Search

Superhydrophobicity is a well-known wetting phenomenon found in numerous plants and insects. It is achieved by the combination of the surface's chemical properties and its surface roughness. Inspired by nature, numerous synthetic superhydrophobic surfaces have been developed for various applications. Designated surface coating is one of the fabrication routes to achieve the superhydrophobicity. Yet, many of these coatings, such as fluorine-based formulations, may pose severe health and environmental risks, limiting their applicability. Herein, we present a new family of superhydrophobic coatings comprised of natural saturated fatty acids, which are not only a part of our daily diet, but can be produced from renewable feedstock, providing a safe and sustainable alternative to the existing state-of-the-art. These crystalline coatings are readily fabricated via single-step deposition routes, namely thermal deposition or spray-coating. The fatty acids self-assemble into highly hierarchical crystalline structures exhibiting a water contact angle of ∼165° and contact angle hysteresis lower than 6°, while their properties and morphology depend on the specific fatty acid used as well as on the deposition technique. Moreover, the fatty acid coatings demonstrate excellent thermal stability. Importantly, this new family of coatings displays excellent anti-biofouling and antimicrobial properties against Escherichia coli and Listeria innocua, used as relevant model Gram-negative and Gram-positive bacteria, respectively. These multifunctional coatings hold immense potential for application in numerous fields, ranging from food safety to biomedicine, offering sustainable and safe solutions.

Human limb surrogates, of varying biofidelity, are used in the performance assessment of sports personal protective equipment (PPE). Such biofidelic surrogates have incorporated soft tissue simulants (silicones) and synthetic bone (short fibre filled epoxy). Testing surrogates incorporating realistic synthetic bone could help to further our knowledge of fracture trauma mechanics, and applications such as the effectiveness of sports PPE. Limb surrogates with embedded synthetic bone are rarely tested to fracture, mainly due to the effort and cost of replacing them. This paper proposes additive manufacturing of synthetic bones, with appropriate bone like fracture characteristics, potentially making them more accessible and cost effective. A Markforged® X7™ printer was used as it prints a base filament (Onyx™) alongside a continuous strand of reinforcement (e.g., carbon fibre). The properties of specimens from this printer vary with the type, volume fraction and position of reinforcement. Bar specimens (10 × 4 × 120 mm) with varying amounts of carbon fibre reinforcement were printed for three-point bend testing to determine the feasibility of achieving mechanical properties close to compact bone (bending modulus of ∼15 GPa, bending strength of ∼180 MPa). Bending strength for the various bar specimens ranged from 32 to 378 MPa, and modulus values ranged from 1.5 to 25.8 GPa. Based on these results, four 140 mm long oval shaped cylindrical specimens of ø14 and ø16 mm were printed to represent a basic radius bone model. Three-point bend testing of these bone models showed similar bending modulus (3.8 to 5.3 GPa vs. 3.66 to 14.8 GPa) to radius bones reported in the literature, but higher bending strength (147 to 200 MPa vs. 80.31 ± 14.55 MPa).