Basswood samples were exposed to oxygen glow-discharge plasmas for 30 min, and etching of radial and tangential longitudinal surfaces was measured. It was hypothesized that there would be a positive correlation between etching and plasma energy, and differential etching of wood surfaces because of variation in the microstructure and chemical composition of different woody tissues. Etching at the surface of basswood samples was examined using profilometry. Light and scanning electron microscopy were used to examine the microstructure of samples exposed to plasma. There was a large effect of plasma energy on etching of basswood surfaces, and radial surfaces were etched to a greater extent than tangential surfaces. However, rays at radial surfaces were more resistant to etching than fibers, resulting in greater variation in the etching of radial versus tangential surfaces. The same phenomenon occurred at radial surfaces of balsa wood, jelutong and New Zealand white pine subjected to plasma etching. The possible reasons for the greater resistance of rays to plasma etching are explored, and it is suggested that such differential etching of wood surfaces may impose a limitation on the use of plasma to precisely etch functional patterns at wood surfaces (raised pillars, grooves), as has been done with other materials. [ABSTRACT FROM AUTHOR]

Optically transparent wood is a type of composite material, combining wood as a renewable resource with the optical and mechanical properties of synthetic polymers. During this study, the effect of monochromatic UV-C (λ—250 nm) radiation on transparent wood was evaluated. Samples of basswood were treated using a lignin modification method, to preserve most of the lignin, and subsequently impregnated with refractive-index-matched types of acrylic polymers (methyl methacrylate, 2-hydroxyethyl methacrylate). Optical (transmittance, colour) and mechanical (shore D hardness) properties were measured to describe the degradation process over 35 days. The transmittance of the samples was significantly decreased during the first seven days (12% EMA, 15% MMA). The average lightness of both materials decreased by 10% (EMA) and 17% (MMA), and the colour shifted towards a red and yellow area of CIE L*a*b* space coordinates. The influence of UV-C radiation on the hardness of the samples was statistically insignificant (W+MMA 84.98 ± 2.05; W+EMA 84.89 ± 2.46), therefore the hardness mainly depends on the hardness of used acrylic polymer. The obtained results can be used to assess the effect of disinfection of transparent wood surfaces with UV-C radiation (e.g., due to inactivation of SARS-CoV-2 virus) on the change of its aesthetic and mechanical properties. [ABSTRACT FROM AUTHOR]