Search

Porous cerium oxide (ceria) nanoparticles were prepared with and without manganese (Mn) by using the flash combustion technique. Samples with different loadings (Ce/Mn ratio ranged from 100 to 10) were prepared by using a one-step process and water only as a solvent. Moreover, citric acid was utilized as a fuel in an aqueous medium, and the overall synthesis mixture was dried at 100 °C overnight and then calcinated at 550 °C for 3 h. The obtained final solid product was characterized by inductively coupled plasma (ICP), X-ray powder diffraction (XRD), diffuse reflectance ultraviolet-visible spectroscopy (DR-UV-Vis), and scanning electron microscopy (SEM), which was coupled with Energy Dispersive X-Ray Analysis (EDX), high resolution transmission electron microscopy (HR-TEM), and photoluminescence (PL) analysis. The characterization data showed that Mn ions were totally incorporated into the framework of ceria up to the applied loading. Under visible light illumination, the photocatalytic activity of the prepared samples was tested in the decolorization reaction of methyl green (MG) dye (wavelength greater than 425 nm). The results showed that increasing Mn content improved the photocatalytic activity of ceria. The sample with a Ce/Mn ratio of 10 performed 1.8 times better than bare porous ceria. Finally, the reusability of the best-performing sample was investigated in four consecutive runs without treatment, and slight deactivation was monitored after the fourth run. [ABSTRACT FROM AUTHOR]

In this work, the photocatalytic hydrogen evolution from ammonia borane under near-infrared laser irradiation at ambient temperature was demonstrated by using the novel core-shell upconversion-semiconductor hybrid nanostructures (NaGdF4:Yb3+/Er3+@NaGdF4@Cu2O). The particles were successfully synthesized in a final concentration of 10 mg/mL. The particles were characterized via high resolution transmission electron microscopy (HRTEM), photoluminescence, energy dispersive X-ray analysis (EDAX), and powder X-ray diffraction. The near-infrared-driven photocatalytic activities of such hybrid nanoparticles are remarkably higher than that with bare upconversion nanoparticles (UCNPs) under the same irradiation. The upconverted photoluminescence of UCNPs efficiently reabsorbed by Cu2O promotes the charge separation in the semiconducting shell, and facilitates the formation of photoinduced electrons and hydroxyl radicals generated via the reaction between H2O and holes. Both serve as reactive species on the dissociation of the weak B-N bond in an aqueous medium, to produce hydrogen under near-infrared excitation, resulting in enhanced photocatalytic activities. The photocatalyst of NaGdF4:Yb3+/Er3+@NaGdF4@Cu2O (UCNPs@Cu2O) suffered no loss of efficacy after several cycles. This work sheds light on the rational design of near-infrared-activated photocatalysts, and can be used as a proof-of-concept for on-board hydrogen generation from ammonia borane under near-infrared illumination, with the aim of green energy suppliers. [ABSTRACT FROM AUTHOR]

This work investigates the degradation of the azo dye solochrome dark blue (SDB) by measurement of the photocatalytic, sonocatalytic and sonophotocatalytic activities, under low ultrasonic frequency (40 kHz) and UV-C (254 nm) light, using Mn-doped ZnS semiconductor quantum dots (Mn2+:ZnS Qds) as catalysts, prepared by a simple chemical precipitation procedure. In order to study the different morphological and optical crystal properties, various characterization techniques were used, such as high resolution transmission electron microscopy, scanning electron microscopy, energy dispersive X-ray analysis, X-ray diffraction, N2 adsorption-desorption at −196 °C and ultraviolet-visible spectroscopy. The average particle size of the semiconductor Qds was in the range of 3–4 nm. The optimal parameters affecting dye degradation, such as the catalyst loading, solution pH, time of irradiation, initial concentration of dye, dopant concentration, ultrasonic power and frequency effect were evaluated. The synthesized catalytic material exhibited a high activity for sonophotocatalytic degradation of SDB (89%), larger than that observed for sonocatalysis (69.7%) or photocatalysis (55.2%) alone, which was due to the improved electron-holes separation, formation of more reactive radicals and enhancement of the active surface area. Qds showed good stability and reusability after five repeated cycles. Finally, the degradation products were identified by liquid chromatography-mass spectrometry (LC-MS). [ABSTRACT FROM AUTHOR]

The proximity of the "post-antibiotic era", where infections and minor injuries could be a cause of death, there are urges to seek an alternative for the cure of infectious diseases. Copper nanoparticles and their huge potential as a bactericidal agent could be a solution. In this work, Cu and Cu oxide nanoparticles were synthesized by laser ablation in open air and in argon atmosphere using 532 and 1064 nm radiation generated by nanosecond and picosecond Nd:YVO4 lasers, respectively, to be directly deposited onto Ti substrates. Size, morphology, composition and the crystalline structure of the produced nanoparticles have been studied by the means of field emission scanning electron microscopy (FESEM), high resolution transmission electron microscopy (HRTEM), the energy dispersive spectroscopy of X-rays (EDS), selected area electron diffraction (SAED) and X-ray diffraction (XRD). The UV-VIS absorbance of the thin layer of nanoparticles was also measured, and the antibacterial capacity of the obtained deposits tested against Staphylococcus aureus. The obtained deposits consisted of porous coatings composed of copper and copper oxide nanoparticles interconnected to form chain-like aggregates. The use of the argon atmosphere contributed to reduce significantly the formation of Cu oxide species. The synthesized and deposited nanoparticles exhibited an inhibitory effect upon S. aureus. [ABSTRACT FROM AUTHOR]

Mesoporous TiO2 containing different potassium content was prepared from potassium titanate by mediating the pH value of the ion exchange, which was used as catalytic support to load NiMo for hydrodesulfurization of dibenzothiophene. The as-prepared samples were characterized by X-ray diffraction, N2 physical adsorption/desorption, temperature-programmed reduction, scanning electron microscope/energy dispersive X-ray mapping analysis, high resolution transmission electron microscopy, and pyridine-adsorbed Fourier transform infrared spectroscopy. The characterization results showed that NiO and MoO3 were well dispersed on mesoporous TiO2 with varying potassium content. A crystal NiMoO4 phase was formed on the TiO2 with relatively high potassium content, which could decrease the reduction temperature of oxidized active species. The evaluation results from the hydrodesulfurization displayed that as the potassium content of the catalyst increased, the dibenzothiophene conversion firstly increased and then slightly decreased when potassium content exceeded 6.41 wt %. By contrast, the direct desulfurization selectivity could continuously increase along with the potassium content of catalyst. Furthermore, the change in direct desulfurization selectivity of a TiO2-supported NiMo catalyst was independent of the reaction condition. The mesoporous TiO2-supported NiMo catalyst incorporated with potassium could have near both 100% of dibenzothiophene and 100% of direct desulfurization selectivity. According to the structure–performance relationship discussion, the incorporation of potassium species could benefit the formation of more sulfided active species on mesoporous TiO2. Moreover, excessive free potassium species may poison the active sites of the hydrogenation pathway. Both factors determined the characteristics of complete hydrodesulfurization of dibenzothiophene via a direct desulfurization pathway for potassium-incorporated mesoporous TiO2 supported NiMo catalysts. [ABSTRACT FROM AUTHOR]