Search

Objective: To assess the effects of two polishing techniques on the surface roughness of a commercial and experimental dental ceramic for use in a chairside CAD-CAM system., Methods: A standard onlay was reproduced fifteen times in each of the two materials. Each stub was retained and examined using confocal microscopy in reflection mode. Five random samples of each were polished with Sof-Lex aluminium oxide discs, five polished with diamond impregnated polishing wheels and five left in the as-machined state. Surface roughness parameters were measured for each material group in each condition and statistical analyses carried out to determine the efficacy of the polishing techniques for each material., Results: The as-machined surfaces of both materials had a statistically similar surface finish. Polishing with Sof-Lex discs was effective at reducing surface roughness of both materials. Whilst the polishing wheels were effective in reducing surface roughness for the commercial material, there was no statistically significant difference in the surface roughness of the experimental material in the as-machined or wheel polished states., Significance: Although Sof-Lex discs were effective in reducing surface roughness of the two materials examined in this study, wheel polishing should not be used to reduce surface roughness of the experimental material. This will need to be taken into consideration in any future clinical studies of this material.

Objective: To test the null hypothesis that there is no color change when enamel porcelain thickness is changed and to evaluate the ability of a shade guide to prescribe chroma., Methods: Three shades (3M1, 3M2 and 3M3) were selected from a Vitapan 3D master shade guide. Five disk specimens were prepared for each shade, consisting of three layers (opacious dentin, dentin and enamel) at thicknesses of 0.6, 0.8 and 0.6mm, respectively. The color of each disk was measured using a spectrophotometer. Enamel porcelain was reduced in thickness to 0.3mm and porcelain disks were remeasured., Results: Reducing the enamel thickness of porcelain disk specimens significantly increased L) (p<0.05), b*, metric chroma and hue angle (p<0.001). For the three shades studied (3M1, 3M2 and 3M3) L* values were not significantly different (p>0.05) and chroma increased for 3M1 with the lowest chroma to 3M3 with the highest chroma, which is in line with the shade guide specifications. Although statistically significant (p<0.001) changes in hue angle between the three shades were small (less than 3 degrees overall). The difference in chroma between the three shades 3M1, 3M2 and 3M3 was greatest for the thin enamel layer than the thick enamel layer., Significance: A change in enamel thickness from 0.6 to 0.3mm resulted in a three-unit change in L* and metric chroma and a 4 degrees change in hue angle. A change in enamel porcelain thickness will have a greater effect on higher chromatic shades than those with lower chroma. The ability of the shade guide to prescribe chroma was demonstrated but this could be offset by an anomalous enamel thickness.

One hundred maxillary premolar teeth were randomly allocated to ten groups. Each group was restored with one of ten different restorative techniques. The teeth were stored in deionized water for 7d prior to longitudinal sectioning in a mesio-distal plane. Following sectioning, ten specimens from each group were chosen at random from the 20 available sections. The sectioned surfaces were polished using 600-grit SiC abrasive paper and etched for 10 s with 50% phosphoric acid to remove the smear layer produced by sectioning. Five tooth sections from the dentin bonding resin groups were allowed to dry at 20 degrees C for 24h. The glass ionomer-based groups were reimmersed in deionized water during this period. The remaining five sections from each group were replicated using an addition-cure vinyl polysiloxane impression material and an epoxy resin. A comparison was made of the sections and the replicas. All tooth specimens were sputter-coated with gold for 4 min and examined using a scanning electron microscope. Replicas were gold-coated for 3 min. Different tooth/restoration interfaces, associated with different materials, were observed. A marked difference between the replicas and tooth sections was observed for glass ionomer-based restorations but not for resin-based bonding systems. Representative samples of replicas and specimens are shown, and the significance of the observed differences is discussed.

The study aimed to determine the base/restoration combination which allowed the least microleakage in Class II cavities. One hundred premolar teeth were prepared with a standardized, minimal two-surface cavity and randomly ascribed to ten equal groups. The cavities were restored by use of one of ten different material/technique combinations. Restored teeth were sealed to within 1 mm of the restoration margins with nail varnish prior to the immersion of the crowns in 5% (buffered) eosin for 48 h. The teeth were then hemisected longitudinally, in a mesio-distal plane, through the midline of the restoration by means of a diamond disc with water coolant, and one half of each tooth was then photographed. The transparencies were examined by image analysis programmed to facilitate calculation of the percentage of the tooth/restoration interface and of the crown dentin exhibiting dye penetration. Light- and chemically-cured glass-ionomer-based restorations showed similar amounts of leakage when expressed as a percentage area of crown dentin. This was significantly (p less than 0.05) less than that shown by cavities both etched and bonded. Cavities restored without enamel etching or involving the use of a bonding system exhibited significantly (p less than 0.05) greatest leakage.