In this work the Bridgman crystal growth and scintillation properties of both undoped and Tl-doped Cs 3 Cu 2 I 5 are presented. This material is very attractive for gamma and X-ray detection applications, with a density of 4.53 g/cm3 and effective atomic number of 51.9. Undoped Cs 3 Cu 2 I 5 had a light yield of 41,500 photons/MeV, with an energy resolution of 4.4% at 662 keV. Thallium doping at 0.5 mol % resulted in a much-improved scintillation response, in which light yield increased to 98,200 photons/MeV and energy resolution reduced to 3.3% at 662 keV. The X-ray excited emission is centered at 442 nm for the undoped and 500 nm for the Tl-doped crystals. The undoped emission is broad, typical of excitonic emission, while thallium doping results in an even broader band with features of both the undoped and thallium defect-mediated emissions. • Transparent single crystals of undoped Cs 3 Cu 2 I 5 and Cs 3 Cu 2 I 5 (Tl) were grown via the Bridgman technique. • Phase purity was established via powder XRD analysis. • Undoped Cs 3 Cu 2 I 5 has 41,500 photons/MeV and 4.4% energy resolution at 662 keV. • Tl doping at 0.5 mol% improves light yield to 98,200 photons/MeV and energy resolution to 3.3%. [ABSTRACT FROM AUTHOR]

Inch-sized scintillating crystals are required for practical radiation detectors such as hand-held radio-isotope identification devices. In this work, a transparent and colorless 2-inch diameter KCa 0 . 8 Sr 0 . 2 I 3 : 0 . 5 mo % E u 2 + single crystal was grown by the vertical Bridgman method, and the scintillation properties of a ∅ 50 mm × 45 mm long sample were evaluated. The Eu 2 + 5 d 1 - 4 f emission under X-ray excitation is centered at 472 nm. Its scintillation decay time under 137 Cs source irradiation is 2 . 37 μ s , and the absolute light output is 51,000 ± 3000 photons/MeV. The energy resolution at 662 keV was evaluated for different orientations of the crystals with respect to the PMT, and the effect of 40 K background subtraction on energy resolution was evaluated. The performance of the packaged crystal was also investigated. [ABSTRACT FROM AUTHOR]

Europium doped strontium iodide (SrI 2 :Eu 2 +) is one of the cutting-edge halide scintillators for gamma-ray spectroscopy applications due to its low radioactive background, ultrahigh light yield (70,000–100,000 photons/MeV), and excellent gamma-ray energy resolution (2.6%–3% at 662 keV). In this work, we report an improvement in the scintillation characteristics of SrI 2 :Eu 2 + single crystals via tetravalent ion codoping, namely Zr 4 +. High quality SrI 2 :Eu 2 + single crystals codoped with 0, 0.05, 0.1, and 0.2 at.% Zr 4 + were grown by the Multi-ampoule Bridgman method. All of the as-grown crystals are transparent, crack-and inclusion-free. They have high optical quality with a transmittance of over 70%. The effects of Zr 4 + codoping on spectral properties and decay kinetics of SrI 2 :Eu 2 + under optical, and x- and gamma-ray excitation are studied. An enhancement of gamma-ray spectroscopic resolution from 2.8 to 2.5% at 662 keV and 5.4 to 5% at 122 keV is achieved upon Zr 4 + codoping with a slightly enhanced light yield of 95,000 photons/MeV. [ABSTRACT FROM AUTHOR]