Search

Obtaining a desired quantity of retained austenite (RA) in press-hardened steels (PHSs) with a martensitic matrix is of great interest for the performance of safety critical components in vehicle bodies, as it improves the ductility/toughness without compromising strength. In this study, RA in a 1.7 GPa−PHS was stabilized via local chemical heterogeneity associated with Cr-enriched carbides. The Cr-rich carbide was introduced as a temporary reservoir of Cr and C into the pre-hot stamping microstructure by an annealing treatment. During the subsequent austenitization in hot stamping, the slow decomposition kinetics of Cr-rich carbide contributed to localized enrichment of Cr and C, which stabilized the austenite and resulted in a significant amount of RA with a core-shell structure after die quenching. Finally, sufficient RA ensured that the 1.7 GPa−PHS had a total elongation of ∼9.3%, which is about 43% higher than that of the 1.5 GPa−PHS grade 22MnB5 (∼6.5%). [Display omitted] [ABSTRACT FROM AUTHOR]

This study aimed to overcome the existing trade-off in strength–ductility in carbide free bainitic steel and improve ductility without compromising strength. Herein, we proposed a novel and simple method to obtain Mn-rich cementite via a pre-annealing (PA) treatment. PA promoted the partitioning of Mn into cementite particles. The Mn-rich cementite increased the Mn content in the retained austenite (RA) and enhanced the RA stability. Moreover, the initial number of Mn-rich cementite microstructures is positively correlated with RA. The effect of PA on the bainitic ferrite (BF) content was evaluated via comparison with the non-PA sample, revealing that the PA treatment promoted BF nucleation and increased the BF content. The PA-treated samples exhibited the optimal transformation induced plasticity (TRIP) effect and mechanical properties; in particular, the PA-3 sample (with 3 h treatment period) improved ductility and formability, with the total elongation increased from 11.9% in the non-PA sample to 18.0% in the PA-3 sample, corresponding to an increase of ∼51.2%. Additionally, the Erichsen cupping value increased from 7.52 mm in the non-PA sample to 9.78 mm in the PA-3 sample, corresponding to an increase of 30.1%. The overall applicability of PA for the improvement of formability of the carbide free bainitic steel is evident in all PA-treated samples. • The PA treatment is a novel and simple way to improve the ductility and formability of the material. • The PA promoted the partitioning of Mn into cementite particles. • The Mn-rich cementite results in Mn enrichment in the retained austenite (RA) and enhanced the RA stability. • The PA treatment reduced fresh martensite content and improved bainitic ferrite content. • Excellent strength and ductility in low-carbon bainitic steel was obtained via short-term PA treatment. [ABSTRACT FROM AUTHOR]

The effect of testing temperatures on wear-induced austenite-martensite transformation and the resultant wear resistance in metastable austenite-containing steels remains unclear. This issue is addressed in the current study, wherein the wear behavior of medium Mn steel was studied using a ball-on-disk sliding test at 20 °C, 0 °C, −50 °C, and −120 °C. The results demonstrate that the strain hardening and toughness enhancement produced by metastable austenite in austenite-rich steel greatly reduce wear volume at low temperatures. The dominant wear mechanism thereby changes from grooving and ploughing to cutting compared with martensitic steel. The wear resistance of austenite-rich steel depends significantly on the thermal and mechanical stabilities of metastable austenite. This study provides the basis for the development of novel wear resistant steels with relatively low initial hardness applicated at low temperatures. • Effect of testing temperatures on austenite-martensite transformation and resultant abrasion behavior are presented. • Austenite transforms into martensite during wear, and the wear-induced transformation is highly dependent on temperatures. • The enhanced strain hardening and toughening lead to the decreased wear volume at low temperatures inaustenite-rich steel. • Thermal and mechanical stabilities of austenite significantly affect the wear resistance of austenite-rich steel. [ABSTRACT FROM AUTHOR]