Search

Polymeric carbon nitride-hydrogen peroxide adduct (PCN-H2O2) has been prepared, thoroughly characterised and its application for selective photocatalytic conversion of 5-hydroxymethylfurfural (HMF) to 2,5-furandicarboxaldehyde (FDC) in aqueous suspension has been studied. The PCN-H2O2 adduct is stable in aqueous suspension under UV and solar irradiation up to 100 °C. It is also stable up to 200 °C if heated in air, while at temperatures close to 300 °C its decomposition takes place. Based on the obtained characterisation data it has been proposed that H2O2 attaches to the non-polymerised carbon nitride species and to the heptazine nitrogen atoms, thus producing strong hydrogen bonding within the PCN-H2O2 adduct. The blockage of the surface amino-groups in PCN-H2O2 by H2O2 hinders the interaction of HMF with these sites, which are responsible for unselective substrate conversion. PCN-H2O2, although being less active, possesses a superior selectivity in natural solar light assisted oxidation of HMF to FDC reaching 80% with respect to its thermally etched PCN counterpart, which gives rise to a 40–50% selectivity. We believe that the exceptional performance of the applied photocatalyst in the selective photocatalytic conversion of HMF to a high added value FDC in a green solvent under natural illumination makes a significant contribution to the development of environmentally friendly technologies for biomass valorisation.

Two simple routes for the synthesis of a paper-TiO2 composite were tuned up and the efficiency of the resulting paper-TiO2 photocatalyst was investigated in the 2-propanol oxidation in gas phase. The first route involved the in-situ generation over the sheet of paper of a TiO2 layer starting from a solution of Ti (OBu)4 in tert-butanoliacetic acid, followed by hydrothermal treatment at 120 degrees C for 3 h. The sample was labelled as paper-TiO2 (H). The second approach was based on the adsorption on the paper of a ready-made suspension of titania nanoparticles (TiO2 sol), generated in autoclave at 140 degrees C and stable in acid medium at pH

Catalytic and photocatalytic 2-propanol dehydration to propene at atmospheric pressure and a temperature range of 60–120 °C were carried out in gas-solid regime by using bare and supported Keggin H 3 PW 12 O 40 (PW 12 ) and Wells-Dawson H 6 P 2 W 18 O 62 (P 2 W 18 ) heteropolyacids (HPAs). Binary materials were prepared by impregnation of the HPAs on commercial SiO 2 and TiO 2 . The Wells-Dawson was in any case more active than the Keggin heteropolyacid and the differences were enhanced when the supported samples were used. In particular, Wells-Dawson HPA supported on TiO 2 and under irradiation showed the highest activity. The HPA species played the key role both in the catalytic and photo-assisted reactions. The acidity of the cluster accounts for the catalytic role, whereas both the acidity and the redox properties of the HPA species were responsible for the increase of the reaction rate in the photo-assisted catalytic reaction. The estimated apparent activation energy resulted always lower for the photocatalytic process than for the catalytic one.

Commercial and home prepared bare and Pt-supported TiO2 samples were used as the photocatalysts for the aqueous photo-conversion of glucose at ambient pressure and temperature. Aerobic and anaerobic conditions were used to study the products of glucose degradation both in the liquid (arabinose, erythrose, gluconic acid, glucaric acid, fructose and formic acid) and gaseous (H2 and CO2) phases. The distribution of these molecules was different in the presence of the various powders, depending on the structural and physico-chemical properties of the materials, and Pt resulted essential for the anaerobic production of H2. The home prepared samples resulted more active than the commercial ones. The rutile and brookite polymorphs were the most active samples both for glucose conversion and H2 formation (about 1700 μmol of H2 were produced over 7 h of irradiation in the presence of Pt-brookite materials).

Strontium titanate-based perovskites have been prepared in the presence of Y and Co with the aim to substitute Sr and Ti, respectively, in the ST crystalline structure. The obtained samples have been characterized by XRD, Raman spectroscopy, FE-SEM, XPS and tested as photocatalysts in two gas-solid regime reactions: (i) 2-propanol complete mineralization and (ii) propene partial oxidation, using a system simulating solar irradiation. All the tested samples resulted active as photocatalysts but with significant differences. The lattice substitution of Sr by Y displays a beneficial effect on the 2-propanol photodegradation. Conversely, the partial presence of cobalt on the ST surface, as Co-oxide nanodispersed clusters with a dominant Co(II) phase, plays a substantial detrimental effect on the photo-degradation process of 2-propanol, but favours the photocatalytic partial oxidation of propene to propene oxide. (c) 2014 Elsevier Inc. All rights reserved.

Layered double hydroxides (LDH) containing zinc and aluminium within the brucite-like layers and carbonate as the interlayer anion have been used as precursors for the preparation of mixed metal oxides by calcination. Zinc oxide and the ZnAl 2 O 4 spinel were formed with different degree of crystallinity depending of two parameters, i.e., the Zn 2+ /Al 3+ molar ratio and the calcination temperature (500–800 °C) of the LDH precursor. A pure spinel phase was obtained to remove ZnO upon a basic post-treatment in NaOH solution of the samples calcined at 800 °C. All the samples were tested for the photodegradation of 2-propanol in gas–solid regime. All the samples resulted active as heterogeneous photocatalysts. The photocatalytic activity increased by increasing the Zn 2+ /Al 3+ molar ratio and the calcination temperature of the solids.

The present work reports the preparation of samples based on Millennium PC-500 TiO 2 loaded with different amounts of tungstophosphoric acid (up to 30% in weight) and their characterisation by means of different physicochemical techniques: powder X-ray diffraction, N 2 adsorption–desorption at −196 °C, transmission electron microscopy, UV–vis and FT-IR spectroscopies and thermogravimetric analyses. The acidity of samples was evaluated by FT-IR using pyridine as probe molecule, and the catalysts activity was tested for the photodegradation of 4-nitrophenol in aqueous solution and for the photo-oxidation of propan-2-ol in vapour phase. The results show a noticeable improvement (8 and 2.5 times faster in the photodegradation rate of 4-nitrophenol and propan-2-ol, respectively), in both regimes for these specific substrates, when tungstophosphoric acid is dispersed over the oxide up to a certain amount (20% in weight). A partial leaching of the polyoxometalate was also detected in solution for samples loaded with the largest amounts on this compound.

Liotta, L. F. Ousmane, M. Di Carlo, G. Pantaleo, G. Deganello, G. Marci, G. Retailleau, L. Giroir-Fendler, A.; Co3O4, CeO2 and Co3O4-CeO2 mixed oxides with Co/Ce nominal atomic ratio 0.1:5, prepared by co-precipitation method with sodium carbonate, were tested in the oxidation of propene under lean condition and the catalyst stability was checked by performing three consecutive heating-cooling cycles. Characterization of the textural properties were performed by surface area measurement BET, X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements. Among the Co3O4-CeO2 mixed oxides, Co3O4 (30 Wt%)-CeO2 (70 wt%) gives the best activity attaining full propene conversion at 250 degrees C. This sample is characterized by the presence of Co3O4 particles well dispersed and in good contact with ceria according to BET and XRD data and as evidenced by SEM micrographs. Oxygen temperature-programmed desorption (O-2-TPD) and C3H6-temperature-programmed reduction (C3H6-TPR) experiments were carried out in order to study the surface and bulk oxygen mobility and to correlate it to the activity. At temperature around 200 degrees C, O-2-TPD experiments showed the desorption of mobile surface oxygen species for the most active samples, Co3O4 and Co3O4 (30 wt%)-CeO2 (70 wt%). C3H6-TPR experiments for both of the oxides also evidenced a high reactivity at low temperature, especially, for Co3O4 (30 wt%)-CeO2 (70 wt%) giving at 345 degrees C an intense peak of CO2 formation. Conversely, the ceria sample showed by C3H6-TPR much less pronounced oxygen bulk mobility, starting to react with propene above 500 degrees C and forming only CO. In this case, the catalytic activity of ceria was explained in terms of formation of surface oxygen vacancies which are relevant to the propene oxidation in presence of gaseous oxygen. (c) 2008 Elsevier B.V. All rights reserved.