Benjamin M. Oxley, Michael Waters, Mercouri G. Kanatzidis, Shiqiang Hao, Chris Wolverton, Jeong Bin Cho, Venkat Gopalan, Hye Ryung Byun, Abishek K. Iyer, James M. Rondinelli, and Joon I. Jang
The mixed cation compounds Na1-xKxAsSe2 (x = 0.8, 0.65, 0.5) and Na0.1K0.9AsS2 crystallize in the polar noncentrosymmetric space group Cc. The AAsQ2 (A = alkali metals, Q = S, Se) family features one-dimensional (1D) 1/∞[AQ2-] chains comprising corner-sharing pyramidal AQ3 units in which the packing of these chains is dependent on the alkali metals. The parallel 1/∞[AQ2-] chains interact via short As···Se contacts, which increase in length when the fraction of K atoms is increased. The increase in the As···Se interchain distance increases the band gap from 1.75 eV in γ-NaAsSe2 to 2.01 eV in Na0.35K0.65AsSe2, 2.07 eV in Na0.2K0.8AsSe2, and 2.18 eV in Na0.1K0.9AsS2. The Na1-xKxAsSe2 (x = 0.8, 0.65) compounds melt congruently at approximately 316 °C. Wavelength-dependent second harmonic generation (SHG) measurements on powder samples of Na1-xKxAsSe2 (x = 0.8, 0.65, 0.5) and Na0.1K0.9AsS2 suggest that Na0.2K0.8AsSe2 and Na0.1K0.9AsS2 have the highest SHG response and exhibit significantly higher laser-induced damage thresholds (LIDTs). Theoretical SHG calculations on Na0.5K0.5AsSe2 confirm its SHG response with the highest value of d33 = 22.5 pm/V (χ333(2) = 45.0 pm/V). The effective nonlinearity for a randomly oriented powder is calculated to be deff = 18.9 pm/V (χeff(2) = 37.8 pm/V), which is consistent with the experimentally obtained value of deff = 16.5 pm/V (χeff(2) = 33.0 pm/V). Three-photon absorption is the dominant mechanism for the optical breakdown of the compounds under intense excitation at 1580 nm, with Na0.2K0.8AsSe2 exhibiting the highest stability.