Search

Rice straw fibers are potential raw materials that can be used to produce biogas and reinforcing fibers for composites. In order to ascertain the effects of anaerobic digestion on the structural properties of the fibers, the structure of fibrous residuals with different digestion time, including 0, 10, 20, and 30 days, were investigated. The normalized biogas production volume was 224 mL/g volatile solid of substrate, of which the methane content was about 50%. Fiber detergent analyses of the straw before and after 10 days digestion indicated that the cellulose levels increased from 34.3% to 41.3%, and cellulose crystallinity index ranged from 44.9% to 49.9%, respectively. After the rice straw had been digested for 30 days, the cellulose and hemicelluloses of the rice straw were partially degraded; the crystallinity index of the cellulose decreased from 44.9% to 40.1% based on XRD analyses, and the amount of hydroxyl groups were observed to decrease based on FT-IR analyses. Consequently, the polarity and hygroscopicity of the rice straw fibers were speculated to be lowered based on these observed changes. Furthermore, the relative amount of lignin in the straw residuals increased as digestion time increased, which increased the thermal stability of the resulting fibers. As a result of anaerobic digestion, the properties of the rice straw fibers for their use in plastic composites were enhanced.

Hydrothermal carbonization (HTC) is an efficient conversion process that treats solid digestates from anaerobic digestion plants and converts it into valuable solid products. In this study, digestates of swine manure (DS_M) and rice straw (DS_S) were HTC-treated at 190 °C with biomass-to-water ratios of 1:4 and 1:9. The hydrochars were characterized physically and chemically to elucidate their potential as a valuable resource. The hydrochars from the solid digestates were acidic, and the dissolved organic carbon (DOC), dissolved organic nitrogen (DON), and Brunauer-Emmett-Teller surface area (SBET) were significantly (P < 0.05) higher compared with that of the feedstocks and pyrochars. Mesopores were dominant in the hydrochars, where the pores had slit-type holes and a stratified structure. The hydrochars possessed more O functional groups and aromatic C=C and C-H band than the feedstocks and pyrochars. The hydrochars derived from solid digestates were better as a solid fuel because of their combustion property. The increase in the crystallinity of the hydrochars enhanced their stability. The hydrochars produced from the DS_M were more acidic than those from the DS_S. The HTCDS_S had a better adsorptive effect on pollutants than the HTCDS_M because of the higher SBET and optimal functional groups.

To improve the compatibility between rice straw and reinforcing polymers, rice straw (RS) was pretreated by an anaerobic process, and its biogas residues (BR) were acetylated with acetic anhydride (AA) to prepare acetylated biogas residues (ABR). The optimum conditions of acetylation were determined by orthogonal experiments. When acetylation was performed at 140 °C with 10 mL AA/g BR and 0.08 g catalyst/g BR, the maximum weight gain rate (WGR) obtained was 23.7%. Fourier transform infrared (FTIR) analysis showed that many hydroxyl groups were displaced by acetoxy groups. Scanning electron microscopy (SEM) showed that many defects of BR were filled by the acetylation, and an ester layer was formed over the BR surface. However, the lower crystallinity of ABR than the BR and RS affected the mechanical properties of acetylated biogas residue/low density polyethylene (ABR/LDEP) composite. Interestingly, the BR and ABR showed higher onset decomposition temperature, but they exhibited faster decomposition rates because of the lower crystallinity of BR and ABR. Furthermore, the mechanical properties of the RS/LDEP, BR/LDEP, and ABR/LDEP composites were analyzed. Compared with RS/LDEP composites, the BR/LDEP and ABR/LDEP composites showed obviously better tensile and flexural properties. Consequently, rice straw fibers attained excellent compatibility with non-polar polymers.

The degradation behavior was investigated for eco-composite nursery containers (NCs) prepared with rice husk and cornstarch adhesive modified with urea formaldehyde (UF) as a wet strength agent. The wet shear strength, water absorption capacities, and biological degradation of NCs within soil were also investigated. Quantitative analysis of the thermal degradation behavior of different NC versions was performed by thermo-gravimetric analysis (TGA). The results demonstrated that the introduction of the UF agent accelerated the soil degradation of the NCs matrix to a certain extent. The maximum cumulative mass loss was 51.1% when the UF content of NCs was 8 wt.%. Moreover, the dry strength of the mixed urea formaldehyde-cornstarch adhesive (UCA) was increased by 108.9% compared with cornstarch adhesive (CA). The results of this work indicate the improved biodegradability of the NC eco-composites, which could make them potential sustainable alternatives for conventional plastic pots.

A biodegradable planting container made with rice straw and starch adhesives modified by polyvinyl alcohol was studied in this paper. The effect of heat treatment and polyamide resin on the properties of planting containers was investigated. The physical property and biodegradability were characterized by means of hygroscopicity, FTIR, degradability, and the thermogravimetric analysis. The results showed that the dry strength of planting containers increased as a result of both treatments. The wet strength of planting containers increased as a result of heat treatment, while the wet strength of planting containers decreased as a result of polyamide resin. The hygroscopicity of planting containers decreased with heat treatment and polyamide resin. The effect of heat treatment was more obvious than the effect of polyamide resin. It was observed that the peak intensity and position were changed for the 3400 cm-1, 2900 cm-1, 1640 cm -1, 1500 cm-1, 1400 cm-1, and 1050 cm-1 under the treatment of polyamide resin. The weight loss of specimens treated with polyamide resin was larger because of the presence of nitrogen in the resin. The appearance of planting containers showed the heat treatment containers were not easily prone to mildew when used for planting. The thermogravimetric analysis (TGA) showed that heat treatment can improve the thermal stability, while the polyamide resin was shown to promote the degradation of planting containers.