Search

The effect of heteroepitaxial β-(AlxGa1−x)2O3 film thickness and Al content on surface morphology was characterized to experimentally determine the critical thickness limitations of the (010) β-(AlxGa1−x)2O3/Ga2O3 heterostructure. High-resolution x-ray diffraction was used to assess the strain state of the films; reciprocal space mapping (RSM) revealed that even cracked films were still fully strained. In cracked films, diffuse scattering was observed in RSMs, indicating lattice tilting. Cracking of the films was investigated using atomic force microscopy (AFM), x-ray topography (XRT), bright-field scanning transmission electron microscopy (BF-STEM), and high-resolution transmission electron microscopy. Using both AFM and XRT, the [001] direction was observed to be the most prevalent crack direction; however, cracks were also observed in the [100] direction. In uncracked regions of the films, XRT revealed the alignment of threading dislocations along the [001] direction. Cross-sectional imaging of the crack geometry and propagation was performed using BF-STEM, and it was observed that the cracks in the [001] direction extended through the thickness of the β-(AlxGa1−x)2O3 film (∼205 nm) and a further ∼100–200 nm into the β-Ga2O3 substrate. Experimental data for critical film thickness showed good agreement with previous theoretical calculations based on the Griffith criterion for crack propagation. [ABSTRACT FROM AUTHOR]

The first step of a multi-cycle rapid thermal annealing process was systematically studied. The surface, structure, and optical properties of Mg implanted GaN thin films annealed at temperatures ranging from 900 to 1200 °C were investigated by Raman spectroscopy, photoluminescence, UV-visible spectroscopy, atomic force microscopy, and Nomarski microscopy. The GaN thin films are capped with two layers of in-situ metal organic chemical vapor deposition -grown AlN and annealed in 24 bar of N2 overpressure to avoid GaN decomposition. The crystal quality of the GaN improves with increasing annealing temperature as confirmed by UV-visible spectroscopy and the full widths at half maximums of the E2 and A1 (LO) Raman modes. The crystal quality of films annealed above 1100 °C exceeds the quality of the as-grown films. At 1200 °C, Mg is optically activated, which is determined by photoluminescence measurements. However, at 1200 °C, the GaN begins to decompose as evidenced by pit formation on the surface of the samples. Therefore, it was determined that the optimal temperature for the first step in a multi-cycle rapid thermal anneal process should be conducted at 1150 °C due to crystal quality and surface morphology considerations. [ABSTRACT FROM AUTHOR]

As an emerging optical material, graphene's ultrafast dynamics are often probed using pulsed lasers yet the region in which optical damage takes place is largely uncharted. Here, femtosecond laser pulses induced localized damage in single-layer graphene on sapphire. Raman spatial mapping, SEM, and AFM microscopy quantified the damage. The resulting size of the damaged area has a linear correlation with the optical fluence. These results demonstrate local modification of sp2-carbon bonding structures with optical pulse fluences as low as 14 mJ/cm2, an order-of-magnitude lower than measured and theoretical ablation thresholds. [ABSTRACT FROM AUTHOR]