Search

In spite of many works on the biodegradation of textile dyes and phenolic compounds, we propose a new, inexpensive, environmentally friendly, and sustainable material based on electrospun fiber and immobilized laccase. The polycaprolactone (PCL)/polyethyleneimine (PEI) electrospun fibers were optimized and prepared by electrospinning technique according to the operational parameters like PCL concentration (12 wt%), PEI concentration (10 wt%), voltage (16 kV), needle tip-collector distance (20 cm), and injection speed (0.7 mL/h). Next, characterization studies were performed to investigate the morphology and structure of the electrospun fibers without and with laccase. The crude laccase was obtained by cultivating the white rot fungus T. trogii (TT), and T. versicolor (TV). The resulting electrospun fibers showed a smooth surface with a mean diameter of around 560 nm, and larger diameters were observed after laccase immobilization. According to the results, immobilization increased the stability properties of laccase such as storage, and operational. For instance, the residual activity of the PCL/PEI/ TT L and PCL/PEI/ TV L after 10 repeated cycles, was 33.2 ± 0.2% and 26.0 ± 0.9%, respectively. After 3 weeks of storage, they retained around 30% of their original activity. Moreover, the PCL/PEI/ TT L and PCL/PEI/ TV L were found to possess high decolorization yield to remove Orange II and Malachite Green textile dyes from solutions imitating polluted waters. Among them, the PCL/PEI/ TT L exhibited the highest decolorization efficiencies of Orange II and Malachite Green after 8 continuous uses at pH 5 and a temperature of 50 °C, reaching over 86%, and 46%, respectively. Moreover, PCL/PEI/ TT L and PCL/PEI/ TV L effectively degraded the 2,6-dichlorophenol phenolic compound at an optimal pH and temperature range and exhibited maximum removal efficiency of 52.6 ± 0.1% and 64.5 ± 7.6%, respectively. Our approach combines the advantageous properties of electrospun fiber material and immobilization strategy for the efficient use of industrial scale important enzymes such as laccase in various enzymatic applications. [Display omitted] • Electrospun fibers were produced and used for immobilization of fungal laccases. • Immobilized laccases showed 30% of operational stability for up to 10 reuse cycles. • The highest decolorization efficiency was 86% and 46% for OII and MG, respectively. • In addition, the highest removal efficiency of 2,6-DCP was about 64.5% after 5 h. [ABSTRACT FROM AUTHOR]

This study aims to present a simple and effective carrier matrix to immobilize laccase as opposed to complex and tedious immobilization processes and also to use it in the removal of textile dyes. For this purpose, Cobalt (Co) and Copper (Cu) based metal-organic frameworks (MOFs) were prepared and laccase was immobilized on two different MOFs via encapsulation. The characterization outcomes showed that laccase was well immobilized into MOF supports. Optimum pH and temperature were found for Lac/Co-MOF (pH 4.5 at 50 °C) and Lac/Cu-MOF (pH 5.0 at 50 °C). The Km (0.03 mM) and Vmax (97.4 μmol/min) values of Lac/Cu-MOF were lower than those of Lac/Co-MOF (Km = 0.13 mM, Vmax = 230.7 μmol/min). The immobilized laccases showed good reusability as well as improved resistance to temperature denaturation and high storage stability. For instance, the Lac/Co-MOF and Lac/Cu-MOF retained more than 58% activity after 4 weeks of storage at room temperature. Meanwhile, Lac/Co-MOF and Lac/Cu-MOF maintained 56.5% and 55.8% of their initial activity, respectively, after 12 reuse cycles. Moreover, thermal deactivation kinetic studies of immobilized laccases displayed lower k value, higher t 1/2 , and enhancement of thermodynamic parameters, which means better thermostability. Finally, the decolorization activities for the Lac/Co-MOF were 78% and 61% at the 5th cycle for Reactive Blue 171 and Reactive Blue 198, respectively. In conclusion, it can be inferred that the MOFs are more sustainable and beneficial support for laccase immobilization and they can be efficient for removing textile dyes from industrial wastes. [Display omitted] • Co-MOF, and Cu-MOF were suggested to immobilize laccase. • Immobilized laccases were produced by encapsulation. • The immobilized laccases exhibited enhanced thermal and storage stability. • The immobilized laccases maintained more than 55% activity after 12 cycles. • Reactive Blue 171 and Reactive Blue 198 were decolorized by immobilized laccases. [ABSTRACT FROM AUTHOR]