Search

Background/purpose: Additive manufacturing (AM) technology, such as selective laser melting (SLM), has been used to fabricate medical devices of Ti-6wt.% Al-4wt.%V (Ti6Al4V) alloys in dentistry. Strontium (Sr) has been shown to have the potential to treat osteoporosis. The aim of this study was to investigate the physicochemical and biological properties of strontium-containing coatings on selective laser melted Ti6Al4V (SLM-Ti6Al4V) substrate. Materials and methods: The disk of Ti6Al4V was prepared by SLM method. The strontium-containing coatings were prepared by micro-arc oxidation (MAO) in aqueous electrolytes. The surface topography, chemical composition, and phase of strontium-containing MAO (SrMAO) coatings were performed by scanning electron microscope (SEM), energy dispersive X-ray spectrometer (EDS), and thin film X-ray diffraction (TF-XRD), respectively. The apatite-forming ability of the MAO coatings was conducted in simulating body fluid (SBF), and the cell proliferation was determined by methylthiazoletetrazolium (MTT) assay. Results: The microstructure of SLM-Ti6Al4V displays acicular α-phase organization. The TF-XRD results indicated that the phase of SrMAO coating was anatase, rutile, and titanium. The calcium, phosphorus, and strontium were detected in the coatings by EDS. Using the SEM, the surface morphology of SrMAO coatings exhibited a uniform 3D porous structure. The SrMAO coatings could induce a bone-like apatite layer after immersion in SBF, and presented significantly higher cell proliferation than untreated specimens in in-vitro experiments. Conclusion: All findings in this study indicate that SrMAO coatings formed on SLM-Ti6Al4V surfaces exhibit a benefit on biological responses and thereby are suitable for biomedical applications.

Background/Purpose: Due to the general application of in vitro test, cell culture is generally selected to evaluate the cytocompatibility of devices and materials. The choice of test condition should depend on the probable site and clinical application. The oxygen content of human body could be estimated around 5%∼12%, and the oxygen level of healing bone fracture range from 0.8%∼3.8%%. However, materials for bone implant are traditionally evaluated under laboratory normoxia condition (21% O2) in vitro. The aim was to study the effect of oxygen level on osteoblast upon high stiffness titanium with different roughness. Methods: After sandblasted and acid-etched (SLA) process, we create titanium surfaces with four different roughness. The differentiation and proliferation of MC3T3-E1 osteoblast cultured on SLA-treated specimens were evaluated in designed chamber with oxygen level of 1%, 5%, 10%, 21%. Results: By scanning electron microscopy, all samples had sub-micro pit inside the micro-holes upon SLA-treated Ti disk surface. The decrease of oxygen level from 21% to 5% promoted osteoblast growth of SLA-treated specimens, but 1% O2 delayed cell proliferation. The surface roughness of specimens influenced osteoblast cell differentiation. The differentiation and proliferation ability of the cells upon SLA-treated specimens is proportional to oxygen level. Conclusion: Our results demonstrated that 5% O2 will easily discriminate osteoblasts responses on different SLA-treated specimens. These results suggest that hypoxia (5% O2) environment is better model for biological evaluation of bone-related materials.

Background/purpose: A challenge that arises with periodontal regeneration surgery has been associated with the future development of periodontal regeneration membrane to prevent gingiva and fibroblasts invade the wound and allow alveolar bone successfully regenerated. Materials and methods: Chitosan (CS) has the advantages of non-toxicity, biodegradation, biocompatibility, and has been widely used in wound dressings. A flexible film was made using polyvinyl alcohol (PVA) blending CS based thermosensitive hydrogel. Results: The proposed 2% PVA/CS hydrogel has the highest swelling ratio about 720% after 60 min incubation and keeps its area after 10 min incubation for surgery suture. The elastic modulus of 0%, 1%, 2%, and 4% PVA/CS hydrogel were 7.75 ± 1.96, 0.91 ± 0.16, 0.75 ± 0.21, and 0.37 ± 0.06 MPa, respectively. The maximum strain of 2% PVA/CS hydrogel was 101.00 ± 28.03 (%). After 8 weeks biodegradation, the remain weight of 2% PVA/CS hydrogel was 71.36 ± 0.79 (%). Conclusion: In vitro cytotoxicity tests were performed and demonstrated PVA/CS hydrogel significantly improving cell proliferation. This study realized a promising flexible film for periodontal regeneration membrane that can prevent the rapid growth of fibroblasts to invade the wound and be used for periodontal regeneration surgery.

Background/purpose: In orthodontic applications, NiTi wires are under continuous bending stress and exposed to fluctuations in temperature over long durations. The sensitivity of NiTi to temperature can have a considerable influence on its mechanical properties. This study investigated the effects of deflected NiTi wire, presented in stress-induced (detwinned) martensite microstructure, combined with thermal cycle on the microstructure and mechanical properties. Materials and methods: We tested four types of as-received orthodontic NiTi: (1) Nitinol Classic (3 M Unitek), (2) Sentalloy (Tomy), (3) 27 °C CuNiTi (Ormco) and (4) 40 °C CuNiTi (Ormco). Each group of specimens was subjected to three different testing conditions: (1) temperature fluctuations (5000 cycles) between 5 and 55 °C, (2) continuous three-point bending force and (3) combination of thermal cycling and bending stress. Results: The specimens that underwent thermocycling as well as loading exhibited a substantial narrowing in stress hysteresis, which may be attributed to crystallinity lower than that of as-received NiTi wires. Reduced crystallinity can manifest in a number of imperfections, such as dislocations and internal stress, as well as a less-organized structure. Micro X-ray diffraction (XRD) analysis revealed the existence of martensite phase in Sentalloy wires subject to thermal and stress conditions. Under loading conditions, stress-induced martensite of NiTi wires exposed to temperature fluctuations of 5–55 °C also induced cyclic changes in bending stress. In a simulated intra-oral environment, the stability of austenite↔martensite transformation decreased. Conclusion: This study determined that bending stress in conjunction with repeated temperature fluctuations can greatly affect the microstructure and mechanical properties of NiTi wires.

Abstract Background/purpose: The surface properties, such as hydrophilicity and functional OH groups, play an important role in bone fixation in vivo. In our previous study, the plasma treatments of large grit and acid etching (SLA) method produce functional OH groups on the rough surface. There is no report in discussing the integration between basic TiOH groups and bone-to-implant contact (BIC). The aim of this study was to evaluate the effect of the functional OH groups on the rough surface both in vitro and in vivo. Materials and methods: Functional hydroxyl groups were produced on a SLA-treated surface. The surface topography, roughness, wettability, and chemical composition were examined using various techniques. Twenty-four implants were inserted into the proximal tibia of four New Zealand white rabbits. The biological responses were measured in terms of histomorphometric analysis 4 and 8 weeks post-implantation. Results: The surface morphology and roughness were similar among all groups. However, the concentration of OH groups and hydrophilicity were found increased in the plasma treatment. The cell morphology in RF-plasma treated groups had more polygonal type and higher expression of actin and vinculin. The bone-to-implant contact (BIC) ratios of RF-200W were significantly higher than other groups (P