The purpose of this study was to compare the retention of fiber-reinforced composite (FRC) posts luted with either conventional or self-adhesive resin cement. The FRC posts and core resin were built up in bovine teeth. The posts were luted with standard etch-and- rinse cement, self-etch cement, or one of two self-adhesive cements. The samples were stored in water for 1 or 14 days or subjected to thermal cycling (TC). Retention value was measured with the pull-out test using a universal testing machine. Conventional adhesive resin cement yielded significantly greater retention than self-adhesive resin cement at 1 day. No significant difference was observed in retention among the adhesive systems tested at 14 days or after TC. During the early luting stage, self-adhesive resin cement yielded lower retention value than conventional resin cement. After 14 days storage or TC, retention was comparable to that with conventional resin cement. [ABSTRACT FROM AUTHOR]

The aim of this study was to evaluate the effect of reinforcing polyaromatic polyamide (aramid) fibers with various orientations on the flexural properties of denture base resin. Aramid fibers with four orientations of unidirectional, woven, non-woven and paper-type were pre-impregnated and placed at the bottom of a specimen mold. Heat-polymerized denture base resin was packed over the fibers and polymerized. A three-point bending test was performed using a universal testing machine at a crosshead speed of 5 mm/min. The flexural strengths and fiexural moduli of the unidirectional and woven groups were significantly higher than those of the control and other experimental groups. For the fiexural moduli, all experimental groups showed significantly higher reinforcing effects than the control group. In conclusion, the unidirectional group located perpendicular to the direction of the load was most effective in reinforcing the denture base resin, followed by the woven group. [ABSTRACT FROM AUTHOR]

The objective of this study was to evaluate change in color in experimental titanium-20mass% chromium (Ti-20Cr) alloy in an oral environment. Pure Ti and Ti-6Al-7Nb and Co-29Cr-5Mo alloys, as references to compare change in color, were prepared by casting. The cast specimen was mirror-polished. Each specimen was affixed to a palatal plate and the plate then worn by a volunteer for up to 300 h. A few specimens showed a change in color. These changes and the median values among the tested alloys were not significant. Larger amounts of carbon, nitrogen, and oxygen were observed in the discolored alloys than in the slightly-discolored alloys. The spectra of the constituent elements of the alloys revealed no corrosion. In conclusion, the experimental Ti-20Cr alloys showed a level of resistance to change in color and corrosion similar to that in commercially available Ti and Co-29Cr-5Mo alloys. [ABSTRACT FROM AUTHOR]

The aim of this study was to evaluate the reinforcing effects of three types of fibers at various concentrations and in different combinations on flexural properties of denture base resin. Glass (GL), polyaromatic polyamide (PA) and ultra-high molecular weight polyethylene (PE) fibers were added to heat-polymerized denture base resin with volume concentrations of 2.6%, 5.3%, and 7.9%, respectively. In addition, hybrid fiber-reinforced composite (FRC) combined with either two or three types of fibers were fabricated. The flexural strength, modulus and toughness of each group were measured with a universal testing machine at a crosshead speed of 5 mm/min. In the single fiber-reinforced composite groups, the 5.3% GL and 7.9% GL had the highest flexural strength and modulus; 5.3% PE was had the highest toughness. Hybrid FRC such as GL/PE, which showed the highest toughness and the flexural strength, was considered to be useful in preventing denture fractures clinically. [ABSTRACT FROM AUTHOR]

The aim of this study was to estimate the flexural properties of three kinds of experimental fiber-reinforced composite (FRC) posts and to evaluate their potential use as posts. Experimental FRC posts were fabricated with glass, aramid, and UHMWP fibers. Commercial FRC posts were used for comparison. A three-point bending test was performed at a crosshead speed of 1 mm/min. Experimental glass fiber posts showed significantly higher flexural strengths and moduli than aramid and UHMWP posts. Experimental UHMWP posts demonstrated superior toughness to the commercial posts. The glass fiber posts displayed stiff, strong and brittle features, while the UHMWP posts were flexible, weak and ductile. The flexural properties of the aramid posts fell between those of the glass and UHMWP posts. In conclusion, the glass fiber posts proved excellent in flexural strengths and moduli. However, the superior toughness of UHMWP fibers suggests the possibility of their use as posts in combination with glass fibers. [ABSTRACT FROM AUTHOR]

The mechanical properties of a series of binary Ti-Cr alloys were investigated. Chromium content ranged from 5 to 20 mass%. Dumbbell- and disk-shaped specimens of each alloy were obtained by casting for mechanical testing and microstructural observation. Yield strength (YS) at 0.2%, tensile strength (TS), elongation (EL) and Vickers hardness (Hv) were determined. The TS and YS of Ti-l5Cr were similar to those of Ti-20Cr at approximately 880 or 900 MPa and higher than those of cp-Ti by nearly 55%. Among all Ti-Cr alloys, Ti-l0Cr showed the lowest EL. At 50 μm below the surface, Hv ranged from 370 to 420. Addition of 15 or 20 mass% chromium to titanium yielded sufficient strength and relatively high elongation values. Judging from the results of the mechanical properties, the suitability of Ti-Cr alloys with 15 or 20 mass% chromium for use in dental prostheses. [ABSTRACT FROM AUTHOR]

The aim of this study was to evaluate the durability of unidirectional and bidirectional fiber-reinforced post systems under static and cyclic loading. Three prefabricated fiber posts with one of two core composite resins each or a post resin were used. Each specimen was subjected to a three-point bending test after cyclic loading (1000 times) by 0.1, 0.2 or 0.3 mm deflection. Under cyclic loading, flexure strength and elastic modulus tended to show a decrease with increase in deflection in the unidirectional fiber post specimens. No such tendency, however, was observed in the bidirectional fiber post specimen. In conclusion, use of a prefabricated fiber post in a post-and-core complex improved the flexural properties of the core composite resin, regardless of fiber direction. Although deterioration in flexural properties was observed with cyclic loading in the unidirectional fiber post specimens, no significant difference was observed in the bidirectional fiber post specimen. [ABSTRACT FROM AUTHOR]

The purpose of this study was to determine whether the brushing durability of a titanium dioxide coating on a polymethyl methacrylate (PMMA) substrate was improved by prior treatment with an acryloxypropyl trimethoxysilane-based agent. Titanium dioxide coatings were obtained by spray-coating substrates with or without prior treatment. Structure was investigated using IR, SEM, and an EPMA. Effect on durability against brushing was determined with a brush-wear test machine utilizing a commercial denture brush. A thin layer comprised of siloxane and TiO2 was formed on a PMMA substrate by prior treatment with an acryloxypropyl trimethoxysilane-based agent and spray-coating of TiO2. Prior treatment demonstrated improved stability against brushing, whereas the titanium coating was removed after less than 1x105 brushing cycles without prior treatment. This suggests that prior treatment with an acryloxypropyl trimethoxysilane-based agent would confer improved durability against brushing-induced stress on a TiO2 coating in its application to dentures. [ABSTRACT FROM AUTHOR]

This study examined the mechanical properties of roots combined with prefabricated fiber post. Three types of specimens were evaluated: (1) prefabricated fiber post alone (FP); (2) core composite resin with FP (CFP); and (3) root with CFP (RCFP). The volume fractions of the prefabricated fiber post in the core composite resin (FP/CFP ratio) were set to 0, 0.16, 0.22, 0.28, and 0.48. Bending test for FP and CFP, and diametral compression test for FP, CFP, and RCFP were carried out. The FP/CFP ratio showed no effect on the diametral tensile strength (DTS) of RCFP; and there were no significant differences in DTS with/without FP. The flexural strength of CFP increased with increase in FP/CFP ratio. The DTS of CFP declined in comparison with that of core composite resin only. [ABSTRACT FROM AUTHOR]

This study compared differences in discoloration and dissolution in several titanium alloys with immersion in peroxide- or fluoride-containing solution. Commercially pure titanium (CP-Ti) and six titanium-based alloys were used: Ti-0.15Pd, Ti-6Al-4V, Ti-7Nb-6Al, Ti-55Ni, Ti-10Cu, and Ti-20Cr. Two test solutions were prepared for immersion of polished titanium and titanium alloys: one consisting of 0.2% NaF + 0.9% NaCl (pH 3.8 with lactic acid) and the other of 0.1 mol/l H2O2 + 0.9% NaCl (pH 5.5). Following immersion, color changes were determined with a color meter and released elements were measured using ICP-OES. Discoloration and dissolution rates differed between the two solutions. In the hydrogen peroxide-containing solution, color difference was higher in Ti-55Ni and Ti-6Al-4V than in any of the other alloys, and that Ti-55Ni showed the highest degree of dissolution. In the acidulated fluoride-containing solution, CP-Ti, Ti-0.15Pd, Ti-6Al-4V, Ti-7Nb-6Al, and Ti-10Cu alloys showed remarkable discoloration and dissolution with immersion. On the contrary, Ti-20Cr alloy showed very little discoloration and dissolution in either solution. [ABSTRACT FROM AUTHOR]

Simvastatin acid (SVA) has been reported to stimulate bone formation by increasing expression of BMP-2 in osteoblasts. Due to their multi-functional characteristics and bioadaptability, cyclodextrins (CDs) are capable of forming inclusion complexes with many drugs by including a whole drug molecule inside their cavity. In the present study, we prepared SVA/CD inclusion complex solutions with different pH values. These were then used to determine their SVA release behavior after coating on titanium substrates, as well as to clarify the characteristics of SVA/CD complexes per se. Results showed that the lower the pH value of the solution, the lower the release kinetics of SVA. Besides, the amount of crystalline complexes in the coatings increased with decrease in pH. These results suggested that the release rate of SVA depended on two factors: pH of the solution and concomitant crystallinity of the coating. [ABSTRACT FROM AUTHOR]

The purpose of this study was to compare the retention force of FRC posts which were built up using direct and direct-indirect fabrication techniques with two fiber-reinforced core build-up systems (FibreKor and i-TFC). Posts were cemented in endodontically treated bovine single roots with resin cement using either direct or direct-indirect technique. Following which, the retention force of post-and-cores and fracture sites were examined. It was found that both the retention force and fracture site depended on the fabrication technique and resin cements. Post-and-cores built up with direct-indirect technique had greater retention force than those fabricated using direct technique. Fracture modes most frequently observed were adhesive failure at Resin/Dentin interface, a mixture of adhesive failures at Post/Resin and Resin/Dentin interfaces as well as cohesive failure of resin cements. Based on the results of this study, we concluded that when it comes to post-and-core build-up for endodontically treated tooth, the direct-indirect technique is more effective than the direct technique on the retention force of FRC posts. [ABSTRACT FROM AUTHOR]