High-pressure hydraulic fracture (HF) is an important part of the safety assessment of high concrete dams. A stress-seepage-damage coupling model based on the finite element method is presented and first applied in HF in concrete dams. The coupling model has the following characteristics: (1) the strain softening behavior of fracture process zone in concrete is considered; (2) the mesh-dependent hardening technique is adopted so that the fracture energy dissipation is not affected by the finite element mesh size; (3) four coupling processes during hydraulic fracture are considered. By the damage model, the crack propagation processes of a 1 : 40 scaled model dam and Koyna dam are simulated. The results are in agreement with experimental and other numerical results, indicating that the damage model can effectively predict the carrying capacity and the crack trajectory of concrete gravity dams. Subsequently, the crack propagation processes of Koyna dam using three notches of different initial lengths are simulated by the damage model and the coupling model. And the influence of HF on the crack propagation path and carrying capacity is studied. The results reveal that HF has a significant influence on the global response of the dam. [ABSTRACT FROM AUTHOR]

In this paper, 3D particulate scale modelling on the die compaction of DEM generated initial packings of both soft and hard particles was conducted by employing the multiparticle finite element method (MPFEM). The effects of initial packing structures as well as the compaction pressure on the macroscopic and microscopic properties of the whole powder mass and local structures were investigated. In addition, corresponding physical experiments were carried out for model validation. The results show that the compact obtained from the initial dense packing under vibration undergoes yielding stage earlier than that with natural initial packing (without vibration), and the relative density is much higher. Pores that are significantly smaller and with more uniform size and homogenous stress distribution are observed in the former case. Highest stress regions occur in most cases at a grain boundary with large curvature after deformation. Moreover, the high stress in the central part of both soft and hard particles during compaction is significantly reduced after pressure unloading, reaching a new force balance. In this case, the stress is concentrated mainly at the corners of the deformed particles, which creates the risk of cracking during subsequent sintering at either the contact region between particles or the corners. The numerical results are found to be in good agreement with those from physical experiments, confirming the robustness and reliability of the numerical model used in the simulations. [ABSTRACT FROM AUTHOR]