The characteristics of UF resin prepared with concentrated formaldehyde were studied in this paper. With the molar ratio F/U = 1.1, the UF resin prepared with concentrated formaldehyde showed better mechanical properties than that with formalin. The 13C-NMR and FTIR results indicated that there were more methylene groups, ether groups and urons in a UF resin system prepared with concentrated formaldehyde than those in a normal UF resin. The differential scanning calorimetry and DMA results showed that the curing temperature of UF resin with concentrated formaldehyde was lower than that of a normal UF resin. UF resin with concentrated formaldehyde showed worse thermal stability and higher thermal decomposition temperature.

To develop a soy-based adhesive with good water resistance, non-toxic melamine–glyoxal resin (MG) prepared in the laboratory was used as a cross-linker of soy-based adhesive. The FT-IR and ESI-MS results showed that there was a reaction between melamine and glyoxal. The resulted –CH–OH– groups could be the possible reactive groups for the cross-linking of soy-based adhesive. The wet shear strength of soy-based plywood indicated that the water resistance of soy adhesive cross-linked by MG improved with respect to that with no cross-linker, although it was not good enough to satisfy the relative standard. With the optimized preparation procedures for plywood, specifically, press temperature 180 °C, press time 3 min and resin loading 280 g m−2, type I soy-based plywood could be prepared with a hybrid cross-linker, namely 12%MG + 2% epoxy resin (EPR). The DSC results showed that the reaction between soy-based adhesive and the hybrid cross-linker MG + EPR was very complex.