Search

Objectives: Oral prosthetic rehabilitation has been used for a long time to restore function and natural appearance; however, it is still one of the most challenging areas in dentistry due to its technical fabrication process and biological behavior. Considering the advantages of additive manufacturing technology, this study introduced the feasibility of developing a 3D printed resin-based composition modified with graphene nanoplatelets (GNPs) to improve properties., Methods: Acrylate-based resin was impregnated with different concentrations of GNPs (0.0-0.25 wt%), and then different aspects such as mechanical, physical, biological and antimicrobial were analyzed to evaluate the effectiveness. TEM and SEM were used to characterize GNPs and their existence within the resin. Surface topography and roughness were evaluated using AFM. The degree of conversion and composition were confirmed by FTIR. Mechanical properties were detected using bending strength, microhardness and nanoindentation. Biocompatibility and antimicrobial activities were assessed with oral fibroblast and Candida albicans (C. albicans), respectively. In addition, most of the measurements were performed repeatedly after 3 months of storage in artificial saliva to evaluate performance., Results: GNPs improved strength significantly at low concentrations ≤ 0.05 wt%, while the addition up to 0.25 wt% enhanced printed nanocomposite hardness and elasticity. The modification did not induce a toxic response, as its biocompatibility was within the recommended range of biomedical devices. Antimicrobial activity was of prominence, as GNPs showed an outstanding route of reducing C. albicans activity associated with filler proportion., Significance: The embedment of GNPs in 3D printed resin can become a key material for customized applications that require high antimicrobial, stiffness and strength properties., (Copyright © 2022 Elsevier Inc. All rights reserved.)

Objective: The aim of this study was to investigate the potential antimicrobial and cytotoxic effect of modified 3D printed resin with ZrO 2 nanoparticles, as long-term provisional restoration. In addition, the study involved artificial aging process for three months to observe stability of 3D printed resin., Methods: Functionalized ZrO 2 nanoparticles with γ-MPS were characterized using transmission electron microscopy, scanning electron microscope and Fourier-transform infrared spectroscopy. Dental resin was incrementally impregnated with γ-MPS modified nanoparticles at different concentrations (0, 1, 3, and 5 wt%). Specimens were printed, post-cured and placed in artificial saliva at 37  o C for 48 h or aged for 3 months. Discrepancy in composition and roughness were monitored using FTIR and AFM, respectively. Biocompatibility was evaluated using human oral fibroblasts. Antimicrobials capacity and biofilm adhesion were measured with Streptococcus mutans and Candida albicans., Results: The microscopic and spectroscopic analyses confirmed γ-MPS coating around ZrO 2 nanoparticles. The addition of nanoparticles (>1 wt%) significantly increased the surface roughness. Cytotoxicity results were in agreement with the recommended range of oral biomaterials standard. Moreover, the antimicrobial activity significantly improved with increasing the filler concentration. Despite the decrease in antimicrobial efficacy after 3 months of aging, modified resin revealed a critical ability to dominate biofilm formation., Significance: The addition of ZrO 2 nanoparticles showed significant antimicrobial capability of a 3D printed resin without inducing any cellular side effects. Thus, the modification of a 3D printed resin with ZrO 2 nanoparticles has a promising future in the dental field for fabricating long-term provisional restorations., (Copyright © 2022 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.)

Objective: The aim of this study was to synthesize and characterize reduced nano graphene oxide (RGO) and graphene nanoplatelets (GNPs) doped with silver nanoparticles (nAg) and to prepare an experimental dentin adhesive modified with RGO/nAg and GNP/nAg nanofillers for studying various biological and mechanical properties after bonding to tooth dentin., Methods: Nanoparticles were characterized for their morphology and chemical structure using electron microscopy and infrared spectroscopy. Experimental dentin adhesive was modified using two weight percentage (0.25% and 0.5%) of RGO/nAg and GNP/nAg to study its degree of conversion (DC), antimicrobial potential, and cytotoxicity. The effect and significance of these modified bonding agents on resin-dentin bonded interface were investigated by evaluating interfacial nanoleakage, micropermeability, nanodynamic mechanical analysis, micro-tensile bond strength (µTBS), and four-point bending strength (BS), RESULTS: Both 0.25% and 0.5% GNP/nAg graphene-modified adhesives showed comparable DC values to the commercial and experimental adhesive (range: 42-46%). The bacterial viability of the groups 0.25% and 0.5% GNP-Ag remained very low under 25% compared to RGO/nAg groups with low cytotoxicity profiles (cell viability>85%). Resin-bonded dentin interface created with GNP/nAg showed homogenous, well-defined hybrid layer and regularly formed long resin tags devoid of any microporosity as evidenced by SEM and confocal microscopy. The lowest nanoleakage and highest bending strength and µTBS was recorded for 0.25% GNP/nAg after 12 months of ageing. A significantly increased nanoelasticity was seen for all experimental groups except for control groups., Significance: The addition of 0.25% GNP/nAg showed optimized anti-biofilm properties without affecting the standard adhesion characteristics., (Copyright © 2021 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.)

Objective: This study investigated the effect of post curing light exposure time on the physico-mechanical properties and cytotoxicity of a 3D-printed PMMA-based denture material in comparison to a conventional heat-cured alternative as a control., Methods: 3D-printed specimens were fabricated followed by post-curing for 0, 5, 10 or 20 min at 200 W and light wavelength range of 390-540 nm. Heat-cured specimens were fabricated using a standard protocol. Specimens were placed in artificial saliva at 37 ℃ for 48 h (immediate groups) and 6 months (aged group), then evaluated flexural strength/modulus, fracture toughness, microhardness, and degree of conversion. Water sorption and solubility was assessed after 28 days. Flexural strength, flexural modulus, and fracture toughness were tested through three-point bending tests, while the surface hardness was tested using Vickers's test. Fractured specimens were viewed by scanning electron microscope (SEM). Cytotoxicity in term of cell viability was evaluated using human oral fibroblasts., Results: Flexural strength/modulus, fracture toughness and surface hardness significantly improved with the increase in light curing time up to 20 min. The same pattern of improvement was found with degree of conversion, water sorption, solubility, and cell viability. There was no significant difference (p < 0.01) between heat-cured material and 3D specimens post-cured for 20 min in term of flexural strength/modulus, surface hardness, and degree of conversion at the two-storage time points., Significance: Generally, the physico-mechanical properties of the 3D-printed denture base material improve as post curing time increases up to 20 min which exhibited comparable performance as the conventional heat-cured control., Competing Interests: Conflict of interest The authors report no conflict of interest., (Copyright © 2021 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.)

Objective: To characterize and investigate efficacy of loading functionalized ZrO 2 nanoparticles in 3-dimensional (3D) printed acrylate ester-based resin subjected to accelerated aging in artificial saliva. As well as to evaluate the effect of ZrO 2 nanoparticle volume fraction addition on mechanical and physical properties of printed composite., Methods: Functionalized ZrO 2 nanoparticles were characterized using TEM and Raman spectroscopy. 3D printed dental resin was reinforced, with ZrO 2 nanoparticles, in the concentration range (0-5wt.%). The resulted nanocomposites, in term of structure and physical/mechanical properties were evaluated using different mechanical testing, microscopic and spectroscopic techniques., Results: ZrO 2 based nanocomposite was successful and formed composites were more ductile. Degree of conversion was significant at the highest level with blank resin and 1wt.%. Sorption revealed reduction associated with volume fraction significant to neat resin, however solubility indicated neat and 4wt.% had the lowest significant dissolution. Vickers represented critical positive correlation with filler content, while nanohardness and elasticity behaved symmetrically and had the maximum strength at 3wt.% addition. In addition, 3wt.% showed the highest fracture toughness and modulus. Improvement of flexural strength was significantly linked to filler concentration. Overall properties dramatically were enhanced after 3 months aging in artificial saliva, especially degree of conversion, microhardness, nanoindentation/elasticity, and flexural modulus. However, significant reduction was observed with flexural modulus and fracture toughness., Significance: The outcomes suggest that the newly developed 3D printed nanocomposites modified with ZrO 2 nanoparticle have the superior potential and efficacy as long-term provisional dental restoration materials., (Copyright © 2021 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.)