Search

Abstract: This paper discusses the effects of small amount of Al contamination (<0.1wt%) on high-temperature strength and microstructure of the 9Cr–ODS steel. Increasing Al concentration degraded the ultimate tensile strength as well as the 0.2% proof stress at 973K and 1073K accompanied by decreasing fraction of the elongated grain, i.e., residual-α ferrite acting as reinforcement phase. The decrease of residual-α ferrite proportion provided by increasing Al is contrary to general behavior of conventional steels. Computer simulation on ferrite to austenite phase transformation suggested that the fine oxide dispersion in the elongated ferrite could be attributable to the preferential partitioning of Ti and W in ferrite than in austenite at hot-extrusion process. [Copyright &y& Elsevier]

Abstract: In order to examine irradiation effect on creep rupture strength of Oxide Dispersion Strengthened (ODS) steel claddings, the in-pile creep rupture test was conducted using Material Testing Rig with Temperature Control (MARICO)-2 in the experimental fast reactor JOYO. Fourteen creep rupture events were successfully detected by the temperature change in each capsule and the gamma-ray spectrometry of the cover gas. Time to creep ruptures of six ODS steel specimens were identified by means of Laser Resonance Ionization Mass Spectrometry (RIMS), and no irradiation effect on creep rupture strength was confirmed within the irradiation condition in the MARICO-2 test. [Copyright &y& Elsevier]

Abstract: PbBr2 single crystals were grown by a vertical Bridgman method. The objective of this work is to examine the following two: (i) how the crystal quality is influenced by purification, (ii) how the crystal quality is influenced by growth rate. The following results were obtained. (1) The crystals grown from the materials of 99.99% and 99.999% purity were not transparent if they were not purified. On the other hand, a transparent crystal was obtained even from the material of 99.99% purity when it was refined by directional freezing as well as vacuum distillation. (2) It was found that very slow growth rate was needed to grow transparent crystals. [Copyright &y& Elsevier]

Abstract 9Cr-ODS steel claddings consisting of tempered martensitic matrix, showed prominent creep rupture strength at 1000 °C, which surpassed that of heat-resistant austenitic steels although creep rupture strength of tempered martensitic steels is generally lower than that of austenitic steels at high temperatures. The measured creep rupture strength of 9Cr-ODS steel claddings at 1000 °C was higher than that from extrapolated creep rupture trend curves formulated using data at temperatures from 650 to 850 °C. This superior strength seemed to be owing to transformation of the matrix from the α-phase to the γ-phase. The transient burst strengths for 9Cr-ODS steel were much higher than those for 11Cr-ferritic/martensitic steel (PNC-FMS). Cumulative damage fraction analyses suggested that the life fraction rule can be used for the rupture life prediction of 9Cr-ODS steel and PNC-FMS claddings in the transient and accidental events with a certain accuracy. [ABSTRACT FROM AUTHOR]

The growth of oxide particles in FeCrAl- oxide dispersion strengthened steel (ODSS) considering an accident condition of the light-water reactor at above 1500 K was studied by using a high-temperature annealing. Oxide particles grew from 9 nm to more than 50 nm as maximum at 1623 K for 27 h, with decreasing their number density in two orders of magnitude. Most of the oxide particles in 15Cr-7Al were identified as YAM or YAP, while the oxide particles in 15Cr-7Al-0.4Zr were identified trigonal Y 4 Zr 3 O 12 . Zr addition to 15Cr-7Al ODSS accelerated the growth of the oxide particles, which is quite contrary to the effect of Zr addition during sintering as suggested in the literature. The kinetics of coarsening was characterized by an equation of Ostwald ripening. The diffusion activation energies obtained in the present materials were quite larger than the conventional diffusion activation energy of Y in alpha-iron. Gibbs free energy of oxides should be considered to discuss the coarsening. [ABSTRACT FROM AUTHOR]

Abstract: The size and number density of oxide nanoparticles in 9Cr-oxide dispersion strengthened (ODS) steels with different concentrations of excess O, Ti and W are quantitatively determined using small-angle neutron scattering (SANS) and small-angle X-ray scattering (SAXS). Based on the difference of the SANS and SAXS intensity in absolute units, the “alloy contrast variation (ACV) method” has been used to determine the compositions of the oxide nanoprecipitates. The results indicate that the finest size and highest number density of oxide nanoparticles is obtained by suppressing the amount of excess O and increasing the amount of Ti. The ACV method indicates that the finest oxide nanoparticles have a chemical composition close to Y2Ti2O7. [Copyright &y& Elsevier]

Abstract: The effects of mechanical alloying (MA) conditions on oxygen contamination were investigated to establish the manufacturing technology of oxygen-controlled oxide dispersion strengthened (ODS) martensitic steel. High-temperature mechanical tests and microstructure observations were performed in oxygen-and-titanium-controlled steels in order to demonstrate high-temperature strength improvement using oxygen control. Oxygen content was drastically reduced by the purification of MA atmosphere, Ar gas. It was shown that the lower speed agitation at the beginning of MA was effective for the reduction of oxygen contamination because oxygen was mixed mainly at the beginning of mechanical alloying due to the imperfect replacement of Ar gas. Dense distribution of oxide particle and significant improvement in high-temperature strength were achieved by applying 99.9999wt% Ar in MA atmosphere and reducing oxygen contents. It was revealed that the merely increasing Y2O3 and titanium addition cannot improve the high-temperature strength. The excess oxygen is an important parameter for making oxide particles finely and densely distributed as well as improving high-temperature strength. [Copyright &y& Elsevier]