Search

Friction is one of the main phenomena accompanying sheet metal forming methods, affecting the surface quality of products and the formability of the sheet metal. The most basic and cheapest way to reduce friction is to use lubricants, which should ensure the highest lubrication efficiency and at the same time be environmentally friendly. Due to the trend towards sustainable production, vegetable oils have been used in research as an alternative to petroleum-based lubricants. The analysis of friction in sheet metal forming requires an appropriate tribotester simulating the friction conditions in a specific area of the sheet metal being formed. Research has used a special strip drawing tribometer, enabling the determination the value of the coefficient of friction in the blankholder zone in the deep drawing process. Quantitative analysis of the friction phenomenon is necessary at the stage of designing the technological process and selecting technological parameters, including blankholder pressure. This article presents the results of friction testing of 1.0338 (DC04) steel sheets using a strip drawing test. The experimental tests involved pulling a strip of sheet metal between two countersamples with a rounded surface. The tests were carried out on countersamples with different levels of roughness for the range of contact pressures occurring in the blankholder zone in the deep drawing process (1.7–5 MPa). The values of the coefficient of friction determined under dry friction conditions were compared with the results for edible (corn, sunflower and rapeseed) and non-edible (Moringa, Karanja) vegetable lubricants. The tested oils are the most commonly used vegetable-based biolubricants in metal forming operations. Multi-layer artificial neural networks were used to determine the relationship between the value of the contact pressure, the roughness of the countersamples, the oil viscosity and density, and the value of the coefficient of friction. Rapeseed oil provided the best lubrication efficiency during friction testing for all of the tested samples, with an average surface roughness of Sa 0.44–1.34 μm. At the same time, as the roughness of the countersamples increased, a decrease in lubrication efficiency was observed. The lowest root mean squared error value was observed for the MLP-4-8-1 network trained with the quasi-Newton algorithm. Most of the analysed networks with different architectures trained using the various algorithms showed that the kinematic viscosity of the oil was the most important aspect in assessing the friction of the sheets tested. The influence of kinematic viscosity on the value of the coefficient of friction is strongly dependent on the surface roughness of the countersamples. [ABSTRACT FROM AUTHOR]

Aluminium alloy sheets cause many problems in sheet metal forming processes owing to their tendency to gall the surface of the tool. The paper presents a method for the determination of the kinematic friction coefficient of friction pairs. The determination of coefficient of friction (COF) in sheet metal forming requires specialised devices that 'simulate' friction conditions in specific areas of the formed sheet. In this article, the friction behaviour of aluminium alloy sheets was determined using the strip drawing test. The 1-mm-thick 6082 aluminium alloy sheets in T6 temper were used as test material. Different values for nominal pressures (4.38, 6.53, 8.13, 9.47, 10.63, and 11.69 MPa) and different sliding speeds (10 and 20 mm/min.) were considered. The change of friction conditions was also realised with several typical oils (hydraulic oil LHL 32, machine oil LAN 46 and engine oil SAE 5W-40 C3) commonly used in sheet metal forming operations. Friction tests were conducted at room temperature (24 °C). The main tribological mechanisms accompanying friction (adhesion, flattening, ploughing) were identified using a scanning electron microscope (SEM). The influence of the parameters of the friction process on the value of the COF was determined using artificial neural networks. The lowest value of the COF was recorded when lubricating the sheet metal surface with SAE 5W40 C3 engine oil, which is characterised as the most viscous of all tested lubricants. In dry friction conditions, a decreasing trend of the COF with increasing contact pressure was observed. In the whole range of applied contact pressures (4.38–11.69 MPa), the value of the COF during lubrication with SAE 5W40 C3 engine oil was between 0.14 and 0.17 for a sliding speed of 10 mm/min and between 0.13 and 0.16 for a sliding speed of 20 mm/min. The value of the COF during dry friction was between 0.23 and 0.28 for a sliding speed of 10 mm/min and between 0.22 and 0.26 for a sliding speed of 20 mm/min. SEM micrographs revealed that the main friction mechanism of 6082-T6 aluminium alloys sheet in contact with cold-work tool steel flattens surface asperities. The sensitivity analysis of the input parameters on the value of COF revealed that oil viscosity has the greatest impact on the value of the COF, followed by contact pressure and sliding speed. [ABSTRACT FROM AUTHOR]

AlSi7Mg/SiCp aluminium matrix composites (AMCs) with a high ceramic content (35 vol.%) that were produced by using the field-assisted sintering technique (FAST) were subjected to tribological preconditioning and evaluated as a potential lightweight material to substitute grey cast iron brake discs. However, since an uncontrolled running-in process of the AMC surface can lead to severe wear and thus to failure of the friction system, AMC surfaces cannot be used directly after finishing and have to be preconditioned. A defined generation of a tribologically conditioned surface (tribosurface) is necessary, as was the aim in this study. To simulate tribological conditions in automotive brake systems, the prepared AMC samples were tested in a pin-on-disc configuration against conventional brake lining material under dry sliding conditions. The influence of the surface topography generated by face turning using different indexable inserts and feeds or an additional plasma electrolytic treatment was investigated at varied test pressures and sliding distances. The results showed that the coefficient of friction remained nearly constant when the set pressure was reached, whereas the initial topography of the samples studied by SEM varied substantially. A novel approach based on analysing the material ratio determined by 3D surface measurement was developed in order to obtain quantitative findings for industrial application. [ABSTRACT FROM AUTHOR]

The effect of cylinder liners on engine performance is substantial. Typically, the cylinder surfaces were plateau honed. However, recently additional dimples or grooves were created on them. This work discusses the tribological impacts of textured cylinder liner surfaces based on a review of the literature. The results of the experimental research obtained using test rigs and fired engines were critically reviewed. In addition, the results of the modeling are shown. Circular oil pockets and grooves perpendicular to the sliding direction of piston rings of small depths were typically used. Surface texturing of the cylinder liners governs lubrication between the cylinder liner and the piston ring by an increase in oil film thickness near the reversal points leading to reductions in friction force and wear and in the fired engine to a decrease in fuel consumption and to an increase in power or torque. The correct texturing pattern ensures a decrease in the oil consumption, blow-by, and emissions of the internal combustion engine compared to plateau-honed surfaces. Considerations of future challenges are also addressed. The volume of lubricant reservoir in surface topography, called oil capacity, should be a substantial parameter characterizing textured surfaces. [ABSTRACT FROM AUTHOR]

Friction is one of the most important technological phenomena and has a large influence on the flow characteristics of a deformed material. A strip drawing friction test was used to evaluate the friction characteristics of 0.8 mm thick DC04 steel sheets in a sheet forming operation. Friction tests were carried out using a specially designed friction simulator and uniaxial tensile tests were carried out to determine the mechanical properties of the specimens. In addition, measurements of the sheet surface topography were carried out to identify the tribological properties of the specimens. The friction tests were conducted under different pressure and lubrication conditions. A comparative analysis of the results of the friction tests revealed different changes in the surface topography of the test sheets which can be associated with specific friction mechanisms. It was found that the effectiveness of lubrication depends on the lubricant viscosity and nominal pressure. Increasing the nominal pressure intensifies the phenomenon of asperity flattening and reduces the volume of closed pockets of lubricant. [ABSTRACT FROM AUTHOR]

Polymeric matrix composites are important to the advancement of industries such as the automobile and medicine industries. In this study, the silicon carbide (SiC) particle-reinforced polyamide12 (PA12) matrix composites were fabricated by selective laser sintering system as well as the pure PA12. The surface topographies, mechanical, and tribological properties were further examined. The results indicated that the friction and wear resistance of the composite were improved compared with the PA12 matrix. The compressive strength increased about 8.5%, shore D hardness increased about 6%. The friction coefficient decreased about 10%, the specific wear rate decreased 20% after adding silicon carbide 10% weight to PA12. The wear mechanisms were also discussed. The deformed asperities on the worn surface can withstand more tangential load, and therefore resulted in lower specific wear rate. It was found that the content of SiC particles on the surface were reduced after friction tests. According to the analysis of SEM, EDS, and FTIR results, the wear mechanisms were considered to be the abrasive and fatigue mode. This type of PA12 matrix composite might be a promising potential in marine and energy applications. [ABSTRACT FROM AUTHOR]

The aim of the research described in this paper is to analyse the synergistic effect of types of synthetic oil and their density on the value of the coefficient of friction (COF) of Ti-6Al-4V titanium alloy sheets. Lubrication performance of commercial synthetic oils (machine, gear, engine and hydraulic) was tested in a strip draw friction test. The friction tests consisted of pulling a strip specimen between two cylindrical fixed countersamples. The countersamples were placed in the simulator base mounted on a uniaxial tensile test machine. Due to the complex synergistic effect of different strip drawing test parameters on the COF, artificial neural networks were used to find this relationship. In the case of both dry and lubricated conditions, a clear trend was found of a reduction of the coefficient of friction with nominal pressure. Engine oil 10W-40 was found to be the least favourable lubricant in reducing the coefficient of friction of Grade 5 titanium sheets. The two main tribological mechanisms, i.e., galling and ploughing, played the most important role in the friction process on the test sheets. In the range of nominal pressures considered, and with the synthetic oils tested, the most favourable lubrication conditions can be obtained by using a type of oil with a low viscosity index and a high kinematic viscosity. [ABSTRACT FROM AUTHOR]

Two complementary approaches should be used for the full characterisation of friction pair components. The first approach consists of stereometric studies of machined as well as worn surface topography of the friction components with multiple measurement methods used. The second approach, tribometric studies, enables the tribological characteristics of the friction pair. This work presents the complete characterisation of polymeric pin and ceramic plate friction pair components based on studies with the use of three research instruments: an interference microscope, a scanning electron microscope and a tribological tester. The results of the studies showed that the same treatment conditions used for different but similar ceramic materials did not provide exactly the same characteristics of both the machined and worn surface topography. Moreover, the results showed that the material properties and machined surface topography of the ceramic component significantly affected the friction coefficient and linear wear as well as the wear intensity of the polymeric component. Connecting the two approaches, stereometric studies and tribometric studies, allowed for a better identification of the wear mechanism of the polymeric pin (i.e., abrasion, fatigue and adhesion wear) and the kind of wear products (polymeric material). [ABSTRACT FROM AUTHOR]

Here, staple carbon fiber fabric-reinforced polycarbonate (PC)- and epoxy (EP)-based composites with different impregnating resin levels were fabricated using a modified film stacking process. The effects of surface topographies and resin types on the tribological properties of stable carbon fabric composites (sCFC) were investigated. Friction and wear tests on the carbon composites were conducted under unlubricated sliding using a disk-on-disk wear test machine. Experimental results showed that the coefficient of friction (COF) of the sCFC was dominated by matrix type, followed by peak material portion (Smr1) values, and finalized with core height (Sk) values. The COF of composites decreased by increasing the sliding speed and applied pressure. This also relied on surface topography and temperature generated at the worn surface. However, the specific wear rate was strongly affected by resin impregnation. Partially-impregnated composites showed lower specific wear rate, whereas fully-impregnated composites showed a higher wear rate. This substantially increased by increasing the sliding speed and applied pressure. Scanning electron microscopy observations of the worn surfaces revealed that the primary wear mechanisms were abrasion, adhesion, and fatigue for PC-based composites. For EP-based composites, this was primarily abrasion and fatigue. Results proved that partially-impregnated composites exhibited better tribological properties under severe conditions. [ABSTRACT FROM AUTHOR]

In order to explore the relationship between the surface topography parameters and friction properties of a rough contact interface under fluid dynamic pressure lubrication conditions, friction experiments were carried out. The three-dimensional surface topography of specimens was measured and characterized with a profile microscopy measuring system and scanning electron microscope. The friction coefficient showed a trend of decreasing first and then increasing with the increase in some surface topography parameters at lower pressure, such as the surface height arithmetic mean Sa, surface height distribution kurtosis Sku, surface volume average volume Vvv, and surface center area average void volume Vvc, which are the ISO 25178 international standard parameters. The effects of surface topographic parameters on friction were analyzed and the wear mechanism of the worn surface was presented. The wear characteristics of the samples were mainly characterized as strain fatigue, grinding, and scraping. The results provide a theoretical basis for the functional characterization of surface topography. [ABSTRACT FROM AUTHOR]