Vertical power devices require significant attention to their edge termination designs to obtain higher breakdown voltages without substantial increase in ON-state resistance. A simple edge termination structure for a GaN p-n diode is proposed, comprising a full layer lightly doped p-type GaN region underneath the higher doped ${p} +\!+$ contact layer. A TCAD model of the device is developed, and removal of the portions of ${p}$ ++ cap outside of the device active area in simulations is shown to increase the device blocking voltage capability. It causes the depletion width to increase in the lightly doped p-type layer and allows it to act similar to a junction termination extension (JTE). These predictions are validated empirically, resulting in a 52% measured increase in breakdown capability after selective removal of the ${p}$ ++ cap. This simple edge termination technique can be formed with only a single low-energy nitrogen implant or etching procedure, greatly increasing its manufacturability over more complex structures. Design optimization studies are pursued in TCAD to determine optimal parameter values for further improving breakdown performance. It is shown that the proposed edge termination technique can be employed to produce future high voltage vertical GaN devices without a significant gain in ON-state resistance and with wide tolerance to process variations. [ABSTRACT FROM AUTHOR]

GaN is a favorable martial for future efficient high voltage power switches. GaN has not dominated the power electronics market due to immature substrate, homoepitaxial growth, and immature processing technology. Understanding the impact of the substrate and homoepitaxial growth on the device performance is crucial for boosting the performance of GaN. In this work, we studied vertical GaN PiN diodes that were fabricated on non-homogenous Hydride Vapor Phase Epitaxy (HVPE) substrates from two different vendors. We show that defects which stemmed from growth techniques manifest themselves as leakage hubs. Different non-homogenous substrates showed different distribution of those defects spatially with the lesser quality substrates clustering those defects in clusters that causes pre-mature breakdown. Energetically these defects are mostly mid-gap around 1.8Ev with light emission spans from 450nm to 700nm. Photon emission spectrometry and hyperspectral electroluminescence were used to locate these defects spatially and energetically. [ABSTRACT FROM AUTHOR]

We report selective area n-type doping using ion implantation of Si into semi-insulating, C-doped GaN samples activated using both conventional rapid thermal annealing (RTA) and 30 atm N2 overpressure annealing. Implanted regions were tested for Si activation using Circular Transmission Line Measurements (CTLM), while linear and circular photoconductive switches (PCSS) in the unimplanted regions were used as a test vehicle to separate implanted Si dopant activation from leakage paths generated by N vacancy formation due to damage and decomposition during annealing. We observed that at an optimal temperature around 1060 °C, a low contact resistivity of $1\times 10^{-6}\,\,\Omega $ -cm2 was obtained while preserving the breakdown of the unimplanted regions. [ABSTRACT FROM AUTHOR]