Abstract: The continuous highly aligned hybrid carbon nanofibers (CNFs) with different content of acid-oxidized multi-walled carbon nanotubes (MWCNTs) were fabricated through electrospinning of polyacrylonitrile (PAN) followed by a series of heat treatments under tensile force. The effects of MWCNTs on the micro-morphology, the degree of orientation and ordered crystalline structure of the resulting nanofibers were analyzed quantitatively by diversified structural characterization techniques. The orientation of PAN molecule chains and the graphitization degree in carbonized nanofibers were distinctly improved through the addition of MWCNTs. The electrical conductivity of the hybrid CNFs with 3wt% MWCNTs reached 26S/cm along the fiber direction due to the ordered alignment of MWCNTs and nanofibers. The reinforcing effect of hybrid CNFs in epoxy composites was also revealed. An enhancement of 46.3% in Young’s modulus of epoxy composites was manifested by adding 5wt% hybrid CNFs mentioned above. At the same time, the storage modulus of hybrid CNF/epoxy composites was significantly higher than that of pristine epoxy and CNF/epoxy composites not containing MWCNTs, and the performance gap became greater under the high temperature regions. It is believed that such a continuous hybrid CNF can be used as effective multifunctional reinforcement in polymer matrix composites. [Copyright &y& Elsevier]

Abstract: A kind of composite carbon nanofibers (CNF) containing bioactive glass (BG) nanoparticles was produced for bone regeneration by a combination of electrospinning and sol–gel techniques. To produce the BG, compounds such as calcium nitrate, triethyl phosphate and tetraethyl orthosilicate were used as precursors and hydrolyzed to form a sol–gel solution, which was then added to a polyacrylonitrile (PAN) solution in N,N-dimethylformamide. The resulting mixture was electrospun to form PAN nanofibers containing the BG precursors. Upon oxidation and carbonization, the PAN nanofibers and BG precursors transformed into continuous CNF embedded with BG nanoparticles (CNF/BG). Through this fabrication technique, several CNF/BG composites were obtained by controlling the feeding ratios of the different precursors giving rise to BG nanoparticles with various compositions (i.e. containing 70–90mol% of SiO2 component). In vitro biomineralization in a simulated body fluid and co-culture with MC3T3-E1 osteoblasts studies were performed to evaluate the osteocompatibility of the CNF/BG nanoparticle composites. When compared to pure CNF, the CNF/BG composites showed an improved ability to promote the in vitro formation of apatite and MC3T3-E1 proliferation, which was found to be dependent upon the composition of BG nanoparticles. [Copyright &y& Elsevier]