Search

Fe-based biodegradable materials as next-generation bone implants attract considerable attentions due to outstanding mechanical properties and favorable biocompatibility. However, their too slow degradation to match bone growth is a dilemma which urgently needs to be solved and thus is given special attentions in this review. Analyses and countermeasures to increase degradation rates of Fe-based materials are summarized. Meanwhile, detailed effects of accelerating degradation on biocompatibility and mechanical properties are also discussed. Subsequently, efforts about manufacturing mechanisms and methods of Fe-based biodegradable materials are consolidated and presented. Moreover, future outlook for Fe-based biodegradable materials is proposed. This review provides critical and valid information for development and breakthrough of Fe-based biodegradable materials toward orthopaedic applications.

Designing laboratory-scale degradation experiments for polymer-based biomaterials is crucial for the development of safe and functional implants, in particular regarding high molecular weight polyesters. Within this work, we compared accelerated degradation of solvent cast HMW-PLLA and HMW-P3HB films at 55 °C (16 weeks) with enzyme-associated (proteinase K and lipases) real-time degradation at 37 °C (108 weeks). During real-time degradation, PLLA showed mass loss up to 83%, in contrast to accelerated conditions, where no changes occurred. Moreover, we observed wave-shape development of crystallinity for PLLA and PHB for both degradation conditions applied, whereby PLLA χ value nearly doubled to up to 75%. These results were used to develop a correlation model based on molecular weight decrease and were furthermore discussed in light of a detailed literature review. In summary, real-time in vitro studies could be adapted to accelerated protocols providing the same limiting conditions such as molecular weight and initial crystallinity are given.

Freshly assembled proton exchange fuel cells (PEMFC) require conditioning to reach maximum power density. This process may last up to tens of hours and adds to the cost of commercial fuel cell technology. We present an accelerated conditioning procedure involving starving the cathode of oxidant. In single cells, this procedure conditions a membrane electrode assembly (MEA) within 40 min, without compromising durability. The performance and durability of MEAs conditioned using this technique are compared with US Department of Energy (DOE) and European Union (EU) harmonized protocols, and to an amperometric conditioning protocol. The time to reach peak power density using cathode starvation conditioning is

This study presents a comprehensive evaluation of the mechanical, micro-mechanical and physical properties of Reva Medical Fantom Encore Bioresorbable Scaffolds (BRS) subjected to a thermally-accelerated degradation protocol. The Fantom Encore BRS were immersed in phosphate buffered saline solution at 50 °C for 112 days with radial compression testing, nanoindentation, differential scanning calorimetry, gel permeation chromatography and mass loss characterisation performed at consecutive time points. In the initial stages of degradation (Days 0-21), the Fantom Encore BRS showed increases in radial strength and stiffness, despite a substantial reduction in in molecular weight, with a slight increase in the melt temperature also observed. In the second phase (Days 35-54), the radial strength of the BRS samples were maintained despite a continued loss in molecular weight. However, during this phase, the ductility of the stent showed a reduction, with stent fracture occurring earlier in the crimp process and with lower amounts of plastic deformation evident under visual examination post-fracture. In the final phase (Days 63-112), the load-bearing capacity of the Fantom Encore BRS showed continued reduction, with decreases in radial stiffness and strength, and drastic reduction in the work-to-fracture of the devices. Throughout each phase, there was a steady increase in the relative crystallinity, with limited mass loss until day 112 and only minor changes in glass transition and melt temperatures. Limited changes were observed in nano-mechanical properties, with measured local elastic moduli and hardness values remaining largely similar throughout degradation. Given that the thermally-accelerated in vitro conditions represented a four-fold acceleration of physiological conditions, these results suggest that the BRS scaffolds could exhibit substantially brittle behaviour after ∼ one year of implantation., (Copyright © 2021 Elsevier Ltd. All rights reserved.)

This study presents a systematic evaluation of the physical, thermal and mechanical performance of medical-grade semi-crystalline PLLA undergoing thermally-accelerated degradation. Samples were immersed in phosphate-buffered saline solution at 50 °C for 112 days and mass loss, molecular weight, thermal properties, degree of crystallinity, FTIR and Raman spectra, tensile elastic modulus, yield stress and failure stress/strain were evaluated at consecutive time points. Samples showed a consistent reduction in molecular weight and melting temperature, a consistent increase in percent crystallinity and limited changes in glass transition temperature and mass loss. At day 49, a drastic reduction in tensile failure strain was observed, despite the fact that elastic modulus, yield and tensile strength of samples were maintained. Brittleness increase was followed by rapid increase in degradation rate. Beyond day 70, samples became too brittle to test indicating substantial deterioration of their load-bearing capacity. This study also presents a computational micromechanics framework that demonstrates that the elastic modulus of a semi-crystalline polymer undergoing degradation can be maintained, despite a reducing molecular weight through compensatory increases in percent crystallinity. This study presents novel insight into the relationship between physical properties and mechanical performance of medical-grade PLLA during degradation and could have important implications for design and development of bioresorbable stents for vascular applications., (Copyright © 2021 The Authors. Published by Elsevier Ltd.. All rights reserved.)

The success of blood conduit replacement with synthetic graft is highly dependent on the architecture, and mechanical properties of the graft, especially for biodegradable grafts serving as scaffolds for in-situ tissue engineering. Particularly, the property of the radial compression recovery represents a critical to keep the patency during biointegration. Bi-component composite vascular grafts (cVG) made of polylactic acid (PLA) fabric and polycaprolactone (PCL) were developed with superior mechanical properties. In this research, the compressive and tensile properties of the prototypes were characterized when they were subjected to accelerated degradation. In addition, the prepared cVG were analyzed by scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and wide angle X-ray diffraction (WAXD) to illustrate the gradual loss of mechanical properties. The results demonstrated that the cVG retained the circular cross-section even through its tensile strength decreased during degradation. The cVG samples containing a high percentage of PLA fibers lost their tensile strength faster, while the samples with lower PLA percentage lost the compressive resistance strength more quickly. This unique fabric-based composite biodegradable vascular prosthesis with an outstanding radical compression recovery could be a good candidate for in-situ formation of tissue engineered vascular graft., (Copyright © 2017 Elsevier Ltd. All rights reserved.)