Fireside corrosion behavior of Inconel 740H superalloy was studied at 750 °C in simulated coal ash/flue gas environments by means of XRD, SEM and EDS. The results indicated that the corrosion behavior was strongly related to the SO2 levels and was significantly affected by NaCl additions. In presence of the atmospheres with 0.1 % SO2, the alloy exhibited the highest corrosion resistance due to formation of a stable and dense Cr2O3 film. In presence of the atmosphere with 1.5 % SO2, however, a non-coherent and porous Cr2O3 film was formed. The thickness of film and internal sulfides were substantially increased. The NaCl additions significantly accelerated the corrosion process. A non-protective outer oxide film was formed, composed by multiple layers with serious inner sulfide and spallation. The depths of internal oxidizing and sulfuration zones were significantly increased. The mechanism of ash corrosion formation was also discussed.

Inconel 740H alloy is a candidate material for 700°C advanced ultra-supercritical (A-USC) coal-fired power plants application as superheater/reheater tube. In this work, oxidation behavior of Inconel 740H alloy was studied in static air at 750°C and 850°C, and in dynamic pure steam at 750°C, respectively. The alloy was oxidized approximately following a parabolic law in three test environment. In the static air, the oxidation rate at 850°C was about 50 times of that at the 750°C. More NiCrMn spinal and TiO2 were detected after oxidation at 850°C. Cr2O3, however, was the main oxidation product at 750°C. In the pure steam, Cr2O3 was still the main oxidation product. The oxidation rate was about 2.6 times of that in static air, but the surface roughness was much smaller and edges of oxide particles were more blurred. There was no evidence of cracks or spallation in three test environments.