In the current work, we fabricated gelatin–casein-based edible films (GC-EFs) crosslinked with gallic acid (GA). We analyzed the physiochemical characteristics, crystallinity, thermal stability, and surface properties of the EFs using Fourier-transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). It was found that the edible films possessed a semi-crystalline structure. Addition of GA enhanced the thermal stability of the edible films as well as the surface properties of the films. It was found that a higher concentration of GA (4–5% w/v) significantly improved the surface properties, observed in the surface and cross-sectional examination of SEM micrographs. EFs containing higher amounts of GA showed more compact and denser structures with smoother and more homogeneous surfaces than the control samples. In addition, swelling degree (SD), thickness, water solubility (WS), moisture content (MC), and water vapor permeability (WVP) were found to be low in EFs containing more GA concentration. Mechanical parameters revealed that the Young modulus (Ym) and tensile strength (TS) increased with a rise in GA concentration, and elongation at break (EB) reduced with a rise in GA concentration. In transparency and color analysis, it was observed that GA positively affected the transparency of the edible films. [ABSTRACT FROM AUTHOR]

Biopolymers-based composite edible films are gaining interest in the food packaging industry due to their sustainable nature and diverse biological activities. In the current study, we used sodium alginate (SA) and casein (CA) for the fabrication of composite film using the casting method. We also added orange oil to the edible film and assessed its impact on the biological, chemical, physical, and barrier properties of the films. The fabricated films were analyzed using X-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR). It was observed that CA–SA films loaded with 1.5% OEO had better visual attributes, and a further increase in oil concentration was not found to be as favorable. Mechanical assessment of the films revealed that CA–SA-OEO (1.5%) film showed lower puncture deformation and higher puncture force values. XRD data showed that all samples exhibited peaks at similar positions (21° of 2θ) with different intensities. In FTIR analysis, characteristic peaks of the film components (sodium alginate, casein, and orange oil) were reported at corresponding positions. The thermal stability of films was enhanced after the addition of the OEO (1.5%), however, a greater increase in OEO caused a decrease in the thermal stability, observed during TGA analysis. Moreover, the surface of the blank CA–SA film (FL1) was found to be rough (with cracks) compared to CA–SA films (FL2) containing 1.5% OEO. Additionally, FL2 was found to be relatively better than the other samples in terms of swelling degree (SD), thickness, water solubility (WS), oxygen permeability (OP), water vapor permeability (WVP), moisture content (MC), and transparency (T). [ABSTRACT FROM AUTHOR]