Search

We studied the shear bond strength (SBS) of two PEEK composites (BioHPP, BioHPP plus) with three veneering composites: Visio.lign, SR Nexco and VITA VM LC, depending on the surface treatment: untreated, sandblasted with 110 μm Al 2 O 3 , sandblasted and cleaned ultrasonically in 80% ethanol, with or without adhesive Visio.link, with applied Visio.link and MKZ primer. For the BioHPP plus, differential scanning calorimetry (DSC) revealed a slightly lower glass transition temperature ( T g 150.4 ± 0.4 °C) and higher melting temperature ( T m 339.4 ± 0.6 °C) than those of BioHPP ( T g 151.3 ± 1.3 °C, T m 338.7 ± 0.2 °C). The dynamical mechanical analysis (DMA) revealed a slightly higher storage modulus of BioHPP ( E' 4.258 ± 0.093 GPa) than of BioHPP plus ( E ' 4.193 ± 0.09 GPa). The roughness was the highest for the untreated BioHPP plus, and the lowest for the polished BioHPP. The highest hydrophobicity was achieved on the sandblasted BioHPP plus, whereas the highest hydrophilicity was found on the untreated BioHPP. The highest SBSs were determined for BioHPP and Visio.lign, adhesive Visio.link (26.31 ± 4.17 MPa) or MKZ primer (25.59 ± 3.17 MPa), with VITA VM LC, MKZ primer and Visio.link (25.51 ± 1.94 MPa), and ultrasonically cleaned, with Visio.link (26.28 ± 2.94 MPa). For BioHPP plus, the highest SBS was determined for a sandblasted surface, cleaned ultrasonically, with the SR Nexco and Visio.link (23.39 ± 2.80 MPa).

This study investigated the influence of viscose fibre (VF) geometry on the microstructures and resulting properties of high-density polyethylene (HDPE) composites. Seven types of viscose fibres varying in cross-section shape, linear density, and length were pelletised, compounded into HDPE with a twin-screw extruder, and injection moulded. The microstructures of the composites were characterised by investigating their cross-sections and by extracting the fibres and measuring their lengths using optical microscopy (OM). The mechanical and thermal properties of the composites were characterised using differential scanning calorimetry (DSC), tensile tests, Charpy impact tests, and dynamic mechanical analysis (DMA). The composites prepared using cylindrical fibres with a linear density of 1.7 dtex exhibited the best fibre dispersion, highest orientation, and lowest fibre-fibre contact area. The decrease in the linear density of the cylindrical fibres resulted in increasingly worse dispersion and orientation, while composites containing non-cylindrical fibres exhibited a comparably larger fibre-fibre contact area. The initial fibre length of about 3 to 10 mm decreased to the mean values of 0.29 mm to 0.41 mm during processing, depending on the initial geometry. In general, cylindrical fibres exhibited a superior reinforcing effect in comparison to non-cylindrical fibres. The composites containing cylindrical fibres with a linear density of 1.7 dtex and a length of 5 mm exhibited the best reinforcing effect with an increase in tensile modulus and strength of 323% and 141%, respectively.

Composites of polyolefin matrices (HDPE and PP) were prepared by melt processing using two commercially available nano ZnO powders (Zinkoxyd aktiv and Zano 20). The mechanical and thermal properties, UV-Vis stability, and antibacterial activity of composites were studied. Tensile testing revealed that both nano ZnO types have no particular effect on the mechanical properties of HDPE composites, while some positive trends are observed for the PP-based composites, but only when Zano 20 was used as a nanofiller. Minimal changes in mechanical properties of composites are supported by an almost unaffected degree of crystallinity of polymer matrix. All polyolefin/ZnO composites exposed to artificial sunlight for 8-10 weeks show more pronounced color change than pure matrices. This effect is more evident for the HDPE than for the PP based composites. Color change also depends on the ZnO concentration and type; composites with Zano 20 show more intense color changes than those prepared with Zinkoxyd aktiv. Results of the antibacterial properties study show very high activity of polyolefin/ZnO composites against Staphylococcus aureus regardless of the ZnO surface modification, while antibacterial activity against Escherichia coli shows only the composites prepared with unmodified ZnO. This phenomenon is explained by different membrane structure of gram-positive ( S. aureus ) and gram-negative ( E. coli ) bacteria.