A theoretical-experimental methodology for failure analysis of the c-Al0.66Ti0.33N / Interface / M2 steel coating system is proposed here. This c-Al0.66Ti0.33N coating was deposited by the arc-PVD technique. For coating modeling the traction-separation law and the extended finite element method-XFEM were applied, the cohesive zones model was used for interface modeling and the Ramberg-Osgood law for substrate modeling. Experimental values using the instrumented nanoindentation technique, the scratch test and tensile stress test were obtained and introduced into the model. By means of nanoindentation the elastic modulus of coating, the fracture energy release rate and the nano-hardness. Normal and shear stress values of the interface were obtained with the scratch test, at the adhesive and cohesive critical loads. Vickers indentation was used to generate cracking patterns in the c-Al0.66Ti0.33N / Interface / M2 steel coating system. Radial and lateral cracks were generated and analyzed after transversal FIB cuts of the fracture zones. A finite element analysis was carried out to understand the relationship between the load-displacement curve and mechanical failure of in the system, associating the pop-in with nucleation, crack growth and cracking pattern. This works present a theoretical-experimental methodology for failure analysis of hard coatings (monolithic body) allowing to calculate fracture toughness of the coating material and model cracking patterns caused by contact mechanics.

The effect of graded or constant bias voltages (-40 V, -80 V and -40/60/80 V) on size grain and surface defects of arc PVD deposited CrN films was investigated. Corrosion resistance evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic curves (Tafel) and the mechanical behavior evaluated by means of instrumented nanoindentation and scratch testing was correlated with the microstructural changes. It was found that the bias voltage variation affects corrosion behavior due to the presence of defects (i.e. open voids, droplets) which also affects the failure mechanisms and increasing spallation. High bias voltage (-80 V) increases nano-hardness and the elastic modulus due to the dense microstructure of the CrN coating.

The effect of isothermal pre-oxidation treatments on the \b{eta}-(Ni,Pt)Al + Ren\'e N5 system degradation is here reported. The oxidation treatments were carried out from 900 (mostly {\theta}-Al2O3 growing conditions) to 1200{\deg}C (mainly {\alpha}-Al2O3 growing conditions) for 5 h, under a purified Ar-stream with a fixed pO2= 1 x 10-5 atm. Results are discussed based on the correlation between the structural, microstructural and chemical properties of the \b{eta}-(Ni,Pt)Al BC showing that pre-oxidation parameters have an important effect on the multi-elemental counter diffusion phenomena along BC. For instance, a significant BC+IDZ thickness increase of 55% at 1200 {\deg}C was observed with respect to as-received sample just after 5 h of oxidation resulting in a severe BC degradation., Comment: 18 pages, 7 Figures