Search

Objective: Dentinal MMPs have been claimed to contribute to the auto-degradation of collagen fibrils within incompletely resin-infiltrated hybrid layers and their inhibition may, therefore, slow the degradation of hybrid layer. This study aimed to determine the contribution of a synthetic MMPs inhibitor (galardin) to the proteolytic activity of dentinal MMPs and to the morphological and mechanical features of hybrid layers after aging., Methods: Dentin powder obtained from human molars was treated with galardin or chlorhexidine digluconate and zymographically analyzed. Microtensile bond strength was also evaluated in extracted human teeth. Exposed dentin was etched with 35% phosphoric acid and specimens were assigned to (1) pre-treatment with galardin as additional primer for 30s and (2) no pre-treatment. A two-step etch-and-rinse adhesive (Adper Scotchbond 1XT, 3M ESPE) was then applied in accordance with manufacturer's instructions and resin composite build-ups were created. Specimens were immediately tested for their microtensile bond strength or stored in artificial saliva for 12 months prior to being tested. Data were evaluated by two-way ANOVA and Tukey's tests (alpha=0.05). Additional specimens were prepared for interfacial nanoleakage analysis under light microscopy and TEM, quantified by two independent observers and statistically analyzed (chi(2) test, alpha=0.05)., Results: The inhibitory effect of galardin on dentinal MMPs was confirmed by zymographic analysis, as complete inhibition of both MMP-2 and -9 was observed. The use of galardin had no effect on immediate bond strength, while it significantly decreased bond degradation after 1 year (p<0.05). Interfacial nanoleakage expression after aging revealed reduced silver deposits in galardin-treated specimens compared to controls (p<0.05)., Conclusions: This study confirmed that the proteolytic activity of dentinal MMPs was inhibited by the use of galardin in a therapeutic primer. Galardin also partially preserved the mechanical integrity of the hybrid layer created by a two-step etch-and-rinse adhesive after artificial aging., (Copyright (c) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.)

Objectives: The purpose of this study was to measure the contraction stress development of three flowable resin-composite materials (Grandio Flow, VOCO GmbH, Cuxhaven, Germany; Tetric Flow, Ivoclar Vivadent, Schaan, Liechtenstein; Filtek Supreme XT Flowable Restorative, 3M ESPE, ST. Paul, MN, USA) and an universal micro-hybrid composite resin (Filtek Z250, 3M ESPE, St. Paul, MN, USA) during photopolymerization with a halogen curing light, using a novel stress-measuring gauge., Methods: Curing shrinkage stress was measured using a stress-analyzer. Composites were polymerized with a halogen curing unit (VIP, Bisco Inc., Schaumburg, IL, USA) for 40s. The contraction force (N) generated during polymerization was continuously recorded for 180s after photo-initiation. Contraction stress (MPa) was calculated at 20s, 40s, 60s, 120s and 180s. Data were statistically analyzed., Results: Filtek Supreme XT Flowable Restorative exhibited the highest stress values compared to other materials (p<0.05), while the lowest values were recorded with Tetric Flow (p<0.05). Tetric Flow was also the only flowable composite showing stress values lower than the conventional composite Filtek Z250 (p<0.05)., Significance: Flowable composites investigated with this experimental setup showed shrinkage stress comparable to conventional resin restorative materials, thus supporting the hypothesis that the use of flowable materials do not lead to marked stress reduction and the risk of debonding at the adhesive interface as a result of polymerization contraction is similar for both type of materials.

Objective: Most of current dental adhesive systems show favorable immediate results in terms of retention and sealing of bonded interface, thereby counteracting polymerization shrinkage that affects resin-based restorative materials. Despite immediate efficacy, there are major concerns when dentin bonded interfaces are tested after aging even for short time period, i.e. 6 months., Methods: This study critically discusses the latest peer-reviewed reports related to formation, aging and stability of resin bonding, focusing on the micro and nano-phenomena related to adhesive interface degradation., Results: Most simplified one-step adhesives were shown to be the least durable, while three-step etch-and-rinse and two-step self-etch adhesives continue to show the highest performances, as reported in the overwhelming majority of studies. In other words, a simplification of clinical application procedures is done to the detriment of bonding efficacy. Among the different aging phenomena occurring at the dentin bonded interfaces, some are considered pivotal in degrading the hybrid layer, particularly if simplified adhesives are used. Insufficient resin impregnation of dentin, high permeability of the bonded interface, sub-optimal polymerization, phase separation and activation of endogenous collagenolytic enzymes are some of the recently reported factors that reduce the longevity of the bonded interface., Significance: In order to overcome these problems, recent studies indicated that (1) resin impregnation techniques should be improved, particularly for two-step etch-and-rinse adhesives; (2) the use of conventional multi-step adhesives is recommended, since they involve the use of a hydrophobic coating of nonsolvated resin; (3) extended curing time should be considered to reduce permeability and allow a better polymerization of the adhesive film; (4) proteases inhibitors as additional primer should be used to increase the stability of the collagens fibrils within the hybrid layer inhibiting the intrinsic collagenolytic activity of human dentin.