Search

In the aircraft industry, the high-strength aluminum alloys AA7075 and AA2024 are extensively used for the manufacture of structural parts like stringers and skins, respectively. Additive manufacturing (AM) of the AA7075-T6 aluminum alloy via friction stir deposition to build continuously multilayered parts on a substrate of AA2024-T4 aluminum has not been attempted so far. Accordingly, the present work aimed to explore the applicability of building multilayers of AA7075-T6 alloy on a substrate sheet of AA2024-T4 alloy via the additive friction stir deposition (AFSD) technique and to optimize the deposition process parameters. The experiments were conducted over a wide range of feed rates (1–5 mm/min) and rotation speeds (200–1000 rpm). The axial deposition force and the thermal cycle were recorded. The heat input to achieve the AFSD was calculated. The AA7075 AFSD products were evaluated visually on the macroscale. The microstructures were also investigated utilizing an optical microscope and scanning electron microscope (SEM) equipped with an advanced EDS technique. As well as the presence phases, the mechanical performance of the deposited materials in terms of hardness and compressive strength was also examined. The results showed that the efficiency of the deposition process was closely related to the amount of heat generated, which was governed by the feeding rate, the rotational speed, and the downward force. AA7075 defect-free continuously multilayered parts were produced without any discontinuity defects at the interface with the substrate at deposition conditions of 1, 2, 3, and 4 mm/min and a constant 400 rpm consumable rod rotation speed (CRRS). The additively deposited AA7075-T6 layers exhibited a refined grain structure and uniformly distributed fragment precipitates compared to the base material (BM). The gain size decreased from 25 µm ± 4 for the AA7075-T6 BM to 1.75 µm ± 0.41 and 3.75 µm ± 0.78 for the AFSD materials fabricated at 1 and 4 mm/min deposition feeding rates, respectively, at 400 rpm/min. Among the feeding rates used, the 3 mm/min and 400 rpm rod rotation speed produced an AA7075 deposited part possessing the highest average hardness of 165 HV ± 5 and a compressive strength of 1320 MPa. [ABSTRACT FROM AUTHOR]

The effects of La and Y on the microstructure and mechanical properties of cast Al-Si-Cu alloys were investigated by X-ray diffractometer (XRD), optical microscope (OM), and scanning electron microscope (SEM). The results indicated that the addition of La and Y had a great effect on the refinement of α-Al grains, the modification of eutectic Si phase, and the reduction of β-Al5FeSi length in Al-Si-Cu alloys. The A380 + 0.6 wt.% La/Y alloy exhibited the best microstructure and mechanical properties. The UTS and EI of the A380 + 0.6 wt.% La/Y alloy were 215.3 MPa and 5.1%, which were 22.9% and 37.8% higher than those of the matrix alloy, respectively. In addition, neither Al11La3 nor Al3Y generated by the addition of La and Y could not serve as the nucleation core of α-Al grains, so the grain refinement of α-Al originated from the growth limitation and constitutional supercooling. Since La and Y promote twinning generation and constitutional supercooling, the eutectic Si phase also changed from stripe-like to short fibrous or even granular and was significantly refined. Furthermore, thermodynamic calculations indicated that the Al11La3 phase was formed first and the Al3Y phase was generated on the Al11La3 phase. [ABSTRACT FROM AUTHOR]

FeCrMnNi high-entropy alloys prepared by vacuum induction melting were tested and characterized using an X-ray diffractometer, a scanning electron microscope, a micro hardness tester and a universal tensile tester to investigate the effects of the heat treatment temperature on the microstructure and mechanical properties of the alloys and the heat-resistant corrosion properties of FeCrMnNi alloy after annealing at 800 °C. It is a high-entropy alloy with a typical dendritic (DR) morphology. With the increase in the heat-treatment temperature, the amount of ultrafine precipitates with the BCC structure in the matrix increased; furthermore, the amount of ultrafine precipitates started to decrease at temperatures above 900 °C, and the DR structure gradually weakened. After heat treatment at temperatures above 800 °C, the alloy showed a tensile strength of 721.1 MPa and an elongation at break of 26.7%, which indicates improved strength of the alloy while maintaining good plasticity, mainly because a large amount of nanoscale particles precipitated between the DR structures and enabled fine grain strengthening. Therefore, an appropriate heat-treatment temperature helps to improve the overall mechanical properties of the high-entropy alloy. [ABSTRACT FROM AUTHOR]

In the present paper, the Mg-11Gd-2Y-1Zn alloys with different Al addition were fabricated by the gravity permanent mold method. The effect of Al content on microstructure evolution and mechanical properties of as-cast Mg-11Gd-2Y-1Zn alloy was studied by metallographic microscope, scanning electron microscope, XRD and tensile testing. The experimental results showed that the microstructure of as-cast Mg-11Gd-2Y-1Zn alloy consisted of α-Mg phase and island-shaped Mg3 (RE, Zn) phase. When Al element was added, Al2RE phase and lamellar Mg12REZn (LPSO) phase were formed in the Mg-11Gd-2Y-1Zn alloy. With increasing Al content, LPSO phase and Mg3 (RE, Zn) phase gradually decreased, while Al2RE phase gradually increased. There were only α-Mg and Al2RE phases in the Mg-11Gd-2Y-1Zn-5Al alloy. With the increase of Al content, the grain size decreased firstly and then increased. When the Al content was 1 wt.%, the grain size of the alloy was the minimum value (28.9 μm). The ultimate tensile strength and elongation increased firstly and then decreased with increasing Al addition. And the fracture mode changed from intergranular fracture to transgranular fracture with increasing addition. When Al addition was 1 wt.%, the maximum ultimate tensile strength reached 225.6 MPa, and the elongation was 7.8%. When the content of Al element was 3 wt.%, the maximum elongation reached 10.2% and the ultimate tensile strength was 207.7 MPa. [ABSTRACT FROM AUTHOR]

To enhance the mechanical properties (e.g., strength and elongation) of the face-centered cubic (fcc) α-phase in the Au-Cu-Al system, this study focused on the introduction of the martensite phase (doubled B19 (DB19) crystal structure of Au2CuAl) via the manipulation of alloy compositions. Fundamental evaluations, such as microstructure observations, phase identifications, thermal analysis, tensile behavior examinations, and reflectance analysis, have been conducted. The presence of fcc annealing twins was observed in both the optical microscope (OM) and the scanning electron microscope (SEM) images. Both strength and elongation of the alloys were greatly promoted while the DB19 martensite phase was introduced into the alloys. Amongst all the prepared specimens, the 47Au41Cu12Al and the 44Au44Cu12Al alloys performed the optimized mechanical properties. The enhancement of strength and ductility in these two alloys was achieved while the stress plateau was observed during the tensile deformation. A plot of the ultimate tensile strength (UTS) against fracture strain was constructed to illustrate the effects of the introduction of the DB19 martensite phase on the mechanical properties of the alloys. Regardless of the manipulation of the alloy compositions and the introduction of the DB19 martensite phase, the reflectance stayed almost identical to pure Au. [ABSTRACT FROM AUTHOR]