Search

Commingled plant and polypropylene fibres (PP) nonwovens are attractive for automotive industry because of their interesting mechanical performances combined with good acoustical properties. This double function is achieved thanks of controlled porosity within the composite material. Indeed, from a same material, different functions (acoustic or mechanical) can be obtained by only varying the compaction rate during moulding. This study aims to highlight the necessity of a very large porosity volume fraction (60%) to reach good acoustic properties and understand the mechanical effect behind it. By combining tensile testing, acoustic absorption measurement and scanning electron imaging analysis, the microstructure, acoustic and mechanical properties have been investigated and were found to be intimately related to the material porosity content. As expected, when increasing porosity level from 5 to 60%, the material behaviour change and its tensile properties (modulus, strength and elasticity domain) drop drastically to a point where the material is no longer elastic (70% porosity) due to a modification of the material microstructure involving different failure mechanisms. [ABSTRACT FROM AUTHOR]

Abstract: In this work, a starch-based biopolymer was reinforced with flax strands. Composite materials at different fiber content were obtained by means of high-shearing mixing followed by injection molding processing. The evaluation of the mechanical properties gave a significant increase of the strength and stiffness of composites with the percentage of flax strands. The enhancement was analyzed in terms of compatibility and extension of the adhesion at fiber–matrix interface. The intrinsic mechanical properties of the reinforcement were measured and the behavior of the obtained composites was studied in terms of the modified rule of mixtures and the modified Halpin–Tsai equations. [Copyright &y& Elsevier]

Abstract: Thermoplastics reinforced by natural fibres are mainly used for fitting-up products in the automotive industry. The aim of this work is to study the tensile properties of natural fibre-biopolymer composites in order to determine whether or not, biocomposites may replace glass fibre reinforced unsaturated polyester resins. The materials used are flax fibre, polylactic acid (PLA), l-polylactide acid (PLLA), poly(3-hydroxylbutyrate) (PHB), polycaprolactone and starch thermoplastic (MaterBi® Z), poly(butylene succianate) (PBS) and poly(butylene adipate-co-terephtalate) (PBAT). The tensile properties of the flax fibres have already been determined [C. Baley, Analysis of the flax fibres tensile behaviour and analysis of the tensile stiffness increase, Comp Part A 2002;33:939–948]. The composites are manufactured using a film stacking technique. After studying the processing parameters, these are then adapted to each thermoplastic composites. Test samples are cut out from the composites to test their mechanical properties under tensile loading conditions. These tensile properties are then compared to those of similar polypropylene flax composites. Preliminary results show that the tensile properties are improved with the fibre volume fraction. The tensile strength and Young’s modulus of PLLA and PLA flax composites are greater than those of similar PP/flax fibre composites. The specific tensile strength and modulus of flax fibre/PLLA composite have proved to be very close to those of glass fibre polyester composites. [Copyright &y& Elsevier]