Search

We report on the coexistence of magnetic and superconducting states in CeFeAsO1-xFx for x=0.06(2), characterized by transition temperatures T_m=30 K and T_c=18 K, respectively. Zero and transverse field muon-spin relaxation measurements show that below 10 K the two phases coexist within a nanoscopic scale over a large volume fraction. This result clarifies the nature of the magnetic-to-superconducting transition in the CeFeAsO1-xFx phase diagram, by ruling out the presence of a quantum critical point which was suggested by earlier studies., Comment: 4 pages, 3 figs, accepted for publication as PRB Rapid comm

In this paper we report a detailed $\mu^{+}$SR and {}$^{19}$F-NMR study of the La$_{0.7}$Y$_{0.3}$FeAsO$_{1-x}$F$_{x}$ class of materials. Here, the diamagnetic La$_{1-y}$Y$_{y}$ substitution increases chemical pressure and, accordingly, sizeably enhances the optimal superconducting transition temperature. We investigate the magnetic-superconducting phase transition by keeping the Y content constant ($y = 0.3$) and by varying the F content in the range $0.025 \leq x \leq 0.15$. Our results show how magnetism and superconductivity coexist for $x = 0.065$. Such coexistence is due to segregation of the two phases in macroscopic regions, resembling what was observed in LaFeAsO$_{1-x}$F$_{x}$ materials under applied hydrostatic pressure. This scenario is qualitatively different from the nanoscopic coexistence of the two order parameters observed when La is fully substituted by magnetic rare-earth ions like Sm or Ce., Comment: Proceedings of QCNP12 Conference

$^{19}$F NMR measurements in SmFeAsO$_{1-x}$F$_x$, for $0.15\leq x\leq 0.2$, are presented. The nuclear spin-lattice relaxation rate $1/T_1$ increases upon cooling with a trend analogous to the one already observed in CeCu$_{5.2}$Au$_{0.8}$, a quasi two-dimensional heavy-fermion intermetallic compound with an antiferromagnetic ground-state. In particular, the behaviour of the relaxation rate either in SmFeAsO$_{1-x}$F$_x$ or in CeCu$_{5.2}$Au$_{0.8}$ can be described in the framework of the self-consistent renormalization theory for weakly itinerant electron systems. Remarkably, no effect of the superconducting transition on $^{19}$F $1/T_1$ is detected, a phenomenon which can hardly be explained within a single band model., 4 figures

The nuclear and magnetic structure of Fe1+y(Te1-x,Sex) (0 < x < 0.20) compounds was analyzed between 2 K and 300 K by means of Rietveld refinement of neutron powder diffraction data. Samples with x < 0.075 undergo a tetragonal to monoclinic phase transition at low temperature, whose critical temperature decreases with increasing Se content; this structural transition is strictly coupled to a long range antiferromagnetic ordering at the Fe site. Both the transition to a monoclinic phase and the long range antiferromagnetism are suppressed for 0.10 < x < 0.20. The onset of the structural and of the magnetic transition remains coincident with the increase of Se substitution. The low temperature monoclinic crystal structure has been revised. Superconductivity arises for x > 0.05, therefore a significant region where superconductivity and long range antiferromagnetism coexist is present in the pseudo-binary FeTe - FeSe phase diagram., 33 pages, 4 tables, 13 figures

We present a study concerning the partial substitution of yttrium at the lanthanum site of the undoped LaFeAsO and superconducting LaFeAsO0.85F0.15 compounds. We prepared samples with a nominal yttrium content up to 70% producing simultaneous shrinkage of both the a- and c-lattice parameters by 1.8% and 1.7%, respectively. The chemical pressure provided by the partial substitution with this smaller ion size causes a lowering of the spin density wave temperature in the undoped compounds, as well as an increase of the superconducting transition temperatures in the doped ones. The 15% fluorine-doped samples reach a maximum critical temperature of 40.2 K for the 50% yttrium substitution. Comparison with literature data indicates that chemical pressure cannot be the only mechanism which tunes drastically both TSDW and Tc in 1111 compounds. Our data suggest that structural disorder induced by the partial substitution in the La site or by doping could play an important role as well.

Recent investigations have shown that the first proposed explanations of the disagreement between experimental and theoretical value of isotope coefficient in MgB2 need to be reconsidered. Considering that in samples with residual resistivity of few mu-Ohm cm critical temperature variations produced by disorder effects can be comparable with variations due to the isotopic effect, we adopt a procedure in evaluating the B isotope coefficient which take account of these effects, obtaining a value which is in agreement with previous results and then confirming that there is something still unclear in the physics of MgB2., Comment: 8 pages, 3 figures Title has been changed A statement has been added in page 7 of the pdf file "Finally we would..." Reference 21 has been added Figure 1 anf Figure 2 have been changed

A comparative study of thermal properties of SmFeAsO, SmFeAs(O0.93F0.07) and SmFeAs(O0.85F0.15) samples is presented. Specific heat and thermal conductivity show clear evidences of the spin density wave (SDW) ordering below TSDW 135 K in undoped SmFeAsO. At low level of F-doping, SmFeAs(O0.93F0.07), SDW ordering is suppressed and superconducting features are not yet optimally developed in both specific heat and thermal conductivity. At optimal level of F-doping SmFeAs(O0.85F0.15) anomalies related to the superconducting transition are well noticeable. By a compared analysis of doped and undoped samples we conclude that, despite F-doping modifies definitely the electronic ground state, it does not substantially alter phonon and electron parameters, like phonon modes, Sommerfeld coefficient, electro-phonon coupling. The analysis of the thermal conductivity curves provides an evaluation of SDW and superconducting energy gap, showing that phonons can suitably probe features of electronic ground state.

In this paper the magnetic behaviour of SmFeAsO and SmFeAs(O0.85F0.15) samples is presented and discussed. Molar susceptibility of SmFeAsO exhibits a local peak at T around 140K due to the establishment of a long range antiferromagnetic ordering of the Fe moments in Fe-As layers. This feature has already been observed with different techniques, and frequently ascribed to the onset of a Spin Density Wave (SDW). At TN around 6K another peak, which we attribute to the establishment of antiferromagnetic ordering of Sm ion sublattice, is observed. Furthermore, a temperature independent signal (Pauli paramagnetism, Landau and core diamagnetism...) is also present in the magnetic behaviour of this sample. In SmFeAs(O0.85F0.15) the antiferromagnetic ordering in Fe-As plane is suppressed and superconductivity occurs at T = 52 K, whereas the antiferromagnetic ordering of Sm ions at low temperature persists, leading to the coexistence and competition between superconducting and magnetic orderings. Above the transition temperature, after the subtraction of the Sm ion sublattice paramagnetic contribution and of the temperature independent contribution to the experimental susceptibility data, a Curie-Weiss behaviour for Fe is observed, with a magnetic moment of 1.4 Bohr magneton., Comment: submitted to Physical Review B

SmFeAsO and the isostructural superconducting SmFeAs(O0.93F0.07) samples were prepared. Characterization by means of Rietveld refinement of X-ray powder diffraction data, scanning electron microscope observation, transmission electron microscope analysis, resistivity and magnetization measurements were carried out. Sintering treatment strongly improves the grain connectivity, but, on the other hand, induces a competition between the thermodynamic stability of the oxy-pnictide and Sm2O3, hence worsening the purity of the sample. In the pristine sample both magnetization and resistivity measurements clearly indicate that two different sources of magnetism are present: the former related to Fe ordering at 140 K and the latter due to the Sm ions that orders antiferromagnetically at low temperature. The feature at 140 K disappears in the F-substituted sample and, at low temperatures a superconducting transition appears. The magnetoresistivity curves of the F-substituted sample probably indicates very high critical field values., Submitted to: Superconductor Science and Technology

In DC and AC practical applications of MgB2 superconducting wires an important role is represented by the material sheath which has to provide, among other things, a suitable electrical and thermal stabilization. A way to obtain a large enough amount of low resistivity material in to the conductor architecture is to use it as external sheath. In this paper we study ex-situ multifilamentary MgB2 wires using oxide-dispersion-strengthened copper (GlidCop) as external sheath in order to reach a good compromise between critical current density and thermal properties. We prepared three GlidCop samples differing by the content of dispersed sub-microscopic Al2O3 particles. We characterized the superconducting and thermal properties and we showed that the good thermal conductivity together the good mechanical properties and a reasonable critical current density make of GlidCop composite wire a useful conductor for applications where high thermal conductivity is request at temperature above 30K, such as Superconducting-FCL., Comment: Submitted to Supercond. Sci. Technol