Search

• The strength of chars was heightened significantly by the bi-component flame retardant (PODSE/APP). • 20 wt% PODSE/APP led to an 88.1 % and 87.0 % reduction in pSPR and TSP. • The char residue was substantially increased by 89.2 % with 20 wt% PODSE/APP. • PODSE/APP changed the internal structure of chars into honeycomb with higher expanded ratio. The intrinsic flammability and high smoke production are two major defects that epoxy resin (EP) must overcome during the practical application. However, few current studies have acknowledged in both fire resistance and smoke suppression performance, which is vitally interrelated with quality of char layers. Herein, a P/S-containing compounds (PODSE) was prepared via esterification and then supplemented with ammonium polyphosphate (APP) to develop an intumescent flame retardant for heightening the strength of char. With 20 wt% PODSE/APP, the peak of smoke produce rate (pSPR) and total smoke production (TSP) of EP3 reduced by 88.1 % and 87.0 %, respectively, indicative of superior smoke suppression performance. It attained a limited oxygen index (LOI) value of 40.0 % with V-0 rating during vertical burning test (UL-94) and the char residues at 700 °C increased from 15.8 % to 29.9 % compared with pure EP. More importantly, in order to figure out the reason for such highly-improved performance, the residual chars after cone calorimeter (CC) test were comprehensively investigated. The result showed that the internal chars of the samples modified by PODSE/APP exhibited honeycomb-like structure instead of irregular network structure of the one modified with single PODSE, endowing the char layers with higher expanded ratio and strength, which responded to excellent insulation effect. This finding provided theoretical and experimental basis for further exploration of P/S synergistic intumescent flame retardant. [ABSTRACT FROM AUTHOR]

With the specialization and diversification of the use environment of composite products, composite materials should have good comprehensive properties. Abiding by this target, we successfully prepared a transparent epoxy resin (EP) composite with flame retardancy, low smoke, enhanced toughness, high glass transition temperature by blending the flame-retardant POI synthesized in this work. POI was synthesized from phosphophenanthrene, vanillin and histidine, and the combination of these three raw meticulously selected endowed POI molecule with excellent versatility. EP composite modified with 10 wt% POI (EP/POI-10) obtained a limiting oxygen index (LOI) of 30.5% and received the V-0 grade (UL-94). The reduction of total smoke production by 78.1% via cone calorimeter tests was obtained. The impact strength of EP/POI-7 increased by 48.2% due to the energy dissipation of cracks from POI. The comprehensive analysis of the dual-phase revealed that the improvement of flame retardance was attributed to the joint action of the gaseous phosphorus free radicals quenching and the protecting of condensed coke. Moreover, EP/POI obtained high glass transition temperature as well as good transparency. [Display omitted] • A bio-based flame retardant molecule POI was synthesized. • High-performance composites of EP/POI with high T g , toughened and transparent were prepared. • The EP/POI showed a remarkable smoke suppression effect with a 78.1% reduction in TSP. [ABSTRACT FROM AUTHOR]

• A phosphaphenanthrene/benzimidazolone-containing flame retardant (POBDBI) was synthesized successfully. • POBDBI imparted excellent flame retardancy and smoke suppression to EP. • POBDBI exerted flame-retardant effect both in condensed phase and gaseous phase. A novel flame retardant POBDBI was generated by the reaction of p-dibenzaldehyde, 5-amino-2-benzimidazolinone and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO), and employed to epoxy resin. The structure of POBDBI was measured by FT-IR and NMR tests. Then flame-retardant EP was fabricated by using POBDBI as a flame-retardant. The thermal stability, flame-retardant performance and fire behavior were investigated by a serious of comprehensive instruments. Combustion tests show the flame-retardant performance of composite materials has been significantly improved. For example, the EP/POBDBI-1.0 with the phosphorus content of 1.0% accorded a V-0 rating and its limiting oxygen index (LOI) value increased to 36.5%. Besides, total smoke production (TSP), peak heat release rate (PHRR) and total heat release (THR) of EP/POBDBI-1.0 dropped significantly, and the corresponding values were decreased by 48.4%, 48.9% and 8.7%, respectively. At the same time, the composition, morphology of chars and gaseous products of POBDBI were studied by X-ray photoelectron spectroscopy (XPS), FT-IR, scanning electron microscope (SEM) and Py-GC/MS. These results presented that POBDBI could not only exerted free radical capture effect, but also enhanced the density of char residue. [ABSTRACT FROM AUTHOR]