Dynamic crack propagation across a perpendicular interface in a glass specimen was investigated to understand the interaction between the crack and the interface under impact loading. The glass specimen was composed of two glass plates in an edge-to-edge configuration with an adhesive layer in between. One of the plates had a notch for a plastic projectile to strike. A single crack developed from the notch tip, and propagated perpendicularly into the interface. The patterns of crack propagation across the interface depend on the adhesive conditions on the interface. Within a range of impact speeds, the crack is arrested at the interface without any adhesive. The crack passes across a firmly bonded interface with little obstruction by the interface. The crack branches into multiple cracks after it passes through a thicker interface filled with adhesive. Projectiles having higher kinetic energies cause more severe crack branching after the crack extends into the second glass plate [ABSTRACT FROM AUTHOR]

Glass impact experiments were designed at three different scales-0.22-cal, 0.375-cal, and 0.50-cal-named after the diameter of the bullets. Four experimental series were conducted at the three scale sizes: (1) Lexan®-only experiments; (2) monoblock glass experiments; (3) single impact bonded glass experiments, and (4) multi-hit experiments. The experiments were conducted to obtain residual velocity Vr as a function of impact (striking) velocity Vs, including sufficient partial penetrations to calculate a ballistic limit velocity V50. The Vs - Vr data were fit to the Lambert equation to obtain another estimate of V50. The objective of the experiments was to investigate whether a time dependency exists in glass damage/failure for ballistic experiments, and if so, quantify this dependence. No scale effect was observed in experimental results for the Lexan®-only experiments. But a variety of scale effects were observed in the glass impact experiments, suggesting that failure is time dependent within the timeframe of ballistic events [ABSTRACT FROM AUTHOR]