Search

The purpose of this study was to evaluate the effect of heat treatment on the anisotropy of the microstructure and mechanical properties of cobalt-chromium-molybdenum (Co-Cr-Mo) alloys fabricated by selective laser melting (SLM). Dumbbell samples were fabricated with the axes deviating from the build direction by 0° (0°-sample), 45° (45°-sample), or 90° (90°-sample) and were subjected to heat treatment at various temperatures (750, 900, 1050, or 1150 °C) for 6 h. In samples heat-treated at 750, 900, and 1050 °C, the microstructures exhibited columnar grains with a <001> fiber texture along the build direction, the same as in the as-built state. The mechanical properties showed anisotropy; the 0.2% offset yield strengths (YS) of the 0°-samples were lower than those of the 90°-samples, and the elongations of the 0°-samples were significantly higher than those of the 45°- and 90°-samples. By contrast, in samples heated to 1150 °C for 6 h, the anisotropic columnar grains completely disappeared, and equiaxed grains with random orientations were found in all samples, indicating that recrystallization had occurred. Moreover, the specific microstructures and texture generated during SLM disappeared. Regarding tensile properties, the initially strong anisotropy exhibited by the as-SLM samples was significantly reduced. Thus, heat treatment at the recrystallization temperature produced uniform equiaxed grains with random texture, which contributed to reducing the mechanical anisotropy of the SLMed Co-Cr-Mo alloys., (Copyright © 2019. Published by Elsevier Ltd.)

The aim of the study was to investigate the effect of post-heat treatment on the microstructures and fatigue strengths of Co-Cr-Mo (CCM) clasps prepared by selective laser melting (SLM). Clasp specimens and rod-shaped specimens were fabricated by SLM using CCM powders with different angulations (0°, 45°, and 90°). Two heat treatment conditions were used: 1 and 6 h at 1150 °C in an argon atmosphere followed by cooling in a furnace. Subsequently, the fatigue strength and microstructure were investigated. The results revealed that for the control group, the mean fatigue life was different when building angulations were changed as manifested by the control-90 specimen, which exhibited the highest fatigue life, followed by control-45 and then control-0. One-hour heat treated samples showed higher fatigue strength in all axes than the 0°- and 45°-axes control samples and lower fatigue strength than the 90°-axes control samples. The survival rate after heat treatment for 1 h exhibited no significant difference in all the axes. In terms of microstructure, after heat treatment, the samples showed homogeneous equiaxed grain and randomized texture in all angulations. Therefore, using a post-heat treatment can reduce the anisotropy effect on the microstructure and fatigue strength due to homogenized microstructure., (Copyright © 2019 Elsevier Ltd. All rights reserved.)

Selective laser melting (SLM) technology was recently introduced to fabricate dental prostheses. However, the fatigue strength of clasps in removable partial dentures prepared by SLM still requires improvement. In this study, we attempted to improve the fatigue strength of clasps by adding support structures for overhanging parts, which can generally be manufactured at an angle to be self-supporting. The results show that the fatigue strength of the supported specimens was more than twice that of unsupported specimens. Electron back-scattered diffraction analysis revealed that the supported specimens exhibited lower kernel average misorientation values than the unsupported specimens, which suggested that the support structure reduced the residual strain during the SLM process and helped to prevent micro-cracks led by thermal distortion. In addition, the supported specimens cooled more rapidly, thereby forming a finer grain size compared to that of the unsupported specimens, which contributed to improving the fatigue strength. The results of this study suggest that the fatigue strength of overhanging parts can be improved by intentionally adding support structures., (Copyright © 2017 Elsevier Ltd. All rights reserved.)

We aimed to investigate the fatigue strength of Co-Cr-Mo clasps for removable partial dentures prepared by selective laser melting (SLM). The Co-Cr-Mo alloy specimens for tensile tests (dumbbell specimens) and fatigue tests (clasp specimens) were prepared by SLM with varying angles between the building and longitudinal directions (i.e., 0° (TL0, FL0), 45° (TL45, FL45), and 90° (TL90, FL90)). The clasp specimens were subjected to cyclic deformations of 0.25mm and 0.50mm for 10(6) cycles. The SLM specimens showed no obvious mechanical anisotropy in tensile tests and exhibited significantly higher yield strength and ultimate tensile strength than the cast specimens under all conditions. In contrast, a high degree of anisotropy in fatigue performance associated with the build orientation was found. For specimens under the 0.50mm deflection, FL90 exhibited significantly longer fatigue life (205,418 cycles) than the cast specimens (112,770 cycles). In contrast, the fatigue lives of FL0 (28,484 cycles) and FL45 (43,465 cycles) were significantly shorter. The surface roughnesses of FL0 and FL45 were considerably higher than those of the cast specimens, whereas there were no significant differences between FL90 and the cast specimens. Electron backscatter diffraction (EBSD) analysis indicated the grains of FL0 showed preferential close to <001> orientation of the γ phase along the normal direction to the fracture surface. In contrast, the FL45 and FL90 grains showed no significant preferential orientation. Fatigue strength may therefore be affected by a number of factors, including surface roughness and crystal orientation. The SLM process is a promising candidate for preparing tough removable partial denture frameworks, as long as the appropriate build direction is adopted., (Copyright © 2016 Elsevier Ltd. All rights reserved.)

The aim of this study was to investigate the bond strength of dental porcelain and the preheated Zr-14Nb alloy, and compare this strength with that of titanium. White oxide layers, which were predominantly composed of monoclinic zirconia, were formed on the preheated sample groups, and exhibited a greater roughness than the control samples. At the metal-ceramic interface, a greater Nb diffusion range was observed than in the control samples. The bond strengths of the samples subjected to 20min preheating treatment were the lowest (33.6 ± 3.2 MPa), which may be ascribed to the formation of a brittle thick oxide layer under excessive heat treatment. The samples subjected to this heat treatment for 5 min exhibited the highest mean bond strength (43.7 ± 5.9 MPa), which was significantly higher than that of titanium (35.3 ± 3.5 MPa). Thus, the Zr-14Nb alloy is a promising candidate for fixed dental prosthesis, as long as the appropriate treatment conditions are adopted., (Copyright © 2015 Elsevier Ltd. All rights reserved.)