Search

The chitosan/polyvinyl Alcohol/zeolite electrospun composite nanofibrous membrane was fabricated for adsorption of methyl orange. The EDX, TGA and tensile test were carried out for the characterization of the membrane. The Young's Modulus of the nanofibrous membranes increased by more than 100% with the addition of zeolite to chitosan/PVA. The batch adsorption tests were conducted by varying the initial concentration of methyl orange, contact time and pH of the dye solution. UV-vis results showed that most of the dye was adsorbed within 6 min. An adsorption kinetic study was carried out using the pseudo-second-order kinetic model, Lagergren-first-order model and intra particle diffusion model. The adsorption kinetics obeyed the Pseudo second order model. The adsorption mechanism was analyzed using the Langmuir and Freundlich isotherm model. The experimental data fits well with the Freundlich model. The adsorption capacity of the membrane was 153 mg/g. Adsorption capacity was decreased with increasing pH value. The resulting nanofiber became less active over methyl orange after several runs., (Copyright © 2018 Elsevier Ltd. All rights reserved.)

In this study, effect of degree of deacetylation on property and adsorption capacity of chitosan/polyvinyl Alcohol electrospun membrane has been investigated. Resulting nanofibers were characterized by FESEM, FTIR, XRD, TGA, tensile testing, weight loss test and adsorption test. FESEM result shows, finer nanofiber was fabricated from 42h hydrolyzed chitosan and PVA blend solution. FTIR and XRD result showed a strong interaction between chitosan and polyvinyl alcohol. Higher tensile strength was observed for the nanofiber having 42h hydrolyzed chitosan. Blend solution of chitosan/PVA having low DD chitosan had higher viscosity. The nanofibrous membrane was stable in distilled water, acidic and basic medium. The isotherm study shows that the adsorption capacity (q m ) of nanofiber containing higher DD chitosan was higher for Cr(VI). In contrary, the membrane containing chitosan with lower DD showed the higher adsorption capacity for Fe(III) and methyl orange. Moreover, the effect of DD on removal percentage of adsorbate was dependent on the initial concentration of the adsorbate., (Copyright © 2017 Elsevier Ltd. All rights reserved.)

A chitosan/polyvinyl alcohol (PVA)/zeolite composite was fabricated in this study. The composite was analyzed through field emission scanning electron microscopy, Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), thermogravimetric analysis, and weight loss test. FTIR and XRD results revealed a strong interaction among chitosan, PVA, and zeolite. Weight loss test results indicated that the composite was stable in acidic and basic media. Congo red was removed through flocculation, and the removal rate was 94% at an initial concentration of 100mg/L for a dose of 1g/L. The removal rate of methyl orange was controlled by adsorption at an initial concentration of less than 100mg/L. Flocculation occurred at high concentrations. The removal rate was also 94% at an initial concentration of 500mg/L for a dose of 5g/L. The adsorption behavior of the composite for the removal of methyl orange and Cr(VI) was described by using a pseudo-second-order kinetic model. The adsorption capacity of the composite for Cr(VI) was 450mg/g. Therefore, the synthesized composite exhibited versatility during the removal of dyes and heavy metals., (Copyright © 2016 Elsevier Ltd. All rights reserved.)

In this study, chitosan/poly (ethylene oxide) nanofibres were fabricated at different chitosan:PEO weight ratio by electrospinning process. The effects of chitosan/PEO composition onto adsorption capability for Cu(II), Zn(II) and Pb(II) ions were studied. Formation of beadless fibres were achieved at 60:40 chitosan:PEO ratio. Average fiber diameter, maximum tensile strength and the specific surface area of the beadless fibres were found to be 115±31nm, 1.58MPa and 218m 2 /g, respectively. Chitosan/PEO composition that produced beadless fibres tend to possess higher hydrophilicity and maximum specific surface area. These characteristics lead the beadless fibres to the maximum adsorption capability. Adsorption equilibrium data were analysed by Langmuir and Freundlich isotherm. Freundlich isotherm showed the better fit with the experimental data and proved the existence of the monolayer adsorption conditions. The maximum adsorption capacity of the beadless fibres for Cu(II), Zn(II) and Pb(II) ions were found to be 120, 117 and 108mgg -1 , respectively., (Copyright © 2016. Published by Elsevier Ltd.)

Chitosan/PVA/Na-titanate/TiO2 composite was synthesized by solution casting method. The composite was analyzed via Fourier Transform Infrared Spectroscopy, X-ray diffraction, Field Emission Scanning Electron Microscopy, Thermal gravimetric analysis and water stability test. Incorporation of Na-titanate shown decrease of crystallinity for chitosan but increase water stability. However, the composite structure was deteriorated with considerable weight loss in acidic medium. Two anionic dyes, methyl orange and congo red were used for the adsorption test. The adsorption behavior of the composites were described by pseudo-second-order kinetic model and Lagergren-first-order model for methyl orange and congo red, respectively. For methyl orange, adsorption was started with a promising decolorization rate. 99.9% of methyl orange dye was removed by the composite having higher weightage of chitosan and crystalline TiO2 phase. On the other hand, for the congo red the composite having higher chitosan and Na-titanate showed an efficient removal capacity of 95.76%. UV-vis results showed that the molecular backbone of methyl orange and congo red was almost destroyed when equilibrium was obtained, and the decolorization rate was reaching 100%. Kinetic study results showed that the photocatalytic degradation of methyl orange and congo red could be explained by Langmuir-Hinshelwood model. Thus, chitosan/PVA/Na-titanate/TiO2 possesses efficient adsorptivity and photocatalytic property for dye degradation., (Copyright © 2016 Elsevier Ltd. All rights reserved.)