 ± 0.07), and by PEC and PL (0.89 ± 0.11, and 0.78 ± 0.02, respectively). In the selected polarization reversal mode (100 s at −0.1 V every 500 s at 4 V, cell voltage), a similar photocurrent loss after PEC and PECr was observed, suggesting no effect on the activity of the TiO2 mesh. This study can serve as a base for future research on polarization reversal to optimize operation parameters and exploit the procedure to preventing fouling and inactivation of the catalyst. [ABSTRACT FROM AUTHOR]

In this study, the effects of photo-electrocatalysis (PEC) were evaluated as an innovative application of conventional photocatalysis (PC) to remediate water in a recirculating system for rainbow trout (Oncorhynchus mykiss) culture, in relation to fish welfare and health, with a multidisciplinary approach. Three tanks were employed, equipped with conventional biological filters as a control system, and three tanks equipped with the PEC purification system. The concentrations of ammonia, nitrite and nitrate ions in water were monitored, and the fish's oxidative damage and stress response were evaluated in parallel. The water of the PEC-treated experimental group showed lower ammonia (TAN) and nitrite concentrations and higher nitrate concentration, possibly deriving from TAN oxidation through PEC, also leading to gaseous N2. Histological analysis did not reveal any pathological alteration in the gills and liver of both groups. The superoxide dismutase (sod1), glutathione reductase (GR), glutathione peroxidase (GPx1), and Tumor necrosis factor (TNFα) gene expressions were significantly higher in the control group than in the PEC-treated group, while the Heat shock protein 70 (Hsp70) expression did not show any difference in the two groups. These results indicate that the use of PEC filters has a positive effect on water quality, compared to the use of conventional biological filters, inducing a high level of welfare in O. mykiss. [ABSTRACT FROM AUTHOR]

The aim of the present work is to investigate the synthesis of Ti–Nb alloy films obtained by the physical vapor deposition (PVD) magnetron sputtering of Nb films on Ti substrates, followed by low-energy high-current electron beam (LEHCEB) alloying treatment. Ti–Nb alloys were synthetized under two different regimes, one by varying the deposited amount of Nb (from 25 to 150 nm) and treating samples with low applied voltages and a number of pulses (three pulses at either 20 or 25 kV), the second by setting the amount of Nb (100 nm) and alloying it at a higher applied voltage with a different number of pulses (from 10 to 50 at 25 and 30 kV). The synthetized Ti–Nb alloys were characterized by XRD and GDOES for phase identification and chemical composition; SEM and optical microscopy were employed for morphology evaluation; compositional investigation was done by EDS analysis and mechanical properties were evaluated by microindentation tests. LEHCEB treatment led to the formation of metastable phases (α′, α″ and β) which, together with the grain refinement effect, was responsible for improved mechanical properties. [ABSTRACT FROM AUTHOR]

Plasma Electrolytic Oxidation (PEO) was applied to extruded ZM21 Mg alloys to improve their corrosion resistance in a chloride-containing environment. PEO was carried out in DC mode and voltage control in a fluoride-free electrolyte. Potentiodynamic polarization tests in 3.5 wt.% NaCl aqueous solution and neutral salt spray (NSS) tests were carried out. Microstructural and profilometric characterization, as well as NSS tests were performed in different conditions: (i) bare ZM21, (ii) PEO-treated ZM21, (iii) powder-coated ZM21 (without PEO interlayer), and (iv) PEO-treated ZM21 with powder coating top layer (carboxyl-functionalized polyester resin). The PEO + powder coating double layer was identified as the best-performing corrosion protection. [ABSTRACT FROM AUTHOR]

Photoelectrocatalysis (PEC), photolysis (PL), and photocatalysis (PC) were applied to increase the biodegradability of wastewaters effluents sampled from a plant collecting both municipal wastewaters and aqueous waste. In PEC, the catalyst was a porous TiO2 photoanode obtained by plasma electrolytic oxidation and electrically polarized during operation. In PC a dispersion of TiO2 powders was used. The same irradiation shielding, and similar catalyst surface areas were set for PC and PEC, allowing a straightforward evaluation of the catalytic effect of the electrical polarization of TiO2 during operation. Results showed that the chemical oxygen demand (COD) and color removal rates follow the order: PEC > PL and PEC > PC. The specific biodegradability rate (SBR) increased following the same order, the PEC process allowing SBR values more than twice higher than PL and PC. The operating costs were calculated based on the electrical energy per order of COD, color, and SBR values, demonstrating that at the laboratory scale the energy demand of PEC is significantly lower than the other two tested processes. [ABSTRACT FROM AUTHOR]

In this study, we report an investigation of the photoelectrochemical activity of TiO2 films formed by DC plasma electrolytic oxidation (PEO) at a variable potential in a sulfuric acid electrolyte at 0 and 25 °C. The surface morphology was mainly determined by the oxide-forming potential. X-Ray Diffraction and Raman analyses showed that the relative amount of the anatase and rutile phases varied from 100% anatase at low potential (110–130 V) to 100% rutile at high potential (180–200 V), while mixed-phase oxide films formed at intermediate potential. Correspondingly, the band gap of the TiO2 films decreased from about 3.20 eV (pure anatase) to 2.94 eV (pure rutile) and was red-shifted about 0.1 eV by reducing the electrolyte temperature from 25 °C to 0 °C. Glow-Discharge Optical Emission Spectroscopy (GD-OES) and X-ray Photoelectron Spectroscopy (XPS) analyses evidenced S-containing species located preferentially close to the TiO2/Ti interface. The photoelectrochemical activity was assessed by measuring the incident photon-to-current efficiency (IPCE) under Ultraviolet C (UV-C) irradiation, which showed a non-gaussian normal trend as a function of the PEO cell potential, with maximum values exceeding 80%. Photoelectrocatalytic activity was assessed by decolorization of model solutions containing methylene blue. Photoanodes having higher IPCE values showed faster decolorization kinetics. [ABSTRACT FROM AUTHOR]

Carbamazepine (CBZ) is a pharmaceutical compound recalcitrant to conventional wastewater treatment plants and widely detected in wastewater bodies. In the present study, advanced oxidation processes for carbamazepine removal are investigated, with particular regard to the degradation pathways of carbamazepine by photoelectrocatalysis and conventional photocatalysis. Photoelectrocatalysis was carried out onto TiO2 meshes obtained by Plasma Electrolytic Oxidation, a well-known technique in the field of industrial surface treatments, in view of an easy scale-up of the process. By photoelectrocatalysis, 99% of carbamazepine was removed in 55 min while only 65% removal was achieved by photolysis. The investigation of the transformation products (TPs) was carried out by means of UPLC-QTOF/MS/MS. Several new TPs were identified and accordingly reaction pathways were proposed. Above 80 min the transformation products disappear, probably forming organic acids of low-molecular weight as final degradation products. The results demonstrated that photoelectrocatalysis onto TiO2 meshes obtained by plasma electrolytic oxidation is a useful alternative to common advanced oxidation processes as wastewater tertiary treatment aimed at removing compounds of emerging concern. [ABSTRACT FROM AUTHOR]