Search

This study evaluated the effect of the accelerated artificial aging (AAA) on feldspar ceramic strength and the reinforcing effect promoted by adhesive cementation with resin luting agent. One hundred twenty feldspar ceramic disks were obtained. Sixty disks were acid-etched, silanized, and coated with an experimental resin luting agent simulating the adhesive luting procedures. Four groups were created (n=30): uncoated ceramic (control group), uncoated ceramic submitted to AAA, ceramic coated with resin luting agent, and coated ceramic submitted to AAA. Biaxial flexural testing with ball-on-ring setup was carried out. Biaxial flexural strength (s bf , MPa), characteristic strength (s 0 , MPa), and Weibull modulus (m) were calculated for axial positions z=0 (ceramic surface) and z=−t2 (luting agent surface). Data of s bf at positions z=0 and z=-t2 were separately submitted to statistical analyses (a=0.05). The uncoated ceramic submitted to AAA had no significant difference in s bf and s 0 compared with the control group. Resin coating of the ceramic increased s bf and s 0 at z=0. The AAA increased the s bf and s 0 for the resin-coated ceramic specimens at z=0 and also the s 0 at axial position z=-t2. The structural reliability at z=0 and z=-t2 was not influenced by the variables tested. In conclusion, resin coating improved the mechanical strength of the feldspar ceramic. The AAA procedure was not effective in aging the uncoated or resin-coated feldspar ceramic specimens. Resumo Este estudo avaliou o efeito do envelhecimento artificial acelerado (EAA) na resistência da cerâmica feldspática e o reforço promovido pela cimentação adesiva com cimento resinoso. Cento e vinte discos de cerâmica feldspática foram obtidos. Sessenta discos foram condicionados com ácido, silanizados, e recobertos com um cimento resinoso experimental simulando os procedimentos de cimentação adesiva. Quatro grupos foram criados (n=30): cerâmica sem recobrimento (grupo controle), cerâmica sem recobrimento submetida ao EAA, cerâmica recoberta com cimento resinoso, cerâmica recoberta com cimento resinoso submetida ao EAA. O teste de resistência à flexão biaxial foi realizado utilizando o dispositivo pistão-anel. Resistência à flexão biaxial (s fb , MPa), resistência característica (s 0 , MPa), e módulo de Weibull (m) foram calculados para as posições axiais z=0 (superfície da cerâmica) e z=−t2 (superfície do cimento). Os dados de s fb em z=0 e z=−t2 foram submetidos a análises estatísticas separadamente (a=0,05). A cerâmica não recoberta submetida ao EAA não teve diferença significante na s fb e s 0 comparada com o grupo controle. O recobrimento com cimento resinoso da cerâmica aumentou a s fb e s 0 em z=0. O EAA aumentou a s fb e s 0 para os espécimes de cerâmica recobertos com cimento resinoso em z=0 e também a s 0 em z=−t2. A confiabilidade em z=0 e z=−t2 não foi influenciada pelas variáveis testadas. Concluindo, o recobrimento com cimento resinoso melhorou a resistência mecânica da cerâmica feldspática. O procedimento de EAA não foi efetivo em envelhecer os espécimes de cerâmica feldspática recobertos ou não com cimento resinoso.

This study evaluated retrospectively the association among occlusal, periodontal and implant-prosthetic parameters and marginal bone loss (MBL) around implants and survival rate at 5.7 ±3.2 years of follow-up after prosthetic loading. Eighty-two patients received 164 external hexagon implants. After the standard healing period (3 to 6 months), the implants were restored with single-tooth or up to three splinted crowns. All patients were followed according to a strict maintenance program with regular recalls and clinically evaluated by a calibrated examiner. The MBL measurements taken from standardized radiographs made at permanent crown placement (baseline) and after the last evaluation were calculated considering occlusal, periodontal and implant-prosthetic parameters. Veneer fractures and abutment loosening were not considered failure. Two implants failed during the follow-up period, resulting in a survival rate of 98.8%. Cox regression analyses showed MBL associated with non-working side contacts (p=0.047), inadequate anterior guidance (p=0.001), lateral group guidance involving teeth and implants (p=0.015), periimplant plaque index (p=0.035), prosthetic design (p=0.030) and retention (p=0.006). Inadequate occlusal pattern guide, presence of visible plaque, and cemented and splinted implant-supported restoration were associated with greater MBL around the implant. Resumo Este estudo avaliou retrospectivamente a associação entre os parâmetros oclusais, periodontais e implante-protéticos e perda óssea marginal (POM) ao redor de implantes e taxa de sobrevivência, em 5,7 ± 3,2 anos de acompanhamento após o carregamento protético. Oitenta e dois pacientes receberam um total de 164 implantes com hexágono externo. Após o período de cicatrização (3 à 6 meses), os implantes foram restaurados com coroa unitária ou até três coroas ferulizadas. Todos os pacientes seguiram um programa de manutenção rigoroso, com consultas regulares e avaliações clinicas realizadas por um examinador calibrado. As medições de POM obtidas de radiografias padronizadas realizadas na colocação da coroa permanente (baseline) e após a última avaliação foram calculadas considerando os parâmetros oclusais, periodontais e àqueles relacionados ao implante e prótese. Fratura na cerâmica de cobertura e afrouxamento do pilar não foram considerados falhas. Dois implantes falharam durante o período de acompanhamento, resultando em uma taxa de sobrevivência de 98,8%.A análise de regressão de Cox mostrou POM associado com contatos no lado de balanceio (p= 0,047), inadequada guia anterior (p=0,001), guia lateral em grupo envolvendo dentes e implantes (p=0,015), índice de placa visível em torno do implante (p=0,035), tipo de prótese (p= 0,030) e retenção (p=0,006). Guia de padrão oclusal inadequado, presença de placa visível e restaurações implanto-suportadas cimentadas e ferulizadas resultaram em maior POM ao redor do implante.