Search

Ligaments and tendons are comprised of aligned, crimped collagen fibrils that provide tissue-specific mechanical properties with non-linear extension behaviour, exhibiting low stress at initial strain (toe region behaviour). To approximate this behaviour, we report fibrous scaffolds with sinusoidal patterns by melt electrowriting (MEW) below the critical translation speed (CTS) by exploitation of the natural flow behaviour of the polymer melt. More specifically, we synthesised photopolymerizable poly(L-lactide-co-ε-caprolactone-co-acryloyl carbonate) (p(LLA-co-ε-CL-co-AC)) and poly(ε-caprolactone-co-acryloyl carbonate) (p(ε-CL-co-AC)) by ring-opening polymerization (ROP). Single fibre (fØ = 26.8 ± 1.9 µm) tensile testing revealed a customisable toe region with Young's Moduli ranging from E = 29 ± 17 MPa for the most crimped structures to E = 314 ± 157 MPa for straight fibres. This toe region extended to scaffolds containing multiple fibres, while the sinusoidal pattern could be influenced by printing speed. The synthesized polymers were cytocompatible and exhibited a tensile strength of σ = 26 ± 7 MPa after 10 4 cycles of preloading at 10% strain while retaining the distinct toe region commonly observed in native ligaments and tendon tissue., Statement of Significance: Damaged tendons and ligaments are serious and frequently occurring injuries worldwide. Recent therapies, including autologous grafts, still have severe disadvantages leading to a demand for synthetic alternatives. Materials envisioned to induce tendon and ligament regeneration should be degradable, cytocompatible and mimic the ultrastructural and mechanical properties of the native tissue. Specifically, we utilised photo-cross-linkable polymers for additive manufacturing (AM) with MEW. In this way, we were able to direct-write cytocompatible fibres of a few micrometres thickness into crimp-structured elastomer scaffolds that mimic the non-linear biomechanical behaviour of tendon and ligament tissue., (Copyright © 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

Numerous peptide drugs require continuous and local delivery to obtain optimum therapeutic effect. Herein, we describe the incorporation of a model peptide drug, vitamin B12, as well as goserelin acetate, in biodegradable elastomer cylinders through photo-cross-linking. The elastomer was prepared from acrylated star-poly(epsilon-caprolactone-co-D,L-lactide). Release was manipulated through the incorporation of poly(ethylene glycol) diacrylate (PEGD) into the network at concentrations up to 30% (w/w). The PEGD in the network caused rapid swelling that remained constant throughout the release period. The degree of swelling was low, ranging from 10 to 45% (w/w), and increasing as the PEGD content increased. Release proceeded with a minimal initial burst, and extended periods of nearly constant release, ranging from approximately 5 to 70% mass fraction released, were obtained. The release rate was independent of particle size and increased as the cylinder diameter decreased, as the amount of PEGD increased, as the molecular weight of PEGD increased, and as the agent loading increased. Moreover, goserelin acetate, which has a comparable diffusivity but greater aqueous solubility, was released at a greater rate than vitamin B12. This release behavior is explained as a balance between agent dissolution in the swollen polymer matrix and diffusion through the polymer matrix bulk.

Camptothecin is an example of a potent drug with a short half-life that would benefit from a localized drug depot system that maintains its stability prior to being released. For this reason, a thermoplastic, biodegradable polymer drug depot was prepared and characterized, and the in vitro release of camptothecin examined. epsilon-Caprolactone oligomers were prepared by ring-opening polymerization initiated by various alcohols. The polymers were characterized via differential scanning calorimeter (DSC) for thermal transitions, and via a parallel plate rheometer for melt viscosity. Camptothecin was loaded into the oligomers and released into PBS buffer. The viscosity of the oligomers was alterable by the initiator used. The oligomers were semi-crystalline with melting points between 37 and 45 degrees C. Camptothecin was released from the oligomers in a diffusion-controlled manner, with the release rate increasing as the melt viscosity of the oligomer decreased. The unreleased camptothecin remained in its active lactone form for a period of up to 16 weeks., (Copyright 2004 Wiley-Liss, Inc. and the American Pharmacists Association J Pharm Sci 93:1195-1204, 2004)

A polymeric delayed-release protein delivery system was investigated with albumin as a model drug. The polysaccharide chitosan was reacted with sodium alginate in the presence of calcium chloride to form microcapsules with a polyelectrolyte complex membrane. Variables believed to be important for membrane formation were examined; these included reaction time, chitosan molecular weight, alginate concentration, chitosan concentration, and solution pH. An alginate-chitosan reaction time, in the range of 10 to 45 min, had no effect on the release of albumin. Increasing the alginate concentration, however, resulted in a decreased rate of release of albumin (from 37% release at 4 h with 1.5% alginate to 20% release with 2.5% alginate). Another key variable was the chitosan molecular weight. The molecular weight of chitosan was varied from 1.25 x 10(6) to 0.25 x 10(6) through a nitrite oxidation reaction with sodium nitrite. Decreasing the molecular weight increased the release of albumin (from 37% release at 4 h with high molecular weight chitosan to 77% release with low molecular weight chitosan). The pH of the extracapsular environment was found to affect the release of albumin significantly (15% release over 24 h at a pH 3.0 and 73% release at pH 8.0). Capsules produced with high molecular weight chitosan and a combination of high and low molecular weight chitosan gave the best results for reducing elution of albumin in the first 4 h and increasing elution in the following 20 h.