Olive pit powder particles were impregnated with copper and nickel nitrates and pyrolyzed at 400 °C. The resulting material consists of bimetallic CuNi-decorated biochar. CuNi nanocatalysts were found to be as small as 10 nm and very well dispersed over biochar. XRD results evidenced zero valent copper and nickel and formation of copper-nickel solid solutions.The biochar@CuNi was found to be efficient catalyst of the reduction of methyl orange (MO) dye, taken as model pollutant. To sum up, the one pot method devised in this work provided unique CuNi-decorated biochar and opens new horizons for the emerging topic of biochar-supported nanocatalysts.

Rh-based nanoparticles supported on a porous carbon host were prepared with tunable average sizes ranging from 1.3 to 3.0 nm. Depending on the vacuum or hydrogen environment during thermal treatment, either Rh metal or hydride is formed at nanoscale, respectively. In contrast to bulk Rh that can form a hydride phase under 4 GPa pressure, the metallic Rh nanoparticles (∼2.3 nm) absorb hydrogen and form a hydride phase at pressure below 0.1 MPa, as evidenced by the presence of a plateau pressure in the pressure-composition isotherm curves at room temperature. Larger metal nanoparticles (∼3.0 nm) form only a solid solution with hydrogen under similar conditions. This suggests a nanoscale effect that drastically changes the Rh-H thermodynamics. The nanosized Rh hydride phase is stable at room temperature and only desorbs hydrogen above 175 °C. Within the present hydride particle size range (1.3-2.3 nm), the hydrogen desorption is size-dependent, as proven by different thermal analysis techniques.

Control of the work function of GaAs single crystals, under ambient conditions, was achieved by chemisorption of a series of benzoic acid derivatives with varying dipole moments. Quantitative Fourier transform infrared spectroscopy shows that the benzoic acid derivatives bind as carboxylates, via coordination to oxidized Ga or As atoms, with a surface coverage of about one layer and a binding constant of 2.1 104 M-1 for benzoic acid. Contact potential difference measurements reveal that molecules affect the work function by changing the electron affinity while band bending is not affected significantly. The direction of the electron affinity changes depends on the direction of the dipole moments, and the extent of the change increases linearly with the dipole's magnitude. Investigation of the surface composition by X-ray photoelectron spectroscopy shows that the etched surface, onto which the molecules adsorb, is covered by an oxide layer. This may prevent the molecules from affecting band bending.