The study involved the electrospinning of the copolymer poly(L-lactide-co-ε-caprolactone) (PLCL) into tubular grafts. The subsequent material characterization, including micro-computed tomography analysis, revealed a level of porosity of around 70%, with pore sizes of 9.34 ± 0.19 μm and fiber diameters of 5.58 ± 0.10 μm. Unlike fibrous polycaprolactone, the electrospun PLCL copolymer promoted fibroblast and endothelial cell adhesion and proliferation in vitro. Moreover, the regeneration of the vessel wall was detected following implantation and, after six months, the endothelialization of the lumen and the infiltration of arranged smooth muscle cells producing collagen was observed. However, the degradation rate was found to be accelerated in the rabbit animal model. The study was conducted under conditions that reflected the clinical requirements-the prostheses were sutured in the end-to-side fashion and the long-term end point of prosthesis healing was assessed. The regeneration of the vessel wall in terms of endothelialization, smooth cell infiltration and the presence of collagen fibers was observed after six months in vivo. A part of the grafts failed due to the rapid degradation rate of the PLCL copolymer.

Fibrous scaffolds are desired in tissue engineering applications for their ability to mimic extracellular matrix. In this study we compared fibrous scaffolds prepared from polycaprolactone using three different fabrication methods, electrospinning (ES), electro-blowing and melt-blown combined with ES. Scaffolds differed in morphology, fiber diameters and pore sizes. Mesenchymal stem cell adhesion, proliferation and osteogenic differentiation on scaffolds was evaluated. The most promising scaffold was shown to be melt-blown in combination with ES which combined properties of both technologies. Microfibers enabled good cell infiltration and nanofibers enhanced cell adhesion. This scaffold was used for further testing in critical sized defects in rabbits. New bone tissue formation occurred from the side of the treated defects, compared to a control group where only fat tissue was present. Polycaprolactone fibrous scaffold prepared using a combination of melt-blown and ES technology seems to be promising for bone regeneration. The practical application of results is connected with enormous production capacity and low cost of materials produced by melt-blown technology, compared to other bone scaffold fabrication methods.