Search

TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M (NH4)2SO4 solution in a temperature-controlled bath. The pH values of the suspension were 7, 8 or 9. According to the x-ray diffraction (XRD) analysis the anatase crystallite sizes were about 12 nm, which coincided with the average particle size revealed by scanning electron microscopy (SEM). The Raman scattering measurements have shown the presence of a small amount of highly disordered brookite phase in addition to dominant anatase phase with similar nanostructure in all synthesized powders. BET measurements revealed that all synthesized catalysts were fully mesoporous, except the sample synthesized with 0.07 M (NH4)2SO4 at pH=9, which had small amount of micropores. The photocatalytic degradation of herbicide Clomazone was carried out for both the pure active substance and as the commercial product (GAMIT 4-EC) under UV irradiation. The best photocatalytic efficiency was obtained for the catalyst with the largest specific surface area, confirming this parameter as crucial for enhanced photocatalytic degradation of the pure active substance and commercial product of herbicide Clomazone. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. III45018]

The titanium dioxide (TiO2) nanopowders were produced by sol-gel technique from tetrabutyl titanate as a precursor, varying the temperature оf calcination (from 500 to 550°C with the step of 10 °C). XRPD results have shown that all synthesized nanopowders are dominantly in anatase phase. The analysis of the shift and linewidth of the most intensive anatase Eg Raman mode confirmed the XRPD results and added the presence of small amount of highly disordered brookite phase in all samples. The analysis of pore structure from nitrogen sorption experimental data described all samples as mesoporous, with mean pore diameters in the range of 1.5 and 4.5 nm. Nanopowder properties have been related to the photocatalytic activity, tested in degradation of the textile dye (C.I. Reactive Orange 16). The sample calcined at temperature of 510°C showed the best photocatalytic performance. [Projekat Ministarstva nauke Republike Srbije, br. III45018 i br. OI171032]

Forsterite single crystals were grown by the Czochralski technique in air. The lattice parameters were determined by X-ray power diffraction. The IR and Raman spectra of pure and doped (V3+, V5+, and Ni4+) Mg2SiO4 single crystals were measured at room temperature. We studied the phonon properties and discussed the influence of dopants.

Raman spectroscopy has been used for characterization of commercial nanosized TiO2 powder with declared grain size of 5 nm. The Raman spectra measured in Stokes and anti-Stokes regime confirm the anatase phase of TiO2 powder in temperature range 25-1173K. It is shown that phonon-confinement (due to small grain size) and nonstoichiometry (caused by laser irradiation in vacuum) have a great influence on blueshift and broadening of the main Eg Raman mode at low temperatures, while the influence of the strong anharmonic effect becomes dominant at higher temperatures. The phonon confinement effect decreases due to the crystallite growth at temperatures above 673K.

A series of Ce1-xBaxO2-y (5£x£0.20) nanometric powders were synthesized by selfpropagating room temperature synthesis. XRD and Raman scattering measurements were used to characterize the samples at room temperature. All the samples are solid solutions with fluorite type structure with an average crystallite size about 5 nm. The redshift and asymmetric broadening of the Raman F2g mode can be well explained with combined confinement and strain effects because of the nanocrystalline powders nature. The appearance of the additional peaks at ~ 560 cm-1 and ~ 600 cm-1, are attributed to extrinsic and intrinsic O2- vacancies in ceria lattice. Raman spectra of temperature treated Ce0.80Ba0.20O2-d sample revealed the instability of this system.

Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy vibro-mill in a continual regime in air up to 300 minutes. Starting and modified ZnO samples were characterized using XRD, BET and TEM measurements. Optical properties of these samples were investigated by Raman and photoluminescence (PL) spectroscopy. The color of commercial ZnO powder was white while mechanically activated ZnO powder was dark yellow, indicating the presence of nonstoichiometry. In the Raman spectra of non-activated sample Raman modes of bulk ZnO were observed, while the spectra of modified samples point out structural and stoichiometric changes. The PL spectra of modified samples excited by 325 and 442 nm lines of a He-Cd laser show great difference with respect to the spectra of the original sample. This study confirms that change in the defect structure of the ZnO crystal lattice introduced by mechanical activation affects the optical properties of this material.

The infrared (IR) reflectivity of laser synthesized TiO2 nanopowder in the anatase phase with a small deviation from stoichiometry is reported. The samples were characterized by SEM, XRD and BET measurements as well as Raman and photoluminescence spectroscopy. Analysis of the far IR reflectivity spectrum of the nanopowder reveals a presence of a plasmon mode. The charge carriers resulting from the lattice defects, mainly oxygen vacancies, are responsible for this mode. The dielectric function in a factorized form with a plasmon contribution is used to model the IR reflectivity spectrum and a good agreement between theoretical and experimental results has been found.