Search

This work provides a simple method to prepare a hydrophilic/oleophobic coating using polyester filter cloth as the substrate, a mixture of three hydrophilic polymers (poly(aspartic acid), poly(acrylic acid), and poly(vinyl alcohol)); SiO 2 with an average particle size of 30 nm is used to improve the surface roughness of the filter cloth. Then, a long fluorocarbon chain of 1 H ,1 H ,2 H ,2 H -perfluorooctyltriethoxysilane is grafted onto the surface by a vacuum silanization coupling reaction to obtain hydrophilic/oleophobic properties. The water and hexadecane contact angles of the treated filter cloth are 3 and 99.8°, respectively. A separation efficiency of 98% was achieved in hexadecane/water separation. The durability test shows that the separation efficiency of toward hexadecane-water mixture remains more than 98% after 20 cycles. The obtained material also presents a strong underwater antipollution property when using hexane, rapeseed oil, mineral oil, and pump oil as model pollutants. For oils with higher viscosity, the separation efficiency remains above 97%. However, the separation efficiency is ∼80% when treating emulsions.

Surfaces that stay clean when immersed in water are important for an enormous range of applications from ships and buildings to marine, medical, and other equipment. Up until now the main strategy for designing self-cleaning surfaces has been to combine hydrophilic/hydrophobic coatings with a high aspect ratio structuring (typically micron scale pillars) to trap a (semi)static water/air layer for drag and adhesion reduction. However, such coating and structuring can distort optical properties and get damaged in harsh environments, and contamination, i.e., particles, oil droplets, and biofouling, can get trapped and aggregate in the structure. Here we present a radically different strategy for self-cleaning surface design: We show that a surface can be made self-cleaning by structuring with a pattern of very low aspect ratio pillars ("pancakes"). Now the water is not trapped. It can flow freely around the pancakes thus creating a dynamic water layer. We have applied the new pancake design to sapphire windows and made the first surfaces that are self-cleaning through structuring alone without the application of any coating. An offshore installation has now been running continuously with structured windows for more than one year. The previous uptime for unstructured windows was 7 days.

Oleophobic surfaces have been so far realized using complex microscale and nanoscale re-entrant geometries, where primary and secondary structures or overhang geometries are typically required. Here, we propose a new design to create them with noninteracting cavities. The suspension of liquid droplets relies on the mechanism of compression of air under the meniscus leading to stable composite oil-air-solid interfaces. To demonstrate the concept, we make oleophobic surfaces, with contact angle for oleic acid of about 130° (and hexadecane about 110°), using both microholes in silicon and nanoholes in glass. Thanks to the subwavelength dimensions and antireflection effect of the nanoholes, the glass substrate also shows a high degree of optical transparency with optical transmission exceeding that of the initial bare substrate. Crockmeter tests without any significant change in morphology, optical and wetting properties after more than 500 passes also confirm the high mechanical durability of the nanohole surface. The results indicate the possibility of using the proposed oleophobic surfaces for a wide range of applications, including self-cleaning transparent windows and windshields for automobiles and aircrafts.

The utility of omniphobic surfaces stems from their ability to repel a multitude of liquids, possessing a broad range of surface tensions and polarities, by causing them to bead up and either roll or slide off. These surfaces may be self-cleaning, corrosion-resistant, heat-transfer enhancing, stain-resistant or resistant to mineral- or biofouling. The majority of reported omniphobic surfaces use texture, lubricants, and/or grafted monolayers to engender these repellent properties. Unfortunately, these approaches often produce surfaces with deficiencies in long-term stability, durability, scalability, or applicability to a wide range of substrates. To overcome these limitations, we have fabricated an all-solid, substrate-independent, smooth, omniphobic coating composed of a fluorinated polyurethane and fluorodecyl polyhedral oligomeric silsesquioxane. Liquids of varying surface tension, including water, hexadecane, ethanol, and silicone oil, exhibit low-contact-angle hysteresis (<15°) on these surfaces, allowing liquid droplets to slide off, leaving no residue. Moreover, we demonstrate that these robust surfaces retained their repellent properties more effectively than textured or lubricated omniphobic surfaces after being subjected to mechanical abrasion.

Human interaction with touch screens requires physical touch and hence results in contamination of these surfaces, resulting in the necessity of cleaning. In this study we discuss the three bodies of this problem and how each component contributes and can be controlled. Utilizing a standard fingerprint machine and a standard cleanability test, this study examines the influence of parameters such as the wiping speed and pressure, the material and surface area of the cloths, and the surface energy of the contaminated surfaces. It was shown that fingerprint contamination undergoes shear banding and hence is not easily removed. The degree of material removal depends on the position of the shear plane, which is influenced by surface energies and shear rates.