Search

Abstract Self-supporting 110-nm-thick tetrahedral amorphous carbon (ta-C) films with a multilayered structure were fabricated as a carbon film target for the laser-driven ion acceleration. The self-supporting ta-C films consisted of three layers with the thicknesses of 35 nm, 40 nm, and 35 nm thick, and the film density of 3.0 g/cm3, 2.7 g/cm3, and 3.0 g/cm3, respectively. The multilayered ta-C film was fabricated using the T-shape filtered arc deposition method on a Si substrate coated water-soluble material. Silk fibroin and dextran were used as the water-soluble material. The water-soluble material formed between a ta-C film and a Si substrate was dissolved, and then, the ta-C film released from the substrate. Thick single-layer ta-C films partially peeled off on the water-soluble material and broke during the dissolving process. Self-supporting ta-C films were obtained by scooping the released ta-C film on a perforated substrate. The laser was irradiated on the self-supporting ta-C films, and the ta-C film with a higher film thickness and/or film density showed a higher laser irradiation tolerance. Highlights • Fabrication of self-supporting 110-nm-thick tetrahedral amorphous carbon (ta-C) films • A sacrificial layer dissolution method is used for the fabrication. • Silk fibroin and dextran used as a sacrificial layer • The self-supporting films have a flat shape without wrinkles and cracks. • High laser irradiation tolerance with increasing thickness or density of the ta-C films [ABSTRACT FROM AUTHOR]

Abstract: A precise measurement has been made utilizing a stacked CR-39 detectors unit for laser-accelerated high intensity protons. The proton beams are derived from a thin polyimide target exposed to an high intense Ti:sapphire laser 8 J energy and 40 fs duration. The sample sets, stacked radiochromic film and CR-39 detectors covered with 13 μm aluminum filter, are irradiated under vacuum condition. By analyzing the etch pits on the last layer of CR-39 which recorded etchable tracks, the energies of each proton in high-energy region are evaluated more precisely than in the past. The residual ranges for each particle in the last layer has been obtained from etch pit growth curves with multi-step etching technique. The maximum energy of proton is 14.39 ± 0.05 MeV. This method allows us to measure the maximum energy of proton precisely, which can obtain high energy resolution with uncertainty ΔE = 0.1 MeV in the laser-driven particle acceleration experiment. [Copyright &y& Elsevier]

An inhomogeneous spatial distribution of laser accelerated carbon/oxygen ions produced via the hydrodynamic ambipolar expansion of CO 2 clusters has been measured by using CR-39 detectors. An inhomogeneous etch pits spatial distribution has appeared on the etched CR-39 detector installed on the laser propagation direction, while homogeneous ones are appeared on those installed at 45° and 90° from the laser propagation direction. From the range of ions in CR-39 obtained by using the multi-step etching technique, the averaged energies of carbon/oxygen ions for all directions are determined as 0.78 ± 0.09 MeV/n. The number of ions in the laser propagation direction is about 1.5 times larger than those in other directions. The inhomogeneous etch pits spatial distribution in the laser propagation direction could originate from an ion beam collimation and modulation by the effect of electromagnetic structures created in the laser plasma. [ABSTRACT FROM AUTHOR]