Search

Medium-entropy Zr–Nb–Ti (ZNT) alloys are being extensively investigated as load-bearing implant materials because of their exceptional biocompatibility and corrosion resistance, and low magnetic susceptibility. Nevertheless, enhancing their yield strength while simultaneously decreasing their elastic modulus presents a formidable obstacle, significantly constraining their broader utilization as metallic biomaterials. In this study, three medium-entropy ZNT alloys, i.e., Zr 45 Nb 45 Ti 10 , Zr 42.5 Nb 42.5 Ti 15 , and Zr 40 Nb 40 Ti 20 (denoted ZNT 10 , ZNT 15 , and ZNT 20 , respectively), were designed based on the miscibility gap in the ZNT phase diagram and prepared by annealing of cold-rolled ingots. Their microstructures, mechanical properties, wear resistance, corrosion resistance, magnetic susceptibility, and biocompatibility were systematically studied. Spinodal decomposition occurred in the cold-rolled ZNT 10 and ZNTi 15 after annealing at 650 °C for 2 h and resulted in nanoscale Zr-rich β 1 and (Nb, Ti)-rich β 2 phases, which significantly improved their yield strength and reduced their elastic modulus. The wear resistance of the alloys decreased with an increase in Ti content. Dense ZrO 2 , Nb 2 O 5 , and TiO 2 oxide layers were formed during the polarization process in Hanks' solution, which enhanced the corrosion resistance of the alloys. These ZNT alloys exhibited significantly lower magnetic susceptibility than medical Ti alloys. The ZNT alloys showed a cell viability of more than 94 % toward MG-63 cells after culturing for 3 d Overall, the spinodal ZNT 15 showed the best combination of mechanical properties, wear resistance, corrosion resistance, low magnetic susceptibility, and sufficient biocompatibility among the three alloys. This work reports on medium-entropy Zr–Nb–Ti (ZNT) alloys with heterostructure. Spinodal decomposition significantly improved their mechanical strength and reduced the elastic modulus of the alloys. The wear resistance of the ZNT alloys decreased with an increase in Ti content. Dense ZrO 2 , Nb 2 O 5 , and TiO 2 oxide layers were formed during the polarization process in Hanks' solution, which enhanced the corrosion resistance of the alloys. The ZNT alloys exhibited significantly lower magnetic susceptibility than medical Ti alloys. The ZNT alloys showed a cell viability of >94 % toward MG-63 cells after culturing for 3 d The results demonstrate that spinodal ZNT alloys have enormous potential as bone-implant materials due to their outstanding overall mechanical properties, high corrosion resistance, wear resistance, low magnetic susceptibility, and sufficient biocompatibility. [Display omitted] [ABSTRACT FROM AUTHOR]

Metallic biomaterials, such as stainless steels, cobalt–chromium–molybdenum (Co–Cr–Mo) alloys, and titanium (Ti) alloys, have long been used as load-bearing implant materials due to their metallic mechanical strength, corrosion resistance, and biocompatibility. However, their magnetic susceptibility and elastic modulus of more than 100 GPa significantly restrict their therapeutic applicability. In this study, spinodal Zr 60 Nb 40 , Zr 50 Nb 50 , and Zr 40 Nb 60 (at.%) alloys were selected from the miscibility gap based on the Zr–Nb binary phase diagram and prepared by casting, cold rolling, and aging. Their microstructure, mechanical properties, corrosion resistance, magnetic susceptibility, and biocompatibility were systematically evaluated. Spinodal decomposition to alternating nanoscale Zr-rich β 1 and Nb-rich β 2 phases occurred in the cold-rolled Zr–Nb alloys during aging treatment at 650 °C. In addition, a minor amount of α phase was precipitated in Zr 60 Nb 40 due to the thermodynamic instability of the Zr-rich β 1 phase. Spinodal decomposition significantly improved the mechanical strength of the alloys due to nanosized dual-cubic reinforcement. The Zr–Nb alloys showed an electrochemical corrosion rate of 94–262 nm per year in Hanks' solution because of formation of dense passive films composed of ZrO 2 and Nb 2 O 5 during the polarization process. The magnetic susceptibilities of the Zr–Nb alloys were significantly lower than those of commercial Co–Cr–Mo and Ti alloys. The cell viability of the Zr–Nb alloys was more than 98 % toward MC3T3-E1 cells. Overall, the spinodal Zr–Nb alloys have enormous potential as bone-implant materials due to their outstanding overall mechanical properties, extraordinary corrosion resistance, low magnetic susceptibility, and sufficient bicompatibility. This work reports on spinodal Zr–Nb alloys with heterostructure. Spinodal decomposition significantly improved their mechanical strength due to the nanosized dual-cubic reinforcement. The Zr–Nb alloys showed large corrosion resistance in Hanks' solution because of formation of dense passivation films composed of ZrO 2 and Nb 2 O 5 during the polarization process. The magnetic susceptibilities of the Zr–Nb alloys were significantly lower than those of commercial Co–Cr–Mo and Ti alloys. The cell viability of the Zr–Nb alloys was more than 98 % toward MC3T3-E1 cells. The results demonstrate that spinodal Zr–Nb alloys have enormous potential as bone-implant materials due to their outstanding overall mechanical properties, high corrosion resistance, low magnetic susceptibility, and sufficient biocompatibility. [Display omitted] [ABSTRACT FROM AUTHOR]