Search

Heavy pnictogen chalcohalides are often termed lead-free, perovskite-inspired materials. Despite theoretical predictions, incontrovertible experimental demonstrations of heavy pnictogen chalcohalides adopting a perovskite structure are lacking. Here we report our attempts to prepare CsBiSCl 2 adopting a perovskite structure as colloidal nanocrystals. Synthesis of nanoscale materials can indeed rely on fast, nonequilibrium reactions and on large, eventually thermodynamically favorable surface energies, leading to the possibility of stabilizing kinetically trapped or metastable phases. However, we obtained no CsBiSCl 2 , but a mixture of nanocrystals of secondary phases, namely Cs 3 BiCl 6 submicrometric polyhedra, Bi 2 S 3 nanoscopic rods, and Cs 3 Bi 2 Cl 9 nanoscopic dots, whose low polydispersity enabled an effective separation via size/shape selective precipitation. This work confirms that heavy pnictogen chalcohalides are hardly prone to adopting a perovskite structure. Nevertheless, chemistry at the nanoscale offers multiple possibilities for overcoming phase segregation and pursuing the synthesis of prospective mixed anion compound semiconductors.

Because of its electrically conducting properties combined with excellent thermal stability and transparency throughout the visible spectrum, tin oxide (SnO 2 ) is extremely attractive as a transparent conducting material for applications in low-emission window coatings and solar cells, as well as in lithium-ion batteries and gas sensors. It is also an important catalyst and catalyst support for oxidation reactions. Here, we describe a novel nonaqueous sol-gel synthesis approach to produce tin oxide nanoparticles (NPs) with a low NP size dispersion. The success of this method lies in the nonhydrolytic pathway that involves the reaction between tin chloride and an oxygen donor, 1-hexanol, without the need for a surfactant or subsequent thermal treatment. This one-pot procedure is carried out at relatively low temperatures in the 160-260 °C range, compatible with coating processes on flexible plastic supports. The NP size distribution, shape, and dislocation density were studied by powder X-ray powder diffraction analyzed using the method of whole powder pattern modeling, as well as high-resolution transmission electron microscopy. The SnO 2 NPs were determined to have particle sizes between 3.4 and 7.7 nm. The reaction products were characterized using liquid-state 13 C and 1 H nuclear magnetic resonance (NMR) that confirmed the formation of dihexyl ether and 1-chlorohexane. The NPs were studied by a combination of 13 C, 1 H, and 119 Sn solid-state NMR as well as Fourier transform infrared (FTIR) and Raman spectroscopy. The 13 C SSNMR, FTIR, and Raman data showed the presence of organic species derived from the 1-hexanol reactant remaining within the samples. The optical absorption, studied using UV-visible spectroscopy, indicated that the band gap ( E g ) shifted systematically to lower energy with decreasing NP sizes. This unusual result could be due to mechanical strains present within the smallest NPs perhaps associated with the organic ligands decorating the NP surface. As the size increased, we observed a correlation with an increased density of screw dislocations present within the NPs that could indicate relaxation of the stress. We suggest that this could provide a useful method for band gap control within SnO 2 NPs in the absence of chemical dopants., Competing Interests: The authors declare no competing financial interest.

As nanomaterials are dominating 21st century's scene, multiple functionality in a single (nano)structure is becoming very appealing. Inspired by the Land of the Rising Sun, we designed a bifunctional (gas-sensor/photochromic) nanomaterial, made with TiO 2 whose surface was simultaneously decorated with copper and silver (the Cu/Ag molar ratio being 3:1). This nanomaterial outperformed previous state-of-the-art TiO 2 -based sensors for the detection of acetone, as well as the Cu-TiO 2 -based photochromic material. It indeed possessed splendid sensitivity toward acetone (detection limit of 100 ppb, 5 times lower than previous state-of-the-art TiO 2 -based acetone sensors), as well as reduced response/recovery times at very low working temperature, 150 °C, for acetone sensing. Still, the same material showed itself to be able to (reversibly) change in color when stimulated by both UV-A and, most remarkably, visible light. Indeed, the visible-light photochromic performance was almost 3 times faster compared to the standard Cu-TiO 2 photochromic material-that is, 4.0 min versus 10.8 min, respectively. It was eventually proposed that the photochromic behavior was triggered by different mechanisms, depending on the light source used., Competing Interests: The authors declare no competing financial interest.