Solutions of cellulose diacetate (CDA) from two sources (cotton linters and wood pulp Floranier) were analysed in various solvents by size exclusion chromatography (SEC). Without special precautions, the SEC chromatograms presented three peaks — or prehumps — before the main polymer peak. The first prehump which could be eliminated by ultracentrifugation corresponded to microgels whose sugar composition was determined. These microgels were also investigated by electron microscopy, X-ray and electron diffraction analysis. They corresponded mainly to cellulose triacetate (CTA-II) in the case of CDA from cotton linters and a mixture of CTA-II and xylan diacetate (XDA) in the case of CDA from the wood pulp Floranier. The second and third prehumps could be attributed to ionic effects corresponding to the association of remaining sulfate groups on the CDA molecules with residual calcium. It was found that these ionic effects could be eliminated by the addition of LiBr or LiCl to the elution solvents. This led to chromatograms devoid of prehumps.

Xylose-rich polysaccharide fractions were isolated from cell walls of muskmelon (Cucumis melo L. cv. Cantaloup Charentais) stems. A xylan with a (1 4) linked backbone has been characterized as a component of these fractions. Two xylanases excreted by the fungus pathogen Colletotrichum lagenarium were able to degrade this substrate both after extraction and when it was included in the crude cell walls. The results suggest that the xylanases are involved in the parasitism of this pathogen.

Five different glucomannan samples were recrystallized from dilute solution. Depending on the experimental conditions, the crystals obtained could be identified as corresponding to the mannan I (anhydrous precipitate of more or less regular lozenge-shaped crystals) or mannan II (hydrated gel-forming pseudo-fibrillar precipitate). High-molecular-weight material, low temperature of crystallization, or a polar crystallization medium favored the mannan II polymorph, whereas a low-molecular weight, a high temperature of crystallization, and a crystallization medium of low polarity yielded the mannan I polymorph. Since the base-plane unit-cell dimensions are fairly constant with respect to variation of glucose, it is likely that isomorphous replacement of mannose by glucose occurs in glucomannan crystallization; the data also indicate that perfection of the glucomannan crystals was reduced in specimens having a high glucose:mannose ratio. The oriented crystallization of glucomannan on cellulose microfibrils was also studied under conditions where the mannan I polymorph was obtained. This gave shish-kebab structures that were characterized.