\REBa2\Cu3\Ox (REBCO, RE = rare earth) coated conductors are expected to show high performance for superconducting applications because of their high current density and high mechanical strength. Fujikura has developed REBCO coated conductor over 570 A/cm width at 77 K, self field with over 800 m length. In addition, we have succeeded in developing a 5 T cryocooled REBCO magnet with a stored energy of 426 kJ. The magnet is composed of 24 pancake coils with an inner diameter of 260 mm, and the total length of the REBCO coated conductors is approximately 7.2 km. We confirmed that the REBCO magnet could be excited up to 5 T for 720 min 9 months after the fabrication of the magnet. It is important to validate the long-term operation test results of the REBCO magnets with larger diameters in order to use these conductors in practical superconducting applications. On the other hand, we have fabricated and evaluated a model magnet before we fabricated a 426 kJ cryocooled magnet. The model magnet is composed of 6 REBCO pancake coils and 18 “dummy coils” with an inner diameter of 260 mm and an outer diameter of 515 mm. The model magnet is about the same size and shape as the 426 kJ cryocooled magnet. We have confirmed that the calculated critical current (Ic) of the top pancake coil of the model magnet was in good agreement with the measured coil Ic from 30 to 77 K under the conduction-cooled conditions. In addition, we have evaluated the thermal runaway behavior of the model magnet under the conduction-cooled conditions. As a result, we have confirmed that the model magnet with a 0.3-mm-thick copper stabilizer had sufficient time to ramp down without degradation at 361 A transport current after the detected normal transition. [ABSTRACT FROM PUBLISHER]

REBCO coated conductors are expected high performance in superconducting applications because of their high current density and high mechanical strength. However, in order to use these conductors in superconducting applications, a technique is required for fabricating impregnated REBCO coils without degradation.In this work, we fabricated six pancake coils without degradation using wounded REBCO coated conductors. These conductors were laminated with a copper tape as a stabilizer, and were fabricated by the IBAD/PLD method. In addition, we evaluated the V-I characteristics and n-values of the coils in liquid nitrogen and compared the calculated and measured values for the critical current (Ic) of the REBCO coated conductors. The measured Ic of the coils were in good agreement with the calculated ones. Furthermore, we fabricated a stacked coil using an approximately 190 m long REBCO coated conductor and evaluated the stability of the stacked coil at 77, 60 and 50 K under conduction-cooled condition. The thermal runaway current of the stacked coil was 166.4 A, and the central magnetic field was 1.27 T at 50 K. [ABSTRACT FROM PUBLISHER]