Quasi-static tensile test of UHMWPE fiber-reinforced composite laminate is challenging to perform due to low interlaminar shear strength and low coefficient of friction. Tensile tests proposed in the literature were conducted and limitations associated with each method led to the evolution of a new method. Tensile test of single-ply was realized as the best representative of tensile strength of a composite than tensile test of UHMWPE laminate. A fixture was developed for single-ply tests which increased friction and provided the mechanical constraint to slipping. The fixture is easy to fabricate and has provided repeatable results for eight grades of UHMWPE fiber-based (0/90) fabrics. Reported tensile strengths are in quite high range of 900–1500 MPa. • Ballistic composites are quite different from structural composites. • Tensile strength difficult to determine with standard methods. • All available methods tested for efficacy. • A new method is suggested for efficient testing. • Properties of wight commercial grades determined by suggested method. [ABSTRACT FROM AUTHOR]

• Vacuum compression moulded Basalt-Polyeteherimide (PEI) composites manufacturing. • Optimization of Basalt-PEI composite manufacturing moulding parameters. • Basalt-PEI composite under quasi-static and dynamic high strain rate loading. • Elastic recovery of Basalt-PEI composite can help in reflecting the blast wave. High temperature blast and ballistic resistant light weight fibre reinforced plastic composites are very much in demand. Accordingly, the present investigation is focused on the quasi-static and high strain rate behaviour of Basalt/Polyetherimide (PEI) composite. Nine different types of composite samples were fabricated by compression moulding. The moulding pressures and temperatures were varied in the range of 15–25 bars and 325 °C−375 °C, respectively. Quasi-static testing was done at the rate of 3 mm/min to establish the optimum moulding parameters. High strain rate compression tests in the strain rate range of 900/s−3200/s were performed on the optimum moulded composite specimens. High strain rate testing revealed that 40 layered Basalt/PEI composite moulded at 25 bar pressure and 350 °C attained highest stress of 932 MPa whereas, the same was found to attain 446 MPa under quasi-static loading conditons. Thus, establishing the rate depedency of Basalt/PEI composite. Damage studies revealed that Basalt/PEI undergoes brittle damage, typically resulting in shear plane angle of 42°−45°. SEM micrographs revealed brittle fibre failure and matrix free fibre bundles, indicating the importance of process parameter optimiation. [ABSTRACT FROM AUTHOR]